纺织学报 ›› 2022, Vol. 43 ›› Issue (06): 100-106.doi: 10.13475/j.fzxb.20210604907

• 染整与化学品 • 上一篇    下一篇

还原氧化石墨烯/粘胶基钒酸铋光催化材料的制备及其性能

钱佳琪1, 瞿建刚1(), 胡啸林1, 毛庆辉1,2   

  1. 1.南通大学 纺织服装学院, 江苏 南通 226019
    2.国家先进印染技术创新中心, 山东 泰安 271000
  • 收稿日期:2021-06-21 修回日期:2022-03-24 出版日期:2022-06-15 发布日期:2022-07-15
  • 通讯作者: 瞿建刚
  • 作者简介:钱佳琪(1996—),女,硕士生。主要研究方向为功能复合材料的制备。
  • 基金资助:
    南通市基础科学研究项目(JC2019007);生态纺织教育部重点实验室开放基金项目(KLE1708)

Preparation and property of reduced graphene oxide/viscose-based BiVO4 photocatalyst

QIAN Jiaqi1, QU Jian'gang1(), HU Xiaolin1, MAO Qinghui1,2   

  1. 1. School of Textile and Clothing, Nantong University, Nantong, Jiangsu 226019, China
    2. National Advanced Printing and Dyeing Technology Innovation Center, Taian, Shandong 271000, China
  • Received:2021-06-21 Revised:2022-03-24 Published:2022-06-15 Online:2022-07-15
  • Contact: QU Jian'gang

RichHTML

5

PDF (PC)

101

摘要：

针对钒酸铋(BiVO4)光催化效率低、难回收的缺点,利用硅烷偶联剂KH-560和氧化石墨烯(GO)依次对粘胶非织造布改性,再利用搅拌水热法在其表面生长BiVO4制备还原氧化石墨烯(RGO)/粘胶基BiVO4光催化材料。采用扫描电子显微镜、X射线衍射、X射线光电子能谱和紫外-可见吸收光谱对材料进行了表征,并研究了RGO/粘胶基BiVO4材料的光催化活性、重复使用性能和光催化机制。结果表明:BiVO4成功负载在RGO/粘胶非织造布表面,得到了RGO/粘胶基BiVO4光催化材料;在1 kW氙灯照射下,90 min内对活性黑5脱色率达到95%以上,重复5次后仍达到92%以上;自由基捕捉实验表明,光生空穴、超氧自由基和羟基自由基参与了光化学反应,其中羟基自由基的作用最大。

关键词: 石墨烯, 粘胶, 钒酸铋, 光催化, 活性黑5, 废水处理

Abstract:

In order to overcome the disadvantages of low photocatalytic efficiency and recyclability of BiVO4, silane coupling agent KH-560 and graphene oxide (GO) were used to modify the viscose nonwoven fabrics, then BiVO4 was grown on its surface by stirring hydrothermal method to prepare reduced graphene oxide (RGO)/viscose-based BiVO4 photocatalyst. The materials as prepared were characterized by scanning electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy and ultraviolet visible absorption spectroscopy. The photocatalytic activity, reusability and photocatalytic mechanism of RGO/viscose based BiVO4 photocatalyst for C.I. Reactive Black 5 decolorization were studied. The results show that BiVO4 is successfully loaded on RGO/viscose nonwovens and consequently RGO/viscose-based BiVO4 photocatalytic materials are obtained. Under the irradiation of 1 kW xenon lamp, the decolorization rate can reach up to 95% in 90 min, and over 92% is preserved even after five recycles. Furthermore, free radical capture experiments show that photogenerated hole, superoxide radical and hydroxyl radical participate in the photocatalytic reaction, and among which the hydroxyl radical is the most important.

Key words: graphene, viscose, BiVO4, photocatalysis, C.I. Reactive Black 5, waste water treatment

中图分类号: 

  • TS190.3

图1

不同样品的扫描电镜照片 注:图(c)和(d)中的插图为织物的导电性能测试图。"

图2

V-K、GO/V-K和BiVO4/RGO/V-K的X射线衍射图谱"

图3

V-K、GO/V-K和BiVO4/RGO/V-K的XPS谱图和BiVO4/RGO/V-K的V、C、O的高分辨XPS谱图"

图4

粘胶、V-K、GO/V-K、BiVO4/V-K和BiVO4/RGO/V-K的紫外-可见吸收光谱"

图5

BiVO4/V-K和BiVO4/RGO/V-K的带隙能"

图6

V-K、GO/V-K、BiVO4/V-K和BiVO4/RGO/V-K对RB5的光催化性能"

图7

降解前后RB5的可见光谱"

图8

BiVO4/RGO/V-K的重复光催化性能"

图9

不同捕捉剂对BiVO4/RGO/V-K的光催化效果"

[1] 钱怡帆, 周堂, 张礼颖, 等. 聚丙烯腈/醋酸纤维素/TiO2复合纳米纤维膜的制备及其光催化降解性能[J]. 纺织学报, 2020, 41(5): 8-14.
QIAN Yifan, ZHOU Tang, ZHANG Liying, et al. Preparation of polyacrylonitrile/cellulose acetate/TiO2 composite nanofiber membrane and its photocatalytic degradation performance[J]. Journal of Textile Research, 2020, 41(5): 8-14.
[2] 张婷婷, 许可欣, 金梦甜, 等. 纤维素基有机-无机纳米光催化复合材料制备及其水处理应用的研究进展[J]. 纺织学报, 2021, 42(7): 175-183.
ZHANG Tingting, XU Kexin, JIN Mengtian, et al. Recent progress in preparation of cellulose-based organic-inorganic photocatalysts nanohybrids and it's application in water treatment[J]. Journal of Textile Research, 2021, 42(7): 175-183.
doi: 10.1177/004051757204200309
[3] 陈瑞芳, 曲雯雯, 王一均, 等. 溶剂对钨酸铋/石墨烯形貌结构和光催化性能的影响[J]. 材料导报, 2021, 35(6):6008-6014.
CHEN Ruifang, QU Wenwen, WANG Yijun, et al. Effect of solvents on morphology and photocatalytic performance of Bi2WO6/RGO[J]. Materials Reports, 2021, 35(6): 6008-6014.
[4] 朱鸣凡, 卢泽强, 廖春鑫, 等. 花球状Bi2S3/BiOI复合光催化剂去除空气中甲醛的应用[J]. 无机化学学报, 2021, 37(3): 437-442.
ZHU Mingfan, LU Zeqiang, LIAO Chunxin, et al. Application in removal of formaldehyde in air by fliwe spherical Bi2S3/BiOI composite photocatalyst[J]. Chinese Journal of Inorganic Chemistry, 2021, 37(3): 437-442.
[5] 倪鑫, 周扬, 谭瑞琴, 等. 光电化学水扽姐中铁酸盐光阴极的制备与改性[J]. 化学进展, 2020, 32(10): 1515-1534.
doi: 10.7536/PC200334
NI Xin, ZHOU Yang, TAN Ruiqin, et al. Fabrication and modification of ferrite photocathodes for photoelectrochemical water splitting[J]. Progress in Chemistry, 2020, 32(10): 1515-1534.
doi: 10.7536/PC200334
[6] KOUTAVARAPU R, TAMTAM M R, MYLA C R, et al. Enhanced solar-light-driven photocatalytic properties of novel Z-scheme binary BiPO4 nanorods anchored onto NiFe2O4 nanoplates: efficient removal of toxic organic pollutants[J]. Journal of Environmental Sciences, 2021, 102: 326-340.
doi: 10.1016/j.jes.2020.09.021
[7] 蓝舟, 瞿建刚, 王春梅, 等. 纤维基钒酸铋的制备及其光催化性能[J]. 纺织学报, 2018, 39(6): 89-95.
LAN Zhou, QU Jiangang, WANG Chunmei, et al. Preparation and photocatalytic properties of BiVO4 loaded fiber[J]. Journal of Textile Research, 2018, 39(6): 89-95.
[8] LAI C, ZHANG M M, LI B S, et al. Fabrication of CuS/BiVO4 (040) binary heterojunction photocatalysts with enhanced photocatalytic activity for ciprofloxacin degradation andmechanism insight[J]. Chemical Engineering Journal, 2019, 358: 891-902.
doi: 10.1016/j.cej.2018.10.072
[9] 刘巍, 田永胜, 崔佳伟, 等. 铜修饰钒酸铋/膨润土复合材料的制备及可见光催化脱硫性能研究[J]. 化工新型材料, 2021, 49(2): 200-203.
LIU Wei, TIAN Yongsheng, CUI Jiawei, et al. Preparation and characterization of Cu-BiVO4/BTT nanocomposite for visible light photocatalytic desulfurization[J]. New Chemical Materials, 2021, 49(2): 200-203.
[10] FAN Y Y, YANG R J, ZHU R S, et al. CdS decorated artificial leaf BiVO4/InVO4 for photocatalytic hydrogen production and simultaneous degradation of biological hydrogen production wastewater[J]. Catalysis Today, 2021, 364: 190-195.
doi: 10.1016/j.cattod.2020.04.012
[11] 罗佳妮, 李丽君, 张晓思, 等. 氧化石墨烯掺杂TiO2改性活性炭纤维[J]. 纺织学报, 2020, 41(1): 8-14.
LUO Jiani, LI Lijun, ZHANG Xiaosi, et al. Modification of activated carbon fiber using graphene oxide doped titanium dioxide[J]. Journal of Textile Research, 2020, 41(1): 8-14.
[12] 刘稀, 王冬, 张丽平, 等. 醋酸处理对原液着色粘胶纤维黑度的影响研究[J]. 化工新型材料, 2020, 48(11): 188-191.
LIU Xi, WANG Dong, ZHANG Liping, et al. Influence of acetic acid treatment on blackness of spun-dyed viscose fiber[J]. New Chemical Materials, 2020, 48(11): 188-191.
[13] WANG Y L, DING K, XU R, et al. Fabrication of BiVO4/BiPO4/GO composite photocatalytic material for the visible light-driven degradation[J]. Journal of Cleaner Production, 2019, 247: 119108.
doi: 10.1016/j.jclepro.2019.119108
[14] ZHANG H S, YU D, WANG W, et al. Recyclable and highly efficient photocatalytic fabric of Fe (III)@BiVO4/cotton via thiolene click reaction with visible-light response in water[J]. Advanced Powder Technology, 2019, 30(12): 3182-3192.
doi: 10.1016/j.apt.2019.09.027
[15] 娄娅娅, 王静, 董燕超, 等. 粘胶基沸石咪唑骨架材料的制备及其对染料的脱色[J]. 纺织学报, 2021, 42(2): 142-147.
LOU Yaya, WANG Jing, DONG Yanchao, et al. Preparation and decolorization of rayon based zeoliticimidazolate framework functional material[J]. Journal of Textile Research, 2021, 42(2): 142-147.
[1] 费建武, 吕明泽, 刘利伟, 王春红, 韩振邦. 基于双层微纳米纤维膜的气液固三相体系构建及其光催化性能[J]. 纺织学报, 2022, 43(06): 37-43.
[2] 刘锁, 王雅倩, 魏安方, 赵磊, 凤权. 功能化水刺粘胶纤维膜的制备及其在漆酶固定化中的应用[J]. 纺织学报, 2022, 43(05): 124-129.
[3] 谢梦玉, 胡啸林, 李星, 瞿建刚. 还原氧化石墨烯/粘胶多层复合材料的制备及其界面蒸发性能[J]. 纺织学报, 2022, 43(04): 117-123.
[4] 侯倩倩, 李文熙, 赵美华. 光催化条件下棉织物的蓝晒工艺印相[J]. 纺织学报, 2022, 43(04): 110-116.
[5] 徐晓彤, 江振林, 郑钦超, 朱科宇, 王朝生, 柯福佑. 导热结构对聚对苯二甲酸乙二醇酯非等温结晶行为的影响[J]. 纺织学报, 2022, 43(03): 44-49.
[6] 邓杨, 石现兵, 王涛, 刘利伟, 韩振邦. 负载MIL-53(Fe)的改性聚丙烯腈纤维光催化剂的制备及其性能[J]. 纺织学报, 2022, 43(03): 58-63.
[7] 陶旭晨, 李林, 徐珍珍. 杯芳烃/还原氧化石墨烯纤维的制备及其选择性吸附性能[J]. 纺织学报, 2022, 43(03): 64-70.
[8] 魏娜娜, 刘碟, 马政, 焦晨璐. 纤维素/壳聚糖磁性气凝胶的冻融法制备及其对染料吸附性能[J]. 纺织学报, 2022, 43(02): 53-60.
[9] 张梦迪, 张维, 姚继明. 天然黏土矿物在靛蓝染色废水电絮凝中的应用[J]. 纺织学报, 2022, 43(02): 196-201.
[10] 杨腾祥, 申国栋, 钱利江, 胡华军, 毛雪, 孙润军. 外电场极化银-钛酸钡/涤纶织物制备及其光催化性能[J]. 纺织学报, 2022, 43(02): 189-195.
[11] 邹梨花, 杨莉, 兰春桃, 阮芳涛, 徐珍珍. 层层组装氧化石墨烯/聚吡咯涂层棉织物的电磁屏蔽性能[J]. 纺织学报, 2021, 42(12): 111-118.
[12] 施敏慧, 李冰蕊, 王挺, 吴礼光. 高含盐废水中TiO2复合光催化剂光降解甲基橙机制及性能[J]. 纺织学报, 2021, 42(12): 103-110.
[13] 李庆, 陈灵辉, 李丹, 吴志强, 朱炜, 樊增禄. 金属-有机骨架光催化降解染料的研究进展[J]. 纺织学报, 2021, 42(12): 188-195.
[14] 王曙东, 董青, 王可, 马倩. 还原氧化石墨烯增强聚乳酸纳米纤维膜的制备及其性能[J]. 纺织学报, 2021, 42(12): 28-33.
[15] 周园园, 郑煜铭, 吴小琼, 邵再东. 静电纺纳米纤维光催化剂性能增强方法的研究进展[J]. 纺织学报, 2021, 42(11): 179-186.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号　 京公网安备11010502044800号
版权所有 © 2021 《纺织学报》编辑部
地址： 北京市朝阳区延静里中街3号主楼6层《纺织学报》杂志社　邮政编码：100025　
电话：010-65017711,65917740　传真：010-65016539　Email:fangzhixuebao@vip.126.com
本系统由北京玛格泰克科技发展有限公司设计开发