茜草色素对生物基聚酰胺56的染色性能

黄连香1, 王祥荣1,2, 侯学妮1,2(), 钱琴芳3   

  1. 1.苏州大学 纺织与服装工程学院, 江苏 苏州 215006
    2.苏州大学 纺织行业天然染料重点实验室, 江苏 苏州 215123
    3.盛虹集团有限公司, 江苏 苏州 215168
  • 收稿日期:2023-02-13 修回日期:2024-04-11 出版日期:2024-07-15 发布日期:2024-07-15
  • 通讯作者: 侯学妮(1985—),女,高级实验师,博士。主要研究方向为纺织品清洁生产技术及工艺、纺织品测试等。E-mail:houxueni@suda.edu.cn。
  • 作者简介:黄连香(1996—),女,硕士。主要研究方向为纺织品生态染整加工技术。
  • 基金资助:
    江苏省纺织印染节能减排与清洁生产工程中心开放课题项目(SDGC2107)

Dyeing properties of madder pigment on bio-based polyamide 56

HUANG Lianxiang1, WANG Xiangrong1,2, HOU Xueni1,2(), QIAN Qinfang3   

  1. 1. College of Textile and Clothing Engineering, Soochow University, Suzhou, Jiangsu 215006, China
    2. Textile and Apparel Council Key Laboratory of Natural Dyes, Soochow University, Suzhou, Jiangsu 215123, China
    3. Shenghong Group Co., Ltd., Suzhou, Jiangsu 215168, China
  • Received:2023-02-13 Revised:2024-04-11 Published:2024-07-15 Online:2024-07-15

RichHTML

4

PDF (PC)

57

摘要：

为探讨天然染料用于生物基聚酰胺56(PA56)的染色可行性,实现PA56的环保染色工艺,通过单因素实验,以染色后织物K/S值为指标,优化了茜草上染PA56织物的染色工艺条件。采用准一级和准二级动力学模型,研究了茜草上染PA56的染色动力学特性,分析了染液pH值及添加剂对染色动力学参数的影响。结果表明:当染液的pH值为4.2,染色温度为80 ℃时,染色保温40 min后可获得一定染色深度的茜草上染PA56织物;经不同金属离子媒染后,染色织物的色牢度和K/S值均有提高;茜草色素在PA56纤维上的染色吸附过程符合准二级动力学模型,随着染色温度的升高,染料平衡吸附量增加,半染时间缩短,扩散系数增大;在染色中加入元明粉或平平加O,或采用预媒染色,都不会改变茜草上染PA56的准二级动力学特征。

关键词: 天然染料, 茜草色素, 生物基聚酰胺56, 染色, 动力学

Abstract:

Objective Madder pigment is a natural dye of bright red color with stable performance. Bio-based polyamide 56 (PA56)is an environment-friendly and excellent bio-based polyamide material. In this research, madder pigment was adopted to dye PA56 fabrics, the dyeing process was optimized,and the dyeing kinetic mechanism was studied. The research results provide a theoretical basis for the application of madder natural dyes to bio-based PA56 fabrics. Furthermore, applying natural dyes to bio-based materials would meet the requirements of circular economy and low-carbon sustainable development.

Method In order to study the dyeing performance of madder on PA56 fabric, the parameters including pH, dyeing time, dyeing temperature and mass fraction of Peregal O were explored to find the optimal conditions. Through K/S value and color characteristics, the influences of mordants and mordant treatment processes were studied. The optimal conditions obtained were subsequently adopted to study the kinetic of madder pigment dyeing. Pseudo first-order and pseudo second-order kinetic models were adopted to examine the mechanism of the adsorption process. Kinetic parameters of madder pigment dyeing on PA56 fiber with different temperature, pH, auxiliaries and mordant were calculated.

Results The results showed that the optimum process for dyeing bio-based PA56 fabrics with madder pigment was as follows: dyeing pH value is 4.2, dyeing temperature is 80 ℃, dyeing time is 40 min and the amount of Peregal O is 1 g/L. After mordant dyeing, the K/S values of the dyed fabrics were significantly increased, and the color characteristics of dyed fabric changes obviously. Compared with the direct dyed fabric, the color fastness of the mordant dyed fabric has been improved. The kinetics of adsorption for different dye temperatures were evaluated by the pseudo first-order and second-order models. A large equilibrium adsorption density difference between the experiment and calculation was observed for the pseudo first-order model, indicating a poor pseudo first-order fit to the experimental data. The experimental data fitted well to the pseudo second-order kinetic model with high correlation coefficient above 0.999. In addition, the C∞ agreed well with both experiment and calculation, suggesting that the second-order kinetic model well describes the adsorption of madder pigment onto PA56 fiber. The half-dyeing time decreased,and the diffusion coefficient increased with increasing temperature. The influences of dyeing pH, auxiliaries and mordant on the dyeing kinetic parameters were further analyzed. With the increase of pH value, the equilibrium adsorption amount decreased, the half-dyeing time was shortened,and the diffusion coefficient was increased. The addition of sodium sulfate and Peregal O reduced the equilibrium dyeing amount and the half-dyeing time of maddering dye. The rate constant (k2) and the diffusion coefficient were increased with the addition of sodium sulfate and Peregal O. After mordant dyeing, the equilibrium adsorption amount was decreased, the half-dyeing time increased and the diffusion coefficient decreased, but K/S values of the dyed fabrics were increased.

Conclusion The optimal conditions and dyed fabric with darker color of bio-based PA56 dyed with madder pigment were obtained. The type and mode of mordant can enrich the color tone and improve the color fastness. Fitting calculations reveal that the dyeing process of madder pigment dyeing on bio-based PA56 fabrics conforms to the pseudo second order kinetic model. Madder has a fast adsorption rate on PA56 fabric. The adsorption capacity was dependent with pH value. The addition of sodium sulfate and Peregal O, as well as the pretreatment with mordant, the dyeing processes also conform to the quasi-second order kinetic model.

Key words: natural dye, madder pigment, bio-based polyamide 56, dyeing, kinetics

中图分类号: 

  • TS193.2

图1

染色pH值、温度和时间对茜草上染PA56织物K/S值的影响"

表1

平平加O质量浓度对茜草上染PA56织物K/S值的影响"

平平加O质量浓度/
(g·L-1)		 K/S值 Sλ λmax/nm
0.5 2.12 0.024 400
1.0 2.14 0.020 400
1.5 2.05 0.018 400
2.0 2.05 0.017 400

图2

媒染对茜草色素上染PA56织物K/S值的影响"

表2

媒染处理对茜草色素染PA56织物颜色特征的影响"

染色
方式		 L* a* b* C* h/
(°)		 λmax/
nm		 K/S值
直接染色 55.76 8.32 3.21 8.92 21.09 400 1.76
硫酸铝
预媒染		 50.20 28.80 10.50 30.66 20.03 510 3.56
硫酸铝
同浴媒染		 49.07 38.33 1.37 38.36 2.05 510 4.39
硫酸铝
后媒染		 50.80 28.02 12.10 30.52 23.37 510 3.12
硫酸铝
预媒染		 31.55 6.66 -9.51 11.62 305.01 560 7.54
硫酸亚铁
同浴媒染		 43.16 11.33 14.47 18.38 308.06 560 3.57
硫酸亚铁
后媒染		 36.25 5.90 -5.87 8.32 315.12 560 5.26

表3

媒染对茜草色素染PA56织物色牢度的影响"

染色方式 耐光
色牢度		 耐皂洗色牢度 耐摩擦色牢度
变色 棉沾 锦沾 干 湿
硫酸铝预媒染 4 4 4~5 4~5 4 3~4
硫酸铝同浴媒染 4 4 4~5 4~5 4 3~4
硫酸铝后媒染 3 4 4~5 4~5 4 4
硫酸亚铁预染媒 4 4 4~5 4~5 4 4
硫酸亚铁同浴媒染 3 4 4~5 4~5 4 3~4
硫酸亚铁后媒染 4 4 4~5 4~5 4 4
直接染色 2 3 4~5 4~5 4 4

图3

茜草色素质量浓度与吸光度的关系拟合曲线"

图4

不同温度下茜草色素上染PA56纤维的吸附曲线"

图5

不同温度下茜草色素上染PA56纤维的准一级和准二级动力学方程拟合曲线"

表4

不同温度下茜草色素上染PA56纤维的准一级和准二级动力学参数"

温度/℃ 准一级动力学参数 准二级动力学参数
回归方程 R2 C∞,exp/
(mg·g-1)		 C∞, cal/
(mg·g-1)		 k1/
min-1		 回归方程 R2 C∞,exp/
(mg·g-1)		 C∞, cal/
(mg·g-1)		 k2/
(g ·mg-1 ·min-1)
60 y=-0.033x+1.626 0.815 16.81 5.09 0.03 y=0.058x+0.132 0.999 16.81 17.39 0.03
70 y=-0.031x+0.956 0.666 16.99 2.61 0.03 y=0.058x+0.055 0.999 16.99 17.21 0.06
80 y=-0.040x+1.000 0.779 17.35 2.72 0.04 y=0.057x+0.044 0.999 17.35 17.57 0.07

表5

茜草色素上染PA56纤维的半染时间和扩散系数"

温度/℃ 半染时间t1/2/min 扩散系数D/(m2·min-1)
60 2.30 1.60 × 10-12
70 0.95 3.88 × 10-12
80 0.77 4.77 × 10-12

图6

不同pH下茜草色素上染PA56纤维的吸附曲线和准二级动力学拟合曲线"

表6

不同pH值下茜草色素上染PA56纤维的准二级动力学参数"

pH值 回归方程 R2 C∞,exp/
(mg·g-1)		 C∞, cal/
(mg·g-1)		 k2/
(g ·mg-1 ·min-1)		 t1/2/min D/
(m2·min-1)
3.2 y=0.058x+0.084 0.999 17.05 17.24 0.04 1.44 2.55×10-12
4.2 y=0.057x+0.044 0.999 17.35 17.54 0.07 0.77 3.09×10-12
5.2 y=0.062x+0.045 0.999 15.83 16.05 0.09 0.72 4.78×10-12
6.2 y=0.087x+0.058 0.999 11.49 11.52 0.13 0.67 5.10×10-12

图7

不同助剂时茜草色素上染PA56纤维的吸附曲线和准二级动力学拟合曲线"

表7

助剂对茜草色素上染PA56纤维的准二级动力学参数的影响"

助剂 回归方程 R2 C∞,exp/
(mg·g-1)		 C∞, cal/
(mg·g-1)		 k2/
(g ·mg-1 ·min-1)		 t1/2/
min		 D/
(m2·min-1)		 K/S值 λmax/
nm
无助剂 y=0.057+0.044 0.999 17.35 17.54 0.07 0.77 4.78×10-12 2.24 400
元明粉 y=0.068x+0.026 0.999 14.33 14.68 0.18 0.38 9.66×10-12 2.17 400
平平加O y=0.081x+0.058 0.999 12.28 12.38 0.11 0.72 5.13 2.14×10-12 400

图8

媒染剂对茜草色素上染PA56吸附曲线的影响"

图9

媒染剂对茜草色素上染PA56的准二级动力学拟合曲线"

表8

媒染剂对茜草色素上染PA56纤维的准二级动力学参数的影响"

媒染剂 回归方程 R2 C∞,exp/
(mg·g-1)		 C∞, cal/
(mg·g-1)		 k2/
(g ·mg-1 ·min-1)		 t1/2/
min		 D/
(m2·min-1)		 K/S值 λmax/
nm
直接染色 y=0.057x+0.044 0.999 17.35 17.54 0.07 0.77 4.78×10-12 1.76 400
硫酸铝预媒染 y=0.080x+0.079 0.999 12.29 12.47 0.08 0.96 3.74×10-12 3.56 510
硫酸亚铁预媒染 y=0.065x+0.117 0.999 15.31 15.34 0.04 1.79 2.06×10-12 7.54 560
[1] 陈荣圻. 天然染料及其染色[J]. 染整技术, 2016, 38(4): 47-51.
CHEN Rongqi. Natural dyes and the dyeing[J]. Textile Dyeing and Finishing Journal, 2016, 38(4): 47-51.
[2] RATHER L J, AKHTER S, PADDER R A, et al. Colorful and semi durable antioxidant finish of woolen yarn with tannin rich extract of acacia nilotica natural dye[J]. Dyes and Pigments, 2017,139:812-819.
[3] 宋慧君, 翟亚丽, 钞意元, 等. 蚕丝织物的栀子蓝色素染色[J]. 纺织学报, 2020, 41(6): 81-85.
SONG Huijun, ZHAI Yali, CHAO Yiyuan, et al. Silk fabric dyed with gardenia blue pigment[J]. Journal of Textile Research, 2020, 41(6): 81-85.
[4] HOSSAIN S, JALIL M A, KAMAL S A B, et al. A natural dye extracted from the leaves of Mimusops elengi linn and its dyeing properties on cotton and silk fabrics[J]. Journal of The Textile Institute, 2021, 112(3): 455-461.
[5] 刘建平. 广玉兰叶色素染色阳离子改性棉布的抗紫外线性能[J]. 印染, 2021, 47(5):44-46.
LIU Jianping. UV resistance of cationic modified cotton fabric dyed with colorants from Magnolia grandiflora leaves[J]. China Dyeing & Finishing, 2021, 47(5):44-46.
[6] 任燕飞, 巩继贤, 张健飞, 等. 茶色素染液pH值对羊毛织物染色效果及抗菌性能的影响[J]. 纺织学报, 2016, 37(11): 86-91.
REN Yanfei, GONG Jixian, ZHANG Jianfei, et al. Influence of dye solution pH value on dyeing effects and antibacterial properties of wool fabrics dyed with tea natural dye[J]. Journal of Textile Research, 2016, 37(11): 86-91.
[7] 刘艳春, 白刚. 小檗碱在聚丙烯腈/醋酸纤维素复合纤维染色中的应用[J]. 纺织学报, 2020, 41(5):94-98,104.
LIU Yanchun, BAI Gang. Application of berberine in polyacrylonitrile/cellulose acetate composite fiber dyeing[J]. Journal of Textile Research, 2020, 41(5):94-98, 104.
[8] PANDEY R, PATEL S, PANDIT P, et al. Colouration of textiles using roasted peanut skin: an agro processing residue[J]. Journal of Cleaner Production, 2018, 172(20): 1319-1326.
[9] BLACKBURN, RICHARD S. Natural dyes in madder (Rubia spp.) and their extraction and analysis in historical textiles[J]. Coloration Technology, 2017, 133(6):449-462.
[10] MEHRPARVAR L S. SAFAPOUR M. SADEGHI K, et al. A cleaner and eco-benign process for wool dyeing with madder, Rubia tinctorum L, root natural dye[J]. International Journal of Environmental Science and Technology, 2016, 13(11):2569-2578.
[11] 齐迪, 丁洪, 王祥荣. 羟基茜草素络合染料对羊毛的染色性能[J]. 印染, 2022, 48(6):23-27.
QI Di, DING Hong, WANG Xiangrong. Dyeing properties of wool with purpurin complex dyes[J]. China Dyeing & Finishing, 2022, 48(6):23-27.
[12] 张驰, 王祥荣. 茜草色素在真丝织物上染色性能的研究[J]. 丝绸, 2020, 57(1):9-13.
ZHANG Chi, WANG Xiangrong. Study on dyeing property of madder pigment on silk fabrics[J]. Journal of Silk, 2020, 57(1):9-13.
[13] YUSUF, FAQEER M, SHAHID M, et al. Eco-dyeing of wool with Rubia cordifolia root extract: assessment of the effect of Acacia catechu as biomordant on color and fastness properties[J]. Textiles and Clothing Sustainability, 2016,2:10.
[14] 张彦博. 生物基PA56织物的染色性能研究及风格评价[D]. 苏州: 苏州大学, 2022:3-9.
ZHANG Yanbo. Study on dyeing properties of PA56 and evaluation of its fabric style[D]. Suzhou: Soochow University, 2022:3-9.
[15] 孙朝续, 刘修才. 生物基聚酰胺56纤维在纺织领域的应用研究进展[J]. 纺织学报, 2021, 42(4): 26-32.
SUN Chaoxu, LIU Xiucai. Research progress on applications of bio-based polyamide 56 fibers in textile fields[J]. Journal of Textile Research, 2021, 42 (4):26-32.
[16] 杨婷婷, 高远博, 郑毅, 等. 生物基聚酰胺56纤维的热降解动力学及其热解产物[J]. 纺织学报, 2021, 42(4): 1-7.
YANG Tingting, GAO Yuanbo, ZHENG Yi, et al. Thermal degradation kinetics and pyrolysis products of bio-based polyamide 56 fiber[J]. Journal of Textile Research, 2021, 42(4): 1-7.
[17] YANG T T, GAO Y B, WANG X L, et al. Hydrogen bonding and crystalline structure of bio-based PA56[J]. Polymer, 2021. DOI:10.1016/j.polymer.2021.124356.
[18] 李蒙蒙. 生物基纤维PA56的染色性能及功能整理研究[D]. 上海: 东华大学, 2017:3-7.
LI Mengmeng. Research on dyeing properties and functional finishing of bio-based fiber PA56[D]. Shanghai: Donghua University, 2017:3-7.
[19] 郝新敏, 李岳玲, 王建明, 等. 锦纶纤维酸性染料染色动力学对比研究[J]. 纺织学报, 2015, 36(2): 77-80, 97.
HAO Xinmin, LI Yueling, WANG Jianming, et al. Study on acid dyestuff dyeing kinetics of polyamide 56 fiber compared with polyamide 6 and 66[J]. Journal of Textile Research, 2015, 36(2): 77-80, 97.
[20] 王建明, 李永峰, 郝新敏, 等. 生物基锦纶56和锦纶66的结构与吸放湿性能评价[J]. 纺织学报, 2021, 42(8): 1-7.
WANG Jianming, LI Yongfeng, HAO Xinmin, et al. Study on structure and moisture absorption and liberation properties of bio-based polyamide 56 and polyamide 66[J]. Journal of Textile Research, 2021, 42(8): 1-7.
[21] 郝新敏, 郭亚飞, 张长琦, 等. 生物基锦56与锦纶66性能对比研究[J]. 针织工业, 2018 (9): 1-5.
HAO Xinmin, GUO Yafei, ZHANG Changqi, et al. Comparative evaluation on application performance of bio-based polyamide 56 and polyamide 66[J]. Knitting Industries, 2018 (9): 1-5.
[22] 胡传国, 刘宏东, 李蒙蒙, 等. 弱酸性染料在生物基纤维PA56上的染色理论研究[J]. 印染, 2021, 47(7): 11-15, 20.
HU Chuanguo, LIU Hongdong, LI Mengmeng, et al. Dyeing theory of weak acid dyes on bio-based fiber PA56[J]. China Dyeing & Finishing, 47(7):11-15,20.
[23] 张彦博, 徐真真, 楚润善, 等. 生物基PA56织物的酸性染料染色[J]. 印染, 2021, 47(11):5-8.
ZHANG Yanbo, XU Zhenzhen, CHU Runshan, et al. Dyeing process of bio-based PA56 fabric with acid dyes[J]. China Dyeing & Finishing, 2021, 47(11):5-8.
[24] 马雪松, 高艺, 陈英, 等. 生物基尼龙PA56的活性染料染色性能[J]. 印染, 2019, 45(18):9-13,29.
MA Xuesong, GAO Yi, CHEN Ying, et al. Dyeing performance of bio-based nylon PA56 with reactive dyes[J]. China Dyeing & Finishing, 2019, 45(18): 9-13, 29.
[25] 曹诗慧, 李宏伟, 郝新敏. 生物基尼龙56织物的还原染料染色[J]. 印染, 2019, 45(24):31-34.
CAO Shihui, LI Hongwei, HAO Xinmin. Dyeing process of bio-based PA56 fabric with vat dyes[J]. China Dyeing & Finishing, 2019, 45(24):31-34.
[26] 黄连香. 天然染料对锦纶织物的染色性能研究[D]. 苏州: 苏州大学,2022:3-10.
HUANG Lianxiang. Study on dyeing properties of nylon fabric with natural dyes[D]. Suzhou: Soochow University, 2022:3-10.
[27] 王成龙, 李立新, 吴绍明, 等. 染色促进剂对聚丁二酸丁二醇酯纤维分散染料染色动力学和热力学的影响[J]. 纺织学报, 2022, 43(1):147-152.
WANG Chenglong, LI Lixin, WU Shaoming, et al. Effect of dyeing promoter on dyeing kinetics and thermodynamics of polybutylene succinate fiber dyeing with disperse dye[J]. Journal of Textile Research, 2022, 43(1):147-152.
[28] 柴丽琴, 邵建中, 周岚, 等. 栀子黄在棉织物上的染色动力学研究[J]. 纺织学报, 2010, 31(9):56-61.
CHAI Liqin, SHAO Jianzhong, ZHOU Lan, et al. Dyeing kinetics of Gardenia Yellow on cotton[J]. Journal of Textile Research, 2010, 31(9):56-61.
[29] 张驰. 茜草色素对真丝织物的染色和印花工艺研究[D]. 苏州: 苏州大学, 2020:25-26.
ZHANG Chi. Study on dyeing and printing properties of silk fabrics with madder[D]. Suzhou: Soochow University, 2020:25-26.
[30] 李凤艳, 杨巧芬, 洪彩虹, 等. 天然茶色素对棉纤维的铁离子媒染染色[J]. 纺织学报, 2010, 31(7):60-63,68.
LI Fengyan, YANG Qiaofen, HONG Caihong, et al. Natural tea pigment dyeing of cotton fibers with Fe2+ as a mordanting agent[J]. Journal of Textile Research, 2010, 31(7):60-63,68.
[31] 蔡苏英, 曹红梅. 金属离子媒染对天然染料色光的影响[J]. 针织工业, 2009(7):3.
CAI Suying, CAO Hongmei. The influence of the metallic ionic mordant on the color cast of the natural dyes[J]. Knitting Industries, 2009(7):3.
[1] 武守营, 黄启超, 张开封, 张琳萍, 钟毅, 徐红, 毛志平. 铁-三联吡啶配合物活化高碘酸盐体系构建及其对染色废水的催化降解机制[J]. 纺织学报, 2024, 45(06): 105-112.
[2] 袁野, 张安莹, 魏丽菲, 高建伟, 陈咏, 王锐. 含磷阻燃聚酯的合成动力学及其性能[J]. 纺织学报, 2024, 45(04): 50-58.
[3] 李丽丽, 袁亮, 唐雨霞, 杨文菊, 王浩. 聚多巴胺/壳聚糖改性棉织物的茶色素染色及其抗菌和防紫外线性能[J]. 纺织学报, 2024, 45(03): 106-113.
[4] 杨美慧, 李博, 沈艳琴, 武海良. 再生角蛋白凝胶对纺织退浆废水中浆料分子的吸附性能[J]. 纺织学报, 2024, 45(02): 142-152.
[5] 许高平, 孙以泽. 移动机械臂牵引卷装纱线的动态建模与控制[J]. 纺织学报, 2024, 45(01): 1-11.
[6] 常辰玉, 王雨薇, 原旭阳, 刘锋, 卢致文. 基于交织点改进弹簧-质点模型的纬编针织物动态变形模拟[J]. 纺织学报, 2024, 45(01): 99-105.
[7] 寿晨超, 娜仁高娃, 高素芸, 刘剑, 赵丰. 天然染料质谱数据库的建立与应用[J]. 纺织学报, 2023, 44(11): 120-131.
[8] 刘金儒, 李新荣, 王浩, 师帅星. 棉精梳机分离罗拉混合驱动系统优化[J]. 纺织学报, 2023, 44(11): 190-198.
[9] 姜绍华, 梁帅童, 裴刘军, 张红娟, 王际平. 基于概率密度函数的织物染色侵入动力学分析[J]. 纺织学报, 2023, 44(10): 90-97.
[10] 梁志结, 罗正智, 程海兵, 贾维妮, 毛庆辉. 多钒酸盐催化氧化咖啡酸及其对羊毛织物的原位染色性能[J]. 纺织学报, 2023, 44(10): 98-103.
[11] 冯清国, 巫鳌飞, 任家智, 陈宇恒. 棉纺精梳机分离罗拉连杆驱动机构动力学仿真及有限元分析[J]. 纺织学报, 2023, 44(09): 197-204.
[12] 连丹丹, 王镭, 杨雅茹, 尹立新, 葛超, 卢建军. 服用聚苯硫醚纤维的制备及其性能[J]. 纺织学报, 2023, 44(08): 1-8.
[13] 韩博, 王玉霖, 舒大武, 王涛, 安芳芳, 单巨川. 活性染料染色废水的循环染色[J]. 纺织学报, 2023, 44(08): 151-157.
[14] 邵彦峥, 孙将皓, 魏春艳, 吕丽华. 棉秆皮微晶纤维素/改性壳聚糖吸附纤维制备与性能[J]. 纺织学报, 2023, 44(08): 18-25.
[15] 尚小愉, 朱坚, 王滢, 张先明, 陈文兴. 侧基含磷阻燃共聚酯的制备及其固相增黏反应[J]. 纺织学报, 2023, 44(07): 1-9.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号　 京公网安备11010502044800号
版权所有 © 2021 《纺织学报》编辑部
地址： 北京市朝阳区延静里中街3号主楼6层《纺织学报》杂志社　邮政编码：100025　
电话：010-65017711,65917740　传真：010-65016539　Email:fangzhixuebao@vip.126.com
本系统由北京玛格泰克科技发展有限公司设计开发