JOURNAL OF TEXTILE RESEARCH ›› 2017, Vol. 38 ›› Issue (09): 1-7.doi: 10.13475/j.fzxb.20170304907

    Next Articles

Preparation and properties of non-water soluble natural pigment dope-dyed alginate fiber

  

  • Received:2017-03-23 Revised:2017-05-11 Online:2017-09-15 Published:2017-09-20

Abstract:

On account of the dissol ution loss of colorant in natural dyes coloring alginate fiber during wet spinning, copper chlorophyll (CHl-Cu) was used as colorant and sodium alginate dilute solution was used as organic grind auxiliary agent dispersant, dope dyeing spinning solution and alginate fiber were prepared. Properties of coloring spinning solution was characterized by infrared spectroscope, rotary rheometer and transmission electron microscope. The morphology of dyed alginate fiber was observed by scanning electron microscope, and water resistante migration and flame-retardany of fibers were tested. The results show stability of dyed spinning solution is the best when the Chl-Cu content is under 6%, and the Chl-Cu can be distributed evenly with a diameter imaller than 20 nm. The agglomeration of Chl-Cu nano particles are successfully eliminated, on account of Cu2+ cross-linking structure between Chl-Cu nano-particles and SA, Chl-Cu can be ground successful and dispersed stably. Chl-Cu colorant has good water resistant migration, and does not change the fiber surface. The dote-dyed alginate fiber has a prefect flame retardancy, and the limiting oxygen index is above 39%.

Key words: natural pigment, copper chlorophyll, dope dyeing, alginate fiber, spinning solution, nano particle

[1] . Bioactivities and applications of alginate fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(04): 175-180.
[2] . Preparation and properties of carbon black/Lyocell cellulose membrane [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(03): 28-32.
[3] . Microorganisms pigments and application thereof in textile dyeing [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(08): 165-170.
[4] Qin Yimin. Application of gelling fibers in functional wound dressings [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(6): 163-0.
[5] . Current status and development trend of application of alginate fiber [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(2): 145-0.
[6] . Preparation and properties of nanoscale carbon black for dope dyeing of polyacrylonitrile fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(11): 19-0.
[7] Qin Yimin;CAI Liling;ZHU Changjun. Antimicrobial properties of zinc alginate fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2011, 32(2): 18-20.
[8] Qin Yimin;CHEN Jie. Absorption and release of zinc ions by alginate fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2011, 32(1): 16-19.
[9] Hou Xiuliang;Zhao Kuan;Zhao Guoying ;Li Zhaonan;Hu Xiaofeng . Method of dyeing green color wool fabric with sodium copper chlorophyll [J]. JOURNAL OF TEXTILE RESEARCH, 2010, 31(6): 95-99.
[10] QIN Yimin;ZHU Changjun;FENG Deming;ZHOU Juan;WANG Panpan. Comparison of the properties of calcium alginate wound dressing and cotton gauze [J]. JOURNAL OF TEXTILE RESEARCH, 2007, 28(3): 45-48.
[11] QIN Yimin. Preparation methods and properties of silver-contained alginate fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2007, 28(2): 126-128.
[12] QIN Yi-min. Comparative study of the properties of alginate and chitosan fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2006, 27(1): 111-113.
[13] QIN Yi-min . Absorption mechanism analysis about alginate wound dressings [J]. JOURNAL OF TEXTILE RESEARCH, 2005, 26(1): 113-115.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!