Preparation and adsorption kinetics of calixarene fibers with selective adsorption of Pt(IV)

TAO Xuchen(), LI Lin   

  1. College of Textiles and Clothing, Anhui Polytechnic University, Wuhu, Anhui 241000, China
  • Received:2018-04-08 Revised:2018-12-02 Online:2019-03-15 Published:2019-03-15

Abstract:

In order to prepare novel selective adsorption fibers containing calixarene, calixarene polyamide acid (CPAA) fibers were firstly prepared by amidating and electrospinning. Subsequently, the calixarene polyimide (CPI) fibers were obtained by thermal imidization of the CPAA fibers. The CPI and CPAA fibers were characterized by Fourier transform infrared spectrometer, scanning electron microscope and thermogravimetric analysis. The adsorption selectivity and adsorption kinetics of the CPI fibers were also investigated. The results show that calixarene is successfully incorporated into the CPAA and CPI fibers. The CPI fibers possess smaller diameter and higher thermal degradation temperatur by comparison with the CPAA fibers. Only the CPI fibers can adsorb Pt(IV) selectively from the mixture of Pt(IV) and Ag(I). The maximum Pt(IV) absorption capacity of CPI fibers is 28 mg/g at pH 7, and its adsorption behavior fits well with the first-order adsorption kinetics model. The adsorption rate constant is 0.003 9 min-1 at 20 ℃ and increases with the elevating adsorption temperature. The required activation energy for adsorption is only 12.24 kJ/mol, which indicates the CPI fibers adsorbing Pt(IV) is easy to occur.

Key words: calixarene fiber, polyimide, selective adsorption, adsorption kinetics

CLC Number: 

  • TQ342

Fig.1

Preparation process of CPI fibers"

Fig.2

SEM images of CPAA(a)and CPI(b)fibers(×5 000)"

Fig.3

FT-IR spectra of CPAA and CPI fibers"

Fig.4

TG curves of CPAA and CPI fibers"

Fig.5

Adsorption of Pt(IV) and Ag(Ⅰ) on common PI, CPAA and CPI fibers"

Fig.6

Adsorption kinetics curves of Pt(Ⅳ) on CPI fibers"

Fig.7

Relationship between lg (-dc0/dt) and lgc0"

Fig.8

Relationship between lnct and t at various temperatures"

Fig.9

Relationship between lnk and 1/T"

[1] WANG J J, LI J, WEI J. Adsorption characteristics of noble metal ions onto modified straw bearing amine and thiol groups[J]. Journal of Materials Chemistry A, 2015,35(3):18163-18170.
[2] ERMAKOVA T G, SHAULINA L P, KUZNETSOVA N P, et al. Sorption recovery of noble metal ions with a copolymer of 1-vinyl-1,2,4-triazole with acrylo-nitrile[J]. Russian Journal of Applied Chemistry, 2012,85(8):1289-1295.
doi: 10.1134/S1070427212080253
[3] BRAY D J, CLEGG J K, WENZEL M, et al. Selective solvent extraction of silver(I) by tris-pyridyl tripodal ligands and X-ray structure of a silver(I) coordination polymer incorporating one such ligand[J]. Australian Journal of Chemistry, 2015,68(4):549-554.
doi: 10.1071/CH14540
[4] ALI S A, KAZI I W, ULLAH N. New chelating ion-exchange resin synthesized via the cyclopolymerization protocol and its uptake performance for metal ion removal[J]. Industrial and Engineering Chemistry Research, 2015,54(40):9689-9698.
doi: 10.1021/acs.iecr.5b02267
[5] RIVAS B L, POOLEY S A, PEREIRA E, et al. Water-soluble polymer materials as complexing reagents for the separation of metal ions using membrane filtration[J]. Polymers for Advanced Technologies, 2006,17(11/12):671-684.
[6] 凤权, 王清清, 魏取福, 等. Cd2+-PVA/PA6金属配合纳米纤维的制备及反应动力学分析 [J]. 纺织学报, 2012,33(3):5-8.
FENG Quan, WANG Qingqing, WEI Qufu, et al. Preparation of Cd2+-PVA/PA6 metal chelated nanofibers and analysis of reaction kinetics [J]. Journal of Textile Research, 2012,33(3):5-8.
[7] DENG S, ZHANG G S, WANG X, et al. Preparation and performance of polyacrylonitrile fiber functionalized with iminodiacetic acid under microwave irradiation for adsorption of Cu(II) and Hg(II)[J]. Chemical Engineering Journal, 2015,276:349-357.
doi: 10.1016/j.cej.2015.04.043
[8] FONG H, CHUN I, RENEKER D H. Beaded nanofibers formed during electrospinning[J]. Polymer, 1999,40(16):4585-4592.
doi: 10.1016/S0032-3861(99)00068-3
[9] CHASE G G, VARABHAS J S, RENEKER D H. New methods to electrospin nanofibers[J]. Journal of Engineered Fibers and Fabrics, 2011,6(3):32-38.
[10] TAO X C, LI L, HE J X. Synjournal of bis-substituted calix[4]arenes and mechanism of substituents effect on K+ and Hg2+ ions transports through liquid mem-brane[J]. Journal of Donghua University (English Edition), 2011,28(6):621-623.
[11] TAO X C, LI L. Synjournal and transport of K+ ions of mono-substituted calix[4]arenes[J]. Advanced Materials Research, 2012,441:392-397.
doi: 10.4028/www.scientific.net/AMR.441
[12] TAO X C, HE J X. Synjournal of calix [4] arene thia derivative and extraction effect of substituents on mercury (Ⅱ) and lead (Ⅱ)[J]. Journal of Donghua University (English Edition), 2017,34(1):49-52.
[13] CHEN M, WANG C J, FANG W, et al. Electrospinning of calixarene functionalized polyacrylonitrile nanofiber membranes and application as an adsorbent and catalyst support[J]. Langmuir, 2013,29(38):126-127.
[14] 刁国旺, 张旺, 房伟, 等. 一种杯芳烃聚丙烯腈复合纳米纤维的制备方法:102358962A[P]. 2012-02-22.
DIAO Guowang, ZHANG Wang, FANG Wei, et al. A preparation method of calixarene polyacrylonitrile composite nanofibers: 102358962A[P]. 2012-02-22.
[15] LIN S, WEI W, WU X H, et al. Selective recovery of Pd(II) from extremely acidic solution using ion-imprinted chitosan fiber: adsorption performance and mechanisms[J]. Journal of Hazardous Materials, 2015,299(6):10-17.
doi: 10.1016/j.jhazmat.2015.05.050
[16] 陶庭先, 吴之传, 孙志娟. 偕胺肟基纤维对Ni2+的吸附动力学[J]. 华南理工大学学报, 2003,31(9):53-56.
TAO Tingxian, WU Zhichuan, SUN Zhijuan. Kinetics of adsorption of nickel (Ⅱ) ion on fibre containing amidoxime groups[J]. Journal of South China University of Technology, 2003,31(9):53-56.
[17] 李松林, 周亚平, 刘俊吉 .物理化学: 下册[M].5版. 北京: 高等教育出版社, 2009: 517, 529.
LI Songlin, ZHOU Yaping, LIU Junji. Physical Chemistry: Volume 2[M]. 5th ed. Beijing: Higer Education Press, 2009: 517, 529.
[18] LI X J, WANG X, WANG Q Q, et al. Effects of imidization temperature on the structure and properties of electrospun polyimide nanofibers[J]. Journal of Engineered Fibers and Fabrics, 2014,9(4):33-38.
[19] 董世华, 胡运华. 冠醚聚合物的研究Ⅱ:以聚硫醚为主链的硫杂冠醚聚合物的合成及其络合性能[J]. 高分子学报, 1990,1(4):399-405.
DONG Shihua, HU Yunhua. Studies on polymeric crown ethers Ⅱ: syntheses and complexation properties of polymeric thiacrown ethers with polythiaether back-bone[J]. Acta Polymerica Sinica, 1990,1(4):399-405.
[20] 李书干, 焦晓宁. 聚酰亚胺针刺织物与聚苯硫醚针刺物的热稳定性与燃烧性能对比[J]. 纺织学报, 2012,33(12):35-39.
LI Shugan, JIAO Xiaoning. Comparison of thermal stability and combustibility between PI and PPS needle punched fabrics[J]. Journal of Textile Research, 2012,33(12):35-39.
doi: 10.1177/004051756303300105
[21] 孔敏荣. 电荷半径比在无机化学中的应用[J]. 北京师范学院学报(自然科学版), 1992(1):65-68.
KONG Minrong. Some application of charge-radius ratio in inorganic chemistry[J]. Journal of Beijing Teachers College (Natural Sciences Edition), 1992(1):65-68.
[22] 关勇, 孔繁荣. 半径比在无机化学中的某些应用[J]. 北京农学院学报, 1994(2):120-124.
GUAN Yong, KONG Fanrong. Some applications of charge-radius ratio in inorganic chemistry[J]. Journal of Beijing Agricultural College, 1994(2):120-124.
[23] 凤权, 武丁胜, 桓珊, 等. AOPAN/RC纳米纤维膜的制备及对金属离子吸附性能[J]. 高分子材料科学与工程, 2017,33(8):140-144.
FENG Quan, WU Dingsheng, HUAN Shan, et al. Preparation and metal ion adsorption properties of AOPAN/RC nanofibrous membrane[J]. Polymer Materials Science and Engineering, 2017,33(8):140-144.
[1] CHEN Lifu, YU Weidong. Stab resistance of composites with synthetic diamond filled polyimide resin matrix [J]. Journal of Textile Research, 2020, 41(05): 38-44.
[2] DU Xiaodong, LIN Fangbing, JIANG Jinhua, CHEN Nanliang, LIU Yanping. Influence of oxygen plasma modification on surface properties of polyimide fiber [J]. Journal of Textile Research, 2019, 40(09): 22-27.
[3] . High-performance polyimide fiber and its weavability [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(05): 14-19.
[4] . Surface modification of polyimide fabric by carboxylation [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(03): 103-107.
[5] . Thermal properties of polyimide fiber fabrics for textiles [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(08): 62-67.
[6] . Fabrication and selective adsorption on Pt(Ⅳ)of calixarene electrospun fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(03): 13-17.
[7] . Dyeing kinetics and thermodynamics of sorghum husk colorant onto wool fabric [J]. Journal of Textile Research, 2015, 36(03): 70-75.
[8] . Adsorption kinetics of reactive dye onto modified palm fiber activated carbon [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(5): 72-0.
[9] . Acceleration of dioctyl dimethyl ammonium bromide to reactive dyeing of silk [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(12): 60-0.
[10] YIN Chao-Qing, XU Yuan, ZHANG Qing-Hua. Polyimide fiber and its flame retardance [J]. JOURNAL OF TEXTILE RESEARCH, 2012, 33(6): 116-120.
[11] LI Wen-Tao, YAO Shu-Huan, PENG Shu-Ping, WU Meng, ZHANG Chao-Bo, ZHANG Zai-Xing. Thermal oxidizing aging properties of modified aromatic polyoxadiazoles fiber [J]. JOURNAL OF TEXTILE RESEARCH, 2012, 33(6): 151-154.
[12] WANG Yu-Huan, WANG Jian-Qing, ZHANG Yu, CAO Dian-Yuan, LI Rong. Study on adsorption thermodynamics and kinetics of thermal-modified attapulgite clay [J]. JOURNAL OF TEXTILE RESEARCH, 2012, 33(5): 95-100.
[13] .  Comparison of thermal stability and combustibility obetween PI and PPS needle punched fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2012, 33(12): 35-39.
[14] . Research on high-performance Polyimide/PTFE compound filtering media coated by foaming [J]. JOURNAL OF TEXTILE RESEARCH, 2011, 32(4): 29-32.
[15] XU Chaowu~;ZHU Xinsheng~. Adsorptivity of superfine sodium polystyrene sulfonate particles [J]. JOURNAL OF TEXTILE RESEARCH, 2008, 29(10): 21-24.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!