Journal of Textile Research ›› 2019, Vol. 40 ›› Issue (05): 91-96.doi: 10.13475/j.fzxb.20180603906

• Dyeing and Finishing & Chemicals • Previous Articles     Next Articles

De-curling control of single-weft knitted fabric in open width pad-steam dyeing

MA Zhenping1,2, MAO Zhiping1,2,3, ZHONG Yi1,2,3, XU Hong1,2,3()   

  1. 1. Key Laboratory of Science & Technology of Eco-Textiles, Ministry of Education, Donghua University, Shanghai 201620, China
    2. College of Chemistry, Chemical Engineering and Biotechnology, Donghua University, Shanghai 201620, China
    3. Innovation Center for Textile Science and Technology, Donghua University, Shanghai 201620, China
  • Received:2018-06-11 Revised:2019-01-10 Online:2019-05-15 Published:2019-05-21
  • Contact: XU Hong E-mail:hxu@dhu.edu.cn

RichHTML

2

PDF (PC)

43

Abstract:

The edges of single-weft knitted fabric was treated with paste to prevent the edges from curling during the open width pad-steam dyeing process. The sizing agents and their coating applied ways were optimized by comparing the curling rates and washing durability during open-width wet processing. As a result, the polyacrylate-polyurethane was used as a sizing agent. The suitable processes for medium weight and thick knitted fabric are as follows: the serrated coating is applied along the grain direction on the reverse side of fabrics, and the thickness of the coating reaches 0.2 mm. The width of the coating is no less than 2 cm. The results show that the method can effectively control the curling of the knitted fabric in the open width pad-steam dyeing process and has no effect on the dyeing performance.

Key words: open width dyeing, single-weft knitted fabric, polyacrylate-polyurethane, curling, washing durability

CLC Number: 

  • TS181.8

Tab.1

Different anti-curling coating states under different dyeing conditions"

硬挺剂种类 卷边率C/%
浆边烘干 浸轧染液 汽蒸 皂煮 烘干
聚氨酯 0 9.05 0 16.03 12.06
F-404 0 2.03 0 11.44 15.88
EcofunYTJ 0 4.27 0 11.22 10.24
丙烯酸酯-聚氨酯 0 0.00 0 5.73 0.00

Tab.2

Washability of different fabrics after finishing"

硬挺剂种类 整理后质量/g 水洗后质量/g 质量损失率/%
聚氨酯 1.46 1.37 6.2
F-404 1.41 1.35 4.3
EcofunYTJ 1.46 1.41 3.4
丙烯酸酯-聚氨酯 1.46 1.46 0.0

Fig.1

Coating adhesive applied shapes. (a) Fully coated;(b) Strip-like; (c) Non-continuous serrated;(d) Continuous serrated"

Fig.2

Tensile curves for different coating shapes"

Fig.3

Knitted fabric structure and coating position"

Tab.3

Influence of coating position & thickness on anti-curling effect"

浆膜厚度/mm 卷边率C/%
正面 反面
0.20 8.16 0.00
0.25 7.81 0.00
0.30 3.89 0.00
0.40 9.68 0.00
0.50 11.34 0.92

Tab.4

Influence of edge width on anti-curling effect"

浆边宽
度/cm		 卷边率C/%
烘干后 前处理后 浸轧染液 汽蒸 皂煮后
1.0 1.89 16.66 — — —
1.5 0.00 0.87 0 0 0
2.0 0.00 0.00 0 0 0

Fig.4

Influence of continuous serrated coating on dyeing effect at different dye concentrations"

[1] 蒋高明, 高哲. 针织新技术发展现状与趋势[J]. 纺织学报, 2017,38(12):169-176.
JIANG Gaoming, GAO Zhe. Development status and tendency of knitting technology innovation[J]. Journal of Textile Research, 2017,38(12):169-176.
[2] 周坚明. 节能减排的针织物平幅染整加工技术[J]. 纺织服装周刊, 2008(15):31.
ZHOU Jianming. Knitted fabric dyeing and finishing technology for energy saving and emission reduction[J].Textile and Apparel Weekly, 2008(15):31.
[3] 陈祥勤. 针织物连续化平幅练漂染色工艺路线的实现[J]. 针织工业, 2007(08):36-37,72.
CHEN Xiangqin. Realization of continuous bleaching dyeing process route for knitted fabrics[J].Knitting Industries, 2007(8):36-37,72.
[4] 杨昆, 陶肖明, 叶荫权, 等. 一种新型针织用环锭纱的研制及应用[J]. 纺织学报, 2004,25(6):58-60.
YANG Kun, TAO Xiaoming, YE Yinquan, et al. Development and application of a new type of ring yarn for knitting[J]. Journal of Textile Research, 2004,25(6):58-60.
[5] 陈忠. 不同纺纱方法的成纱结构与特性[J]. 纺织导报, 2003(6):142-143.
CHEN Zhong. Yarn structure and characteristics of different spinning methods[J].China Textile Leader, 2003(6):142-143.
[6] 陈国强, 李倩倩, 朱亚楠. 一种抗卷边纬编针织物的织造方法[J]. 上海纺织科技, 2013,41(2):19.
CHEN Guoqiang, LI Qianqian, ZHU Yanan. A weaving method for anti-curling weft knitted fabrics[J]. Shanghai Textile Science & Technology, 2013,41(2):19.
[7] 徐顺成. 针织物平幅连续化前处理工艺与设备:一[J]. 染整技术, 2008(3):12.
XU Shuncheng. Continuous pre-treatment technology and equipment for knitted fabric: I[J].Textile Dyeing and Finishing Journal, 2008(3):12.
[8] 史道鹏. 解决汗布卷边问题的方法[J]. 针织工业, 2008(5):2.
SHI Daopeng. A method to solve the problem of curling[J].Knitting Industries, 2008(5):2.
[9] 徐顺成. 针织物平幅连续化前处理工艺与设备:二[J]. 针织工业, 2011(5):34-36.
XU Shuncheng. Continuous pre-treatment technology and equipment for knitted fabric: Ⅱ[J].Knitting Industries, 2011(5):34-36.
[10] 陈立秋. 针织平幅连续印染的节能减排:一[J]. 染整技术, 2010,32(11):48-53.
CHEN Liqiu. Energy saving and emission reduction of knitting flat continuous printing and dyeing: I[J]. Textile Dyeing and Finishing Journal, 2010,32(11):48-53.
[11] 岳公星. 聚丙烯酸酯乳液型硬挺整理剂的合成与应用研究[D]. 大连:大连工业大学, 2013: 8-9.
YUE Gongxing. Study on synthesis and application of polyacrylate stiffening and finishing agent[D]. Dalian: Dalian Polytechnic University, 2013: 8-9.
[12] 赵涛. 染整工艺与原理:下册[M]. 北京: 中国纺织出版社, 2009: 12-13.
ZHAO Tao. Dyeing & Finishing Technology and Principles: II[M]. Beijing: China Textile & Apparel Press, 2009: 12-13.
[13] 尹诗衡, 张心亚, 朱延安, 等. 改性聚醋酸乙烯乳液研究进展[J]. 化学与粘合, 2004(1):41-44.
YIN Shiheng, ZHANG Xinya, ZHU Yan'an,et al.Research progress of modified polyvinyl acetate emul-sion[J].Chemistry & Adhesion, 2004(1):41-44.
[14] 乔勇, 卢秀萍, 温幸, 等. 复合膜用PUA黏合剂的合成与性能[J]. 天津科技大学学报, 2008,23(4):14-17,26.
QIAO Yong, LU Xiuping, WEN Xing, et al. Synjournal and properties of PUA adhesive for composite membranes[J]. Journal of Tianjin University of Science & Technology, 2008,23(4):14-17,26.
[15] WANG Xinfeng, LUO Xin, WANG Xiaodong, et al. Heat-melt adhesion and mechanical properties of modified thermoplastic polyurethane[J]. Journal of Textile Research, 2017,27(2):59-60.
[1] . Preparation of a novel N-P flame retardant and its flame retardant properties in cotton fabric [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(11): 97-101.
[2] . Influence of structures on curling performance of polyester warp-knitted fabric [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(01): 52-0.
[3] . Preparation and antimicrobial property of silver-loaded color spun rayon fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(1): 91-0.
[4] PAN Hong;ZHAO Tao;. Antibacterial property of fabric treated with a fiber-reactive chitosan derivative [J]. JOURNAL OF TEXTILE RESEARCH, 2011, 32(2): 96-101.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd