Journal of Textile Research ›› 2020, Vol. 41 ›› Issue (12): 1-6.doi: 10.13475/j.fzxb.20200501006

• Fiber Materials •     Next Articles

Preparation and properties of poly(phthalazinone ether ketone) fibers by dry spinning

DONG Dalin1, BIN Yuezhen1(), JIAN Xigao1,2   

  1. 1. School of Chemical Engineering, Dalian University of Technology, Dalian, Liaoning 116024, China
    2. Liaoning Province Engineering Technology Center of High Performance Resins, Dalian, Liaoning 116024, China
  • Received:2020-05-06 Revised:2020-09-04 Online:2020-12-15 Published:2020-12-23
  • Contact: BIN Yuezhen E-mail:binyz@dlut.edu.cn

RichHTML

15

PDF (PC)

251

Abstract:

To expand applications of poly(phthalazinone ether ketone) (PPEK) in fiber preparation, PPEK fibers were prepared by dry spinning with PPEK and mixed solvent of p-chlorophenol and 1,1',2,2'-tetrachloroethane (volume ratio is 1:1). PPEK solution and PPEK fibers were characterized by rotating rheometer, differential scanning calorimeter, polarizing microscope, universal tensile tester, X-ray diffractometer and fiber sound velocimeter. The results show that optimal spinning temperature of 40% PPEK solution is 140 ℃. After being elongated by 1.43 times, breaking strength, elastic modulus and sonic orientation factor of PPEK fibers reach 167.6 MPa, 4.6 GPa and 0.570 5, respectively. Hot elongated PPEK fibers has good heat resistance and remains amorphous with glass transition temperature of higher than 250 ℃.

Key words: poly(aryl ether ketone), diazanaphthalene, mixed solvent, dry spinning, high temperature resistance performance

CLC Number: 

  • TQ342

Fig.1

Illustration of customized spinning machine"

Tab.1

Preparation parameters and linear density of PPEK fibers"

样品
编号		 喷丝
孔直
径/mm		 喷丝
孔长
径比		 柱塞
直径/
mm		 加热料
桶温度/
℃		 柱塞下
降速度/
(mm·s-1)		 纺丝液
喷出速度/
(cm·s-1)		 热甬道7
温度/
℃		 热甬道9
温度/
℃		 收丝辊
线速度/
(cm·s-1)		 牵伸
比		 线密
度/tex
1# 0.5 2.0 14.89 140 0.044 9 3.98 — — — — 516.4
2# 0.5 2.0 14.89 140 0.065 1 5.77 160 280 14.56 2.52 45.0

Fig.2

PPEK precursors"

Fig.3

Viscosity-temperature curve of PPEK solution"

Fig.4

Surface image of 2# fiber (×400)"

Fig.5

DSC spectra of PPEK fibers with different stretching ratio"

Fig.6

Stress-strain curves of PPEK fibers with different stretching ratio"

Tab.2

Mechanical properties of PPEK fibers with different stretching ratio"

拉伸倍数 屈服强度/MPa 屈服应变/% 断裂强度/MPa 断裂应变/% 弹性模量/GPa
未拉伸 53.6±0.2 6.0±0.3 49.5±0.2 170.7±4.4 2.0±0.1
0.50 102.8±0.1 6.9±0.4 97.6±0.3 93.1±1.2 2.8±0.3
1.00 151.3±0.2 9.2±0.5 4.3±0.1
1.43 167.6±0.1 8.8±0.3 4.6±0.1

Fig.7

XRD spectra of PPEK and PPEK fibers"

Tab.3

Sonic orientation factor of PPEK fibers with different stretching ratio"

拉伸倍数 C/(m·s-1) fs
未拉伸 2 490 ± 30 0.268 3
0.50 2 720 ± 20 0.386 8
1.00 3 050 ± 10 0.512 3
1.43 3 250 ± 10 0.570 5
[1] ROSE J B. Production of aromatic polyketones: US, 4396755[P]. 1983-08-02.
[2] SHEKAR R I, KOTRESH T M, RAO P M D, et al. Properties of high modulus PEEK yarns for aerospace applications[J]. Journal of Applied Polymer Science, 2009,112(4):2497-2510.
[3] 李明月, 焦志峰, 张天骄. 聚醚醚酮纤维的制备、性能及应用[J]. 化工新型材料, 2012,40(5):116-118.
LI Mingyue, JIAO Zhifeng, ZHANG Tianjiao. Preparation, properties and application of poly(ether ether ketone) fiber[J]. New Chemical Matetials, 2012,40(5):116-118.
[4] LUAN J S, ZHANG S L, GENG Z, et al. Influence of the addition of lubricant on the properties of poly(ether ether ketone) fibers[J]. Polymer Engineering and Science, 2013,53(10):2254-2260.
[5] LI Y X, ZHAO Y P, TAO L, et al. Development of a high-performance poly(ether ether ketone) copolymer with extremely low melt viscosity[J]. High Performance Polymers, 2018,30(3):267-273.
[6] LI R S, WU T, ZENG L X, et al. Effect of thermotropic liquid crystalline poly(ether ketone)arylates on the processibility and properties of poly(ether ether ketone)s fibers[J]. Journal of Applied Polymer Science, 2014,131(16):1-9.
[7] ZENG L X, LI R S, CHEN P, et al. Synjournal and characterization of thermotropic liquid crystalline polyarylate with ether ether ketone segments in the main chain[J]. Journal of Applied Polymer Science, 2016,133(32):1-9.
[8] 孟跃中, 蹇锡高, 郑海滨, 等. 杂环取代联苯型聚醚酮的合成与表征[J]. 高分子材料科学与工程, 1994(2):22-25.
MENG Yuezhong, JIAN Xigao, ZHENG Haibin, et al. Synjournal and test of a novel poly(ether ketone)[J]. Polymer Materials Science & Engineering, 1994 (2):22-25.
[9] 张海春, 陈天禄, 袁雅桂. 合成带有酞侧基的新型聚醚醚酮: 85108751A[P]. 1985-11-25.
ZHANG Haichun, CHEN Tianlu, YUAN Yagui. Synthesis of novel poly(ether ether ketone) with phthalide side groups: 85108751A[J]. 1985-11-25.
[10] VINOGRADOVA S V, KORSHAK V V, SALAZKIN S N, et al. Aromatic polyethers of the "cardic" type[J]. Polymer Science, 1972,14(12):2962-2970.
[11] CHEN L Z, JIAN X G, ZHU X L. Polymers from dimethyl substituted hydroxyphenyl phthalazinone[J]. Polymer Journal, 1999,31(4):393-395.
[12] WANG M J, LIU C, DONG L M, et al. Synjournal and characterization of new soluble poly(aryl ether nitrile)s containing phthalazinone moiety[J]. Chinese Chemical Letters, 2007,18(5):595-597.
[13] DING Y, HLIL A R, HAY A S. Poly(arylene ether)s and poly(arylene thioether)s containing the 1,2-dihydro-4-henyl(2H)phthalazinone moiety[J]. Journal of Polymer Science Part A:Polymer Chemistry, 1998,36(3):455-460.
[14] WANG G, ZHANG H, QIAN B Q, et al. Preparation and characterization of electrospun poly(phthalazinone ether nitrile ketone) membrane with novel thermally stable properties[J]. Applied Surface Science, 2015,351:169-174.
[15] ZHANG S H, GUAN S S, LIN C D, et al. Effect of chemical structure on the performance of sulfonated poly(aryl ether sulfone) composite nanofiltration mem-branes[J]. Membranes, 2019,9(1):1-12.
[16] ZHANG S H, ZHANG B G, ZHAO G F, et al. Anion exchange membranes from brominated poly(aryl ether ketone) containing 3,5-dimethyl phthalazinone moieties for vanadium redox flow batteries[J]. Journal of Materials Chemistry A, 2014,2(9):3083-3091.
[17] SHI R, BIN Y Z, YANG W X, et al. Optimization and characterization of poly(phthalazinone ether ketone) (PPEK) heat-resistant porous fiberous mat by electrospinning[J]. Applied Surface Science, 2016,379:282-290.
[18] YANG W X, BIN Y Z, YUAN Y J, et al. Evaluation for most probable distance between adjacent amorphous molecular chains taking preferred orientation with respect to a spinning fiber[J]. Polymer, 2016,103:112-123.
[19] LIU Y J, JIAN X G, LIU S J. Synjournal and properties of novel poly(phthalazinone ether ketone ketone)[J]. Journal of Applied Polymer Science, 2001,82(4):823-826.
[20] 兰建武, 蹇锡高, 王国庆, 等. 聚芳醚砜酮纤维的热性能[J]. 合成纤维工业, 2003,26(2):24-26.
LAN Jianwu, JIAN Xigao, WANG Guoqing, et al. Thermal property of poly(aryl ether sulfone ketone) fiber[J]. China Synthetic Fiber Industry, 2003,26(2):24-26.
[21] 朱岿立, 潘鼎. 干-喷湿纺聚丙烯腈纤维拉伸工艺研究[J]. 合成纤维工业, 2003,26(2):9-12.
ZHU Kuili, PAN Ding. Study on drawing process of dry-jet wet spinning of PAN fiber[J]. China Synthetic Fiber Industry, 2003,26(2):9-12.
[1] . Simulation of dry spinning of PVA soluble fiber [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(2): 23-27.
Viewed
Full text
266
HTML PDF
Just accepted Online first Issue Just accepted Online first Issue
0 0 15 0 0 251

  From Others local
  Times 41 225
  Rate 15% 85%

Abstract
470
Just accepted Online first Issue
0 0 470
  From Others local
  Times 63 407
  Rate 13% 87%

Cited
Web of Science  Crossref   ScienceDirect  Search for Citations in Google Scholar >>
 
This page requires you have already subscribed to WoS.
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd