Journal of Textile Research ›› 2021, Vol. 42 ›› Issue (04): 26-32.doi: 10.13475/j.fzxb.20200904907

• Invited Column: Bio-based Polyester and Polyamide Fiber • Previous Articles     Next Articles

Research progress on applications of bio-based polyamide 56 fibers in textile fields

SUN Chaoxu, LIU Xiucai()   

  1. Cathay Biotech Inc., Shanghai 201203, China
  • Received:2020-09-21 Revised:2021-01-25 Online:2021-04-15 Published:2021-04-20
  • Contact: LIU Xiucai E-mail:liujiayu@cathaybiotech.com

RichHTML

50

PDF (PC)

419

Abstract:

China is highly dependent on imported petroleum, and hexanediamine, the main raw material for polyamide 66, is monopolized by overseas companies. In line with the strategic goal of achieving carbon neutralization in China, this paper describes the characteristics of bio-based polyamide 56 fiber in detail, and reviews the research progress in its preparation technology and application fields. Bio-based polyamide 56 fiber has good mechanical properties, moisture absorption, softness, wear resistance, dyeing, heat resistance, chemical resistance and flame retardancy, which is suitable for clothing, home textiles, industrial textiles and other textiles fields. However, the large-scale promotion of bio-based polyamide 56 fiber still faces problems such as the supply and cost control of biological raw materials, the reduction of energy consumption in production and the comprehensive utilization of by-products. In the future, it is necessary to continue to increase research and development investment in fermentation and purification of bio-based monomer, polymerization, spinning and application in order to continuously reduce production costs, so as to promote the large-scale application of bio-based polyamide 56 fiber in the textile field.

Key words: bio-based fiber, bio-based polyamide 56 fiber, spinning technology, 1,5-pentanediamine, founctional fiber, application field

CLC Number: 

  • TQ34
[1] GENAS M. Rilsan (polyamid 11), synthese und eigenschaften[J]. Angewandte Chemie, 1962,74(15):535-540.
[2] Arkema. Rilsan® PA11:created from a renewable source(product data sheet)[M]. Puteeaux:Arkema, 2009: 61-62.
[3] KIND S, KREYE S, WITTMANN C. Metabolic engineering of cellular transport for overproduction of the platform chemical 1,5-diaminopentane in corynebacte-rium glutamicum[J]. Metab Eng, 2001,13:617-627.
pmid: 21821142
[4] 董奎勇, 杨婷婷, 王学利, 等. 生物基聚酯与聚酰胺纤维的研发进展[J]. 纺织学报, 2020,41(1):174-183.
DONG Kuiyong, YANG Tingting, WANG Xueli, et al. Research and development of bio-based polyester and polyamide fibers[J]. Journal of Textile Research, 2020,41(1):174-183.
[5] 刘博. 国产尼龙56长丝一步法纺牵联合机的探究[J]. 价值工程, 2016,35(27):107-110,111.
LIU Bo. Research on one-step spinning and drawing combined machine of domestic nylon 56 filament[J]. Value Engineering, 2016,35(27):107-110,111.
[6] 徐凯. 国产聚酰胺56工业丝纺牵联合机的探究[J]. 价值工程, 2019,38(24):122-125.
XU Kai. Exploration of industrial silk spinning joint machine for domestic polyamide 56[J]. Value Engineering, 2019,38(24):122-125.
[7] 于维才. 尼龙56的物理性能及可纺性探析[J]. 聚酯工业, 2014,27(1):38-39.
YU Weicai. Analysis of the physical properties and spinnability of nylon 56[J]. Polyester Industry, 2014,27(1):38-39.
[8] 张晨. 生物基聚己二酸戊二胺聚合物与长丝性能研究[D]. 上海:东华大学, 2015: 4-6.
ZHANG Chen. Study on properties of bio-based polypentamethylene adipate polymer and filament[D]. Shanghai: Donghua University, 2015: 4-6.
[9] 吴田田. 生物基尼龙 56 的结晶、动态热力学及流变性能研究[D]. 上海:东华大学, 2017: 3-6.
WU Tiantian. Study on the crystallization, dynamic thermodynamics and rheological properties of bio-based nylon 56[D]. Shanghai:Donghua University, 2017: 3-6.
[10] 郝新敏, 郭亚飞. 生物基聚酰胺纤维引领产业绿色发展[J]. 纺织科学研究, 2020(2):74-75.
HAO Xinmin, GUO Yafei. Bio-based polyamide fiber leads the green development of the industry[J]. Textile Science Research, 2020(2):74-75.
[11] 江苏太极实业新材料有限公司, 上海凯赛生物技术股份有限公司. 聚酰胺56高强力工业丝及其制备方法: 201910430213.0[P]. 2019-07-26.
Jiangsu Taiji Industrial New Materials Co Ltd, Cathay Biotech Inc. High-strength industrial yarn for polyamide 56 and preparation method thereof: 201910430213.0[P]. 2019-07-26.
[12] 东丽株式会社. 吸湿性纤维及其织造方法:201180016429.4[P]. 2012-12-19.
Toray Industries. Hygroscopic fiber and its weaving method: 201180016429.4[P]. 2012-12-19.
[13] YASSIR Abdel Gadir Rltahir Hashim. 新型尼龙56纤维的制备和表征[D]. 上海:东华大学, 2015: 2-30.
YASSIR Abdel Gadir Rltahir Hashim. Preparation and characterization of new nylon fibers[D]. Shanghai: Donghua University, 2015: 2-30.
[14] 优纤科技(丹东)有限公司,中国人民解放军总后勤部军需装备研究所,辽宁恒星精细化工有限公司. 一种锦纶56纤维的染色方法:201610428217.1 [P]. 2016-08-24.
Youxian Technology (Dandong) Co Ltd, The Quartermaster Equipment Research Institute The General Logistic Department of PLA, Liaoning Fixed Star Fine Chemical Co Ltd. A dyeing method of nylon 56 fiber: 201610428217.1 [P]. 2016-08-24.
[15] 李蒙蒙, 胡柳, 侯爱芹, 等. 生物基纤维尼龙PA56染色性能及产品开发研究进展[J]. 染料与染色, 2016(5):25-30.
LI Mengmeng, HU Liu, HOU Aiqin, et al. Research progress on dyeing performance and product development of bio-based fiber nylon polyamide 56[J]. Dyestuffs and Coloration, 2016(5):25-30.
[16] 马雪松, 高艺, 陈英, 等. 生物基尼龙PA56的活性染料染色性能[J]. 印染, 2019,45(18):9-13,29.
MA Xuesong, GAO Yi, CHEN Ying, et al. Dyeing performance of bio-based nylon 56 with reactive dyes[J]. China Dyeing & Finishing, 2019,45(18):9-13,29.
[17] 上海凯赛生物技术股份有限公司, CIBT 美国公司. 一种聚酰胺56纤维或聚酰胺56/棉混纺面料的靛蓝染色方法及其产品: 201710888976.0[P]. 2017-09-27.
Cathay Biotech Inc, CIBT America Inc. Indigo dyeing method of polyamide 56 fiber or polyamide 56/cotton blended fabric and product thereof: 201710888976.0[P]. 2017-09-27.
[18] 胡翱翔, 史晓军. 聚酰胺56 POY纤维的开发[J]. 纺织导报, 2019 (8):47-48.
HU Aoxiang, SHI Xiaojun. Development of Polyamide 56 for POY Fiber[J]. China Textile Leader, 2019(8):47-48.
[19] 于海龙. 锦纶56 DTY高弹丝的POY-DTY生产方法: 201410211175.7[P]. 2014-08-06.
YU Hailong. POY-DTY production method of DTY high elastic yarn for nylon 56: 201410211175.7[P]. 2014-08-06.
[20] 展颂股份有限公司. 消光聚酰胺56纤维及其制造方法: 201510087957.9[P]. 2018-08-03.
Zhantong Inc. Dull fiber for polyamide 56 and its manufacturing method: 201510087957.9[P]. 2018-08-03.
[21] 张俊辉, 丛洪莲. 生物基聚酰胺56长丝及面料性能研究[J]. 丝绸, 2018,55(12):25-31.
ZHANG Junhui, CONG Honglian. Study on properties of filament and fabric for bio-based polyamide 56[J]. Journal of Silk, 2018,55(12):25-31.
[22] 宁波福天新材料科技有限公司. 一种尼龙纤维及其制备方法以及一种纺织材料:201511026024.5[P]. 2017-07-07.
Ningbo Futian New Materials Technology Co Ltd. A nylon fiber and its preparation method and a textile material: 201511026024.5[P]. 2017-07-07.
[23] 东丽株式会社. 聚酰胺56纤维、橡胶增强帘子线和增强橡胶:2007236649[P]. 2011-12-07.
Toray Industries. Polyamide 56 fiber, rubber reinforced cord and reinforced rubber: 2007236649[P]. 2011-12-07.
[24] 东丽株式会社. 聚酰胺56细丝、含有它们的纤维结构、以及用气囊织物:200980118941.2 [P]. 2013-09-25.
Toray Industries. Polyamide 56 filaments, fiber structures containing them, airbag fabrics: 200980118941.2[P]. 2013-09-25.
[25] 上海凯赛生物技术股份有限公司, CIBT美国公司, 凯赛(乌苏)生物材料有限公司. 一种高粘聚酰胺56树脂、高强聚酰胺56工业丝及其制备方法与应用: 202010245867.9 [P]. 2020-07-07.
Cayhay Biotech Inc, CIBT America Inc, Cathay(Wusu) Biomaterial Co Ltd. High-viscosity polyamide 56 resin, high-strength polyamide 56 industrial yarn and these preparation method and application: 202010245867.9 [P]. 2020-07-07.
[26] 威海市山花地毯集团有限公司. 生物基尼龙56地毯膨体纱的生产方法: 201410415413.6 [P]. 2016-09-21.
Weihai Mountain Flower Carpet Group Co Ltd. Production method of carpet bulked yarn for bio-based polyamide 56: 201410415413.6[P]. 2016-09-21.
[27] 上海凯赛生物技术股份有限公司, CIBT美国公司. 一种阻燃柔软蓬松聚酰胺5X连续膨体长丝及其制备方法和应用:201710102959.X [P]. 2020-06-05.
Cayhay Biotech Inc, CIBT America Inc. A flame-retardant, soft, fluffy, continuous bulked filament for polyamide 5X and its preparation method and application: 201710102959.X [P]. 2020-06-05.
[28] 优纤科技(丹东)有限公司, 中国人民解放军总后勤部军需装备研究所, 辽宁恒星精细化工有限公司. 一种聚酰胺56短纤及其熔体直纺制备方法: 201610438659.4 [P]. 2016-08-24.
Youxian Technology (Dandong) Co Ltd, The Quartermaster Equipment Research Institute The General Logisitic Department of PLA, Liaoning Fixed Star Fine Chemical Co Ltd. A method for preparing polyamide 56 staple fiber and its melt direct spinning: 201610438659.4 [P]. 2016-08-24.
[29] 上海凯赛生物技术股份有限公司, CIBT美国公司. 一种聚酰胺5X短纤及其制备方法和应用:201710105921.8 [P]. 2019-07-26.
Cayhay Biotech Inc, CIBT America Inc. Polyamide 5X staple fiber and its preparation method and application: 201710105921.8 [P]. 2019-07-26.
[30] 上海凯赛生物技术股份有限公司, CIBT美国公司. 一种聚酰胺56割草丝及其制备方法:201710376174.1 [P]. 2018-12-07.
Cayhay Biotech Inc, CIBT America Inc. Polyamide 56 mowing wire and preparation method: 201710376174.1[P]. 2018-12-07.
[31] 凯赛(乌苏)生物材料有限公司, 上海凯赛生物技术股份有限公司, CIBT美国公司. 一种聚酰胺单丝及其制备方法和应用:201811085458.6 [P]. 2020-03-24.
Cathay(Wusu) Biomaterial Co Ltd, Cayhay Biotech Inc, CIBT America Inc. Polyamide monofilament and its preparation method and application: 201811085458.6[P]. 2020-03-24.
[32] 张若楠. 聚酰胺56/PET 复合纤维制备及性能研究[D]. 上海:东华大学, 2017: 15-30.
ZHANG Ruonan. Study on preparation and performance of polyamide 56/PET composite fiber[D]. Shanghai: Donghua University, 2017: 15-30.
[33] 赵辉. 新型生物基尼龙56异收缩混纤丝的制备及其产品性能研究[D]. 上海:东华大学, 2015: 3-8.
ZHAO Hui. Study on the preparation and performance of differential shrinkage blended fiber for new bio-based nylon 56[D]. Shanghai: Donghua University, 2015: 3-8.
[34] 王学利, 俞建勇, 刘修才, 等. 生物质尼龙56纤维/PBT纤维的FDY/POY异收缩混纤丝及其制备方法: 201610227057.4[P]. 2016-04-13.
WANG Xueli, YU Jianyong, LIU Xiucai, et al. FDY / POY differential shrinkage blended fiber of biomass nylon 56 fiber/PBT fiber and its preparation method:201610227057.4 [P]. 2016-04-13.
[35] 辽宁银珠化纺集团有限公司. 一种具有阻燃性能的聚酰胺56的制备方法和聚酰胺56纤维: 201610782169.6 [P]. 2017-02-22.
Liaoning Yinzhu Chemtex Group Co Ltd. Preparation method of polyamide 56 with flame retardant properties and polyamide 56 fiber: 201610782169.6 [P]. 2017-02-22.
[36] 张瀚誉, 钱思琦, 朱瑞淑, 等. 抗菌生物基聚酰胺56及纤维的制备与性能研究[J]. 合成纤维, 2020,49(12):1-7.
ZHANG Hanyu, QIAN Siqi, ZHU Ruishu, et al. Preparation and study on properties of antimicrobial bio-based polyamide 56 and its fibers[J]. Synthetic Fiber in China, 2020,49(12):1-7.
[1] YANG Tingting, GAO Yuanbo, ZHENG Yi, WANG Xueli, HE Yong. Thermal degradation kinetics and pyrolysis products of bio-based polyamide 56 fiber [J]. Journal of Textile Research, 2021, 42(04): 1-7.
[2] DONG Kuiyong, YANG Tingting, WANG Xueli, HE Yong, YU Jianyong. Research and development progress of bio-based polyester and polyamide fibers [J]. Journal of Textile Research, 2020, 41(01): 174-183.
[3] WEI Yanhong, XIE Chunping, LIU Xinjin, SU Xuzhong, YIN Gaowei. Drafting mechanism and application of spun yarn produced by large diameter soft rubber-covered roll [J]. Journal of Textile Research, 2019, 40(10): 62-67.
[4] . Microfluidic spinning technology for multifunctional nanofibers and application and research progress thereof [J]. Journal of Textile Research, 2018, 39(12): 158-165.
[5] . Development of stainless steel fiber/cotton composite yarn and its performances [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(7): 36-0.
[6] . Industrialized green spinning technology and application of pure chitosan fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(2): 157-0.
[7] LI Xine. Research progress of basalt fibres and fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2010, 31(1): 145-152.
[8] HUANG Lixin;ZHU Chunxiang. Solospun technology and its product properties [J]. JOURNAL OF TEXTILE RESEARCH, 2007, 28(5): 35-37.
[9] XIE Chunping;YANG Lili;SU Xuzhong;FENG Jie. Analysis of compact effect and yarn structure of compact Siro spinning [J]. JOURNAL OF TEXTILE RESEARCH, 2007, 28(3): 9-12.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd