Journal of Textile Research ›› 2021, Vol. 42 ›› Issue (11): 124-128.doi: 10.13475/j.fzxb.20201208305

• Dyeing and Finishing & Chemicals • Previous Articles     Next Articles

Effect of ultrasonic treatment on 4,4'-diaminodiphenylmethane in polyurethane coating of polyester fabric

ZHU Lanfang1(), BAI Jie2, ZHOU Yincheng1, HOU Chengwei3   

  1. 1. Suzhou Institute of Fiber Inspection, Suzhou, Jiangsu 215500, China
    2. China Textile Engineering Society, Beijing 100025, China
    3. TAEKWANG Industrial Co., Ltd., Suzhou, Jiangsu 215500, China
  • Received:2020-12-31 Revised:2021-08-29 Online:2021-11-15 Published:2021-11-29

RichHTML

6

PDF (PC)

142

Abstract:

Aiming at the problem of high detection rate of 4,4'-diaminodiphenylmethane in polyester fabric samples with polyurethane coating treated with xylene solvent decolorization and great difference in results, o-xylene, m-xylene and p-xylene were used as extraction solvents respectively, and polyurethane coated polyester fabric was studied by ultrasonic extraction, and the effects of ultrasonic treatment time, temperature, type of dispersant and volume fraction of dispersant on the peak area response value of 4,4'-diaminodiphenylmethane mass spectrometry were studied.It was found that when the dispersant acetonitrile was transferred, the response value of the target was the highest. When the volume fraction of acetonitrile was 50%, 70%, 70%, respectively, the peak area of the target substance of the extraction residue of o-xylene, m-xylene and p-xylene was the highest, and when the treatment temperature was 40,50,60 ℃, p-xylene, o-xylene and m-xylene were used as extraction solvent, the peak area of the target compound reached the peak, and the extraction efficiency was the best when the treatment time was 45-50 min.

Key words: 4,4'-diaminodiphenylmethane, xylene isomer, polyurethane coating, ultrasonic treatment, polyester fabric

CLC Number: 

  • TS19

Tab.1

Peak area of samples for different kinds of dispersant"

分散剂
种类		 峰面积
邻二甲苯 间二甲苯 对二甲苯
甲醇 263 858 384 858 83 779
乙腈 350 878 509 057 281 455
乙醇 227 587 187 623 214 321

Fig.1

Peak area of samples for different volume fraction of acetonitrile dispersant"

Fig.2

Peak area of samples for different ultrasonic temperature"

Fig.3

Peak area of samples for different ultrasonic time"

[1] 陈红梅, 王胜鹏, 俞建芳. 纺织品及纺织化学品中的高关注度物质(SVHC)[J]. 现代纺织技术, 2012, 20(5):48-55.
CHEN Hongmei, WANG Shengpeng, YU Jianfang. Subtances of very high concern(SVHC) in textiles and textile chemicals[J]. Advanced Textile Technology, 2012, 20(5):48-55.
[2] 杨加仙, 徐济仓, 周岚, 等. 禁用偶氮染料相关法规及检测标准概述[J]. 应用化工, 2015(S1):41-46.
YANG Jiaxian, XU Jicang, ZHOU Lan, et al. Overview of regulations and detection criteria of banned azo dyes[J]. Applied Chemical Industry, 2015(S1):41-46.
[3] 丁友超, 王香香, 王晓琼, 等. 欧盟纺织品中禁用偶氮着色剂检测新旧标准差异[J]. 印染助剂, 2013(3):46-50.
DING Youchao, WANG Xiangxiang, WANG Xiaoqiong, et al. Difference between new and old editions of the European standard on methods for the determination of banned azo colorants in textiles[J]. Textile Auxiliaries, 2013(3):46-50.
[4] 解玉梅. 我国聚酯产业链发展现状及趋势[J]. 化学工业, 2006, 24(4):10-15.
XIE Yumei. Current situation and future development of ethylene industry[J]. Chemical Industry, 2006, 24(4):10-15.
[5] 崔明. 我国对二甲苯的市场分析[J]. 精细与专用化学品, 2018, 26(12):9-12.
CUI Ming. Market analysis of PX in China[J]. Fine and Speciality Chemicals, 2018, 26(12):9-12.
[6] 邓明亮, 伏广伟, 杨萍, 等. 致癌芳香胺4,4'-二氨基二苯甲烷假阳性快速筛查研究[J]. 浙江纺织服装职业技术学院学报, 2016, 15(3):22-24, 53.
DENG Mingliang, FU Guangwei, YANG Ping, et al. Study of the rapid screening of false-positive determination of carcinogenic arylamine (4, 4'-diaminodiphenylmethane)[J]. Journal of Zhejiang Fashion Institute of Technology, 2016, 15(3):22-24, 53.
[7] 胡小钟, 余建新, 倪澜荪, 等. 禁用偶氮染料检测中假阳性结果的鉴别方法[J]. 分析化学, 2000(4):411-416.
HU Xiaozhong, YU Jianxin, NI Lansun, et al. Identification method of false positive result in the detection of prohibited azo dyes[J]. Analytical Chemistry, 2000(4):411-416.
[8] 张红医, 韩利梅, 石志红, 等. 乙腈与水在任何条件下都互溶吗[J]. 化学教育, 2017, 38(20):76-80.
ZHANG Hongyi, HAN Limei, SHI Zhihong, et al. Is acetonitrile miscible with water in any cases[J]. Journal of Chemical Education, 2017, 38(20):76-80.
[9] 杨新磊, 罗明标, 唐毓萍. 三相中空纤维式液相微萃取用于快速富集血浆中的尼古丁[J]. 色谱, 2006(6):555-559.
YANG Xinlei, LUO Mingbiao, TANG Yuping. Enrichment of nicotine in plasma with threephase hollow fiber based liquid phase microextraction[J]. Chinese Journal of Chromatography, 2006(6):555-559.
[10] 赵海凤, 汪澜. 超声波在聚酯纤维分散染料染色中的应用研究[J]. 浙江理工大学学报, 2008(6):649-653.
ZHAO Haifeng, WANG Lan. Application study of ultrasonic dyeing of polyester fiber with disperse dye[J]. Journal of Zhejiang Sci-Tech University, 2008(6):649-653.
[1] PU Dandan, FU Yaqin. Preparation and sound insulation performance of polyester fabric/polyvinyl chloride-hollow glass microspheres composites [J]. Journal of Textile Research, 2021, 42(11): 77-83.
[2] LI Liang, LIU Jingfang, HU Zedong, GENG Changjun, LIU Rangtong. Graphene oxide loading on polyester fabrics and antistatic properties [J]. Journal of Textile Research, 2020, 41(09): 102-107.
[3] LIU Guojin, HAN Pengshuai, CHAI Liqin, WU Yu, LI Hui, GAO Yafang, ZHOU Lan. Preparation and stability of self-crosslinking P(St-NMA) photonic crystals with structural colors on polyester fabrics [J]. Journal of Textile Research, 2020, 41(05): 99-104.
[4] WANG Xiaofei, WAN Ailan. Preparation of polypyrrole/silver conductive polyester fabric by ultraviolet exposure [J]. Journal of Textile Research, 2020, 41(04): 112-116.
[5] DING Fang, REN Xuehong. Flame-retardant finishing of polyester fabrics by grafting phosphorus-nitrogen compounds [J]. Journal of Textile Research, 2020, 41(03): 100-105.
[6] CHEN Ying, ZHOU Shuang, WEI Tianjing, FANG Haoxia, LI Yufei. Preparation and properties of polypyrrole composite fabric by soft template process [J]. Journal of Textile Research, 2019, 40(12): 93-97.
[7] XU Lin, REN Yu, ZHANG Hongyang, WU Shuangquan, LI Ya, DING Zhirong, JIANG Wenwen, XU Sijun, ZANG Chuanfeng. Construction and properties of superhydrophobic layer of titania/fluorosilane on polyester fabric surface [J]. Journal of Textile Research, 2019, 40(12): 86-92.
[8] DAI Yue, ZHANG Ruiping, WANG Qiuping, HU Ya'nan, ZHANG Xianguo. Deodorizing effect of polyester fabric treated by citric acid/β-cyclodextrin [J]. Journal of Textile Research, 2019, 40(12): 104-108.
[9] ZHU Jinming, QIAN Jianhua, SUN Liying, LI Zhengping, PENG Huimin. Properties of functionalized composite polyester fabric prepared from silver nanowires of high aspect ratio [J]. Journal of Textile Research, 2019, 40(11): 113-118.
[10] WANG Fanghe, WANG Rui, WEI Lifei, WANG Zhaoying, ZHANG Anying, WANG Deyi. Preparation and properties of layer-by-layer self-assembled flame retardant modified polyester fabrics [J]. Journal of Textile Research, 2019, 40(11): 106-112.
[11] GAO Jing, WANG Lu. Influence of pretreatment process on superhydrophobic modification of wool/polyester fabric [J]. Journal of Textile Research, 2019, 40(09): 91-96.
[12] ZHANG Huan, YAN Jun, WANG Xiaowu, JIAO Andong, LI Hong, ZHENG Laijiu, HE Tingting. Application of low temperature plasma in surface modification of polyester fiber [J]. Journal of Textile Research, 2019, 40(07): 103-107.
[13] LI Yang, ZHANG Yuanming, JIANG Wei, ZHANG Jianming, WANG Sishe, SU Jianjun, HAN Guangting. Ultrasonic treatment of Modal fiber dyed with madder [J]. Journal of Textile Research, 2019, 40(04): 83-89.
[14] . Preparation and photocatalytic properties of  polyester fabric loaded with titanium dioxide [J]. Journal of Textile Research, 2018, 39(11): 91-95.
[15] . Effect of modified by β-cyclodextrin derivatives of aldehydes crosslinked chitosan on hydrophilicity of polyester fabric [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(07): 82-88.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
[1] . [J]. JOURNAL OF TEXTILE RESEARCH, 2003, 24(06): 33 -34 .
[2] . [J]. JOURNAL OF TEXTILE RESEARCH, 2003, 24(06): 35 -36 .
[3] . [J]. JOURNAL OF TEXTILE RESEARCH, 2003, 24(06): 107 .
[4] . [J]. JOURNAL OF TEXTILE RESEARCH, 2003, 24(06): 109 -620 .
[5] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(01): 1 -9 .
[6] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 101 -102 .
[7] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 105 -107 .
[8] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 108 -110 .
[9] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 111 -113 .
[10] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 119 -120 .
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd