Journal of Textile Research ›› 2023, Vol. 44 ›› Issue (01): 209-218.doi: 10.13475/j.fzxb.20220102010

• Comprehensive Review • Previous Articles     Next Articles

Research progress of preparation of nanofiber-supported catalysts and application thereof in environmental protection

CHEN Mingxing1,2, ZHANG Wei1,2, WANG Xinya1,2(), XIAO Changfa3   

  1. 1. College of Textile and Garments, Hebei University of Science and Technology, Shijiazhuang, Hebei 050018, China
    2. Hebei Province Technology Innovation Center of Textile and Garment, Shijiazhuang, Hebei 050018, China
    3. Fiber Materials Research Center, Shanghai University of Engineering Science, Shanghai 201620, China
  • Received:2022-01-12 Revised:2022-09-28 Online:2023-01-15 Published:2023-02-16

RichHTML

25

PDF (PC)

104

Abstract:

Significance Nano-sized catalysts show higher catalytic activity than bulk analogues by virue of their larger specific surface area. Therefore, nano-sized catalysts have been widely used in the field of catalysis research. However, nano-sized catalysts tend to agglomerate during the application, which leads to the formation of large particles and a huge reduction in catalytic activity. Meanwhile, the recycling of nano-sized catalysts is difficult. These challenges all restrict the application of nano-sized catalysts. In order to solve these problems, some efforts have been made, such as surface modification, and immobilization of the nano-sized catalysts on supports. Among the various supports employed, the nanofibers have attracted much attention by virue of their larger specific surface area and nanoscale diameter. The larger specific surface area of nanofibers leads to an increase in the catalytic activity of nanofiber-supported catalysts as more active sites are available and accessible by reactants in the catalysis process. Moreover, the recovery and reuse of nanofiber-supported catalysts are simple. Hence, the nanofiber-supported catalysts show potential applications in the field of catalysis.
Progress The recent studies about the preparation of nanofiber-supported catalysts and their application in environmental remediation are reviewed. As a general method for preparing nanofibers, electrospinning technology has been known to be able to prepare nanofibers with various compositions and structures. The methods involving electrospinning technology for preparing the nanofiber-supported catalysts could be divided into two ways. One method is coated by an electrospinning process, in which the nano-sized catalysts or catalyst precursors are dispersed into an electrospinning solution followed by the electrospinning process. If the catalyst precursors are added to the electrospinning solution, a post treatment is necessary after the electrospinning process to convert catalyst precursors into nano-sized catalysts. The other method is to deposit the nano-sized catalysts on the surface of nanofiber after electrospinning process. Though the coating method is simple, it is difficult to achieve a homogeneous dispersion of nano-sized catalysts in nanofibers. While the precursor electrospinning deposition method shows more advantages for preparing nanofiber-supported catalysts with quite uniform distribution of the nano-sized catalysts on nanofiber surface. The simplicity of recovery and the higher catalytic activity of nanofiber-supported catalysts makes them economical and environmentally friendly in the application of dye degradation, organic matter degradation, and heavy metal ion reduction, etc.
Conclusion and Prospect According to the reported research, nanofiber-supported catalysts have the advantages of high catalytic activity and recyclability. Thus, nanofiber-supported catalysts have great potential in catalytic applications. However, they still has the disadvantages of poor mechanical properties and low preparation efficiency, which cannot meet the requirement of practical applications. Therefore, some efforts can be made from the following aspects in future research. 1) In view of practical applications, nanofiber-supported catalysts with fine mechanical properties have huge advantages. Some efforts should be made to improve the mechanical properties, such as tailoring the structure by regulating the electrospinning process and using the substrates with excellent mechanical properties as the nanofiber receiver. 2) The large-scale fabrication and commercial application of nanofiber-supported catalysts are still a huge challenge. Therefore, it is necessary to explore the electrospinning process using green solvent and have low cost and high efficiency for fabricating nanofiber-supported catalysts. 3) The catalytic activity of nanofiber-supported catalysts should be improved by optimizing the structure and surface composition of nanofibers as it is highly dependent on the active sites of nanofiber-supported catalysts. Except for the metal-based catalysts, other catalysts should be combined with nanofibers to expand the applications of nanofiber-supported catalysts.

Key words: nanofiber, nanoparticle, catalyst, pollutants degradation, photocatalysis

CLC Number: 

  • TQ34

Fig.1

Illustration of different approaches to prepare nanofiber-supported catalysts. (a) Electrospinning with catalyst; (b)Electrospinning with catalyst precursor; (c)Surface loading"

Fig.2

Schematic of synthesis process of PAN/TiO2/Ag nanofiber membrane"

Tab.1

Principle, advantages, disadvantages and improvement directions of preparation methods of nanofiber-supported catalysts"

制备方法 原理 优点 缺点 改进建议
直接纺丝法 添加纳米催化剂 纺丝液中直接添加纳米催化剂 方法简单,适用范围广 催化剂被纳米纤维包裹,易团聚,催化活性低 实现纳米粒子可控制备,增加纳米粒子和反应物接触面积,提高反应活性
添加纳米催化剂前驱体 纺丝液中添加纳米催化剂前驱体制得纳米纤维,采用一定技术手段将催化剂前驱体转化为纳米催化剂 催化剂在纳米纤维中分散好 工艺复杂,催化剂被纳米纤维包裹,催化活性低
表面负载法 负载金属纳米粒子 将溶液中金属离子还原为金属纳米粒子,并负载到纳米纤维表面 结构可控,催化剂在纳米纤维表面分布均匀,催化活性高 工艺较复杂,适用范围有一定局限性 简化制备流程,降低成本,提高纳米粒子和纳米纤维界面的结合性能
负载金属氧化物纳米粒子 通过水热合成、高温煅烧、物理吸附等方式,将金属氧化物纳米粒子负载到纳米纤维表面
负载其它纳米粒子 通过原位生长、物理吸附等将纳米粒子负载到纳米纤维表面
[1] RODRIGUES T S, DA SILVA A G, CAMARGO P H. Nanocatalysis by noble metal nanoparticles: controlled synthesis for the optimization and understanding of activities[J]. Journal of Materials Chemistry A, 2019, 7(11): 5857-5874.
doi: 10.1039/C9TA00074G
[2] 张婷婷, 许可欣, 金梦甜, 等. 纤维素基有机-无机纳米光催化复合材料制备及其水处理应用的研究进展[J]. 纺织学报, 2021, 42(7): 175-183.
ZHANG Tingting, XU Kexin, JIN Mengtian, et al. Recent progress in preparation of cellulose-based organic-inorganic photocatalysts nanohybrids and its application in water treatment[J]. Journal of Textile Research, 2021, 42(7): 175-183.
doi: 10.1177/004051757204200309
[3] HANSKE C, SANZ-ORTIZ M N, LIZ-MARZáN L M. Silica-coated plasmonic metal nanoparticles in action[J]. Advanced Materials, 2018. DOI: 10.1002/adma.201707003.
doi: 10.1002/adma.201707003
[4] LIU S H, REGULACIO M D, TEE S Y, et al. Preparation, functionality, and application of metal oxide-coated noble metal nanoparticles[J]. The Chemical Record, 2016, 16(4): 1965-1990.
doi: 10.1002/tcr.201600028 pmid: 27291595
[5] LAI C, LIU X G, QIN L, et al. Chitosan-wrapped gold nanoparticles for hydrogen-bonding recognition and colorimetric determination of the antibiotic kana-mycin[J]. Microchimica Acta, 2017, 184(7): 2097-2105.
doi: 10.1007/s00604-017-2218-z
[6] KAKAEI K, RAHNAVARDI M. Synthesis of nitrogen-doped reduced graphene oxide and its decoration with high efficiency palladium nanoparticles for direct ethanol fuel cell[J]. Renewable Energy, 2021, 163: 1277-1286.
doi: 10.1016/j.renene.2020.09.043
[7] MAO H, JI C G, LIU M H, et al. Enhanced catalytic activity of Ag nanoparticles supported on polyacrylamide/polypyrrole/graphene oxide nanosheets for the reduction of 4-nitrophenol[J]. Applied Surface Science, 2018, 434: 522-533.
doi: 10.1016/j.apsusc.2017.10.209
[8] BARAN T, NASROLLAHZADEH M. Facile synthesis of palladium nanoparticles immobilized on magnetic biodegradable microcapsules used as effective and recyclable catalyst in Suzuki-Miyaura reaction and p-nitrophenol reduction[J]. Carbohydrate Polymers, 2019. DOI: 10.1016/j.carbpol.2019.115029.
doi: 10.1016/j.carbpol.2019.115029
[9] WANG Q, ASTRUC D. State of the art and prospects in metal-organic framework (MOF)-based and MOF-derived nanocatalysis[J]. Chemical Reviews, 2020, 120(2): 1438-1511.
doi: 10.1021/acs.chemrev.9b00223 pmid: 31246430
[10] LI S, CUI Z M, LI D M, et al. Hierarchically structured electrospinning nanofibers for catalysis and energy storage[J]. Composites Communications, 2019(13): 1-11.
[11] LI Z H, LIU S T, SONG S G, et al. Porous ceramic nanofibers as new catalysts toward heterogeneous reactions[J]. Composites Communications, 2019(15): 168-178.
[12] 周园园, 郑煜铭, 吴小琼, 等. 静电纺纳米纤维光催化剂性能增强方法的研究进展[J]. 纺织学报, 2021, 42(11): 179-186.
ZHOU Yuanyuan, ZHENG Yuming, WU Xiaoqiong, et al. Research progress of performance enhancement methods for electrospun nanofiber-based photo-catalyst[J]. Journal of Textile Research, 2021, 42(11): 179-186.
[13] KHAN M Q, KHARAGHANI D, ULLAH S, et al. Self-cleaning properties of electrospun PVA/TiO2 and PVA/ZnO nanofibers composites[J]. Nanomaterials, 2018. DOI: 10.3390/nano8090644.
doi: 10.3390/nano8090644
[14] 张梦媛, 黄庆林, 黄岩, 等. 静电纺聚四氟乙烯/二氧化钛光催化纳米纤维膜的制备及其应用[J]. 纺织学报, 2019, 40(9): 1-7.
ZHANG Mengyuan, HUANG Qinglin, HUANG Yan, et al. Electrospun poly(tetrafluoroethylene)/TiO2 photo-catalytic nanofiber membrane and its application[J]. Journal of Textile Research, 2019, 40(9): 1-7.
doi: 10.1177/004051757004000101
[15] 钱怡帆, 周堂, 张礼颖, 等. 聚丙烯腈/醋酸纤维素/TiO2复合纳米纤维膜的制备及其光催化降解性能[J]. 纺织学报, 2020, 41(5): 8-14.
QIAN Yifan, ZHOU Tang, ZHANG Liying, et al. Preparation of polyacrylonitrile/cellulose acetate/TiO2 composite nanofiber membrane and its photocatalytic degradation performance[J]. Journal of Textile Research, 2020, 41(5): 8-14.
[16] LI Y, ZHAO H J, YANG M J. TiO2 nanoparticles supported on PMMA nanofibers for photocatalytic degradation of methyl orange[J]. Journal of Colloid and Interface Science, 2017, 508: 500-507.
doi: 10.1016/j.jcis.2017.08.076
[17] GUO S J, BAI J, LIANG H O, et al. The controllable preparation of electrospun carbon fibers supported Pd nanoparticles catalyst and its application in Suzuki and Heck reactions[J]. Chinese Chemical Letters, 2016, 27(3): 459-463.
doi: 10.1016/j.cclet.2015.12.029
[18] WANG W, WANG K, HE J, et al. A synergistic strategy for nanoparticle/nanofiber composites towards p-nitrophenol catalytic hydrogenation[J]. Chemical Research in Chinese Universities, 2015, 31(6): 1012-1017.
doi: 10.1007/s40242-015-5155-6
[19] CHEN M X, WEI L Y, ZHANG W, et al. Fabrication and catalytic performance of a novel tubular PMIA/Ag@RGO nanocomposite nanofiber membrane[J]. RSC Advances, 2021, 11(36): 22287-22296.
doi: 10.1039/d1ra03707b pmid: 35480820
[20] LIU H J, LIU Y, WANG L M, et al. Nanofiber based origami evaporator for multifunctional and omnidirectional solar steam generation[J]. Carbon, 2021, 177: 199-206.
doi: 10.1016/j.carbon.2021.02.081
[21] ZHAO H, KANG W, MA X, et al. Fabrication and catalytic behavior of hierarchically-structured nylon 6 nanofiber membrane decorated with silver nano-particles[J]. Chinese Journal of Catalysis, 2017, 38(1): 73-82.
doi: 10.1016/S1872-2067(16)62545-7
[22] 于丽娜, 王敏, 神领第, 等. 聚丙烯腈纳米纤维载银复合膜绿色制备及其催化性能[J]. 高分子学报, 2014(2): 239-247.
YU Li'na, WANG Min, SHEN Lingdi, et al. Green fabrication and catalytic properties of Ag/APAN nanofibrous composite membranes[J]. Acta Polymerica Sinica, 2014 (2): 239-247.
[23] CHENG P, LIU Y, YI Z B, et al. In situ prepared nanosized Pt-Ag/PDA/PVA-co-PE nanofibrous membrane for highly-efficient catalytic reduction of p-nitrophenol[J]. Composites Communications, 2018(9): 11-16.
[24] HU D M, XIAO Y C, LIU H, et al. Loading of Au/Ag bimetallic nanoparticles within electrospun PVA/PEI nanofibers for catalytic applications[J]. Colloids and Surfaces A: Physicochemical and Engineering Aspects, 2018, 552: 9-15.
doi: 10.1016/j.colsurfa.2018.05.013
[25] HE F G, DU B, SHARMA G, et al. Highly efficient polydopamine-coated poly(methyl methacrylate) nanofiber-supported platinum-nickel bimetallic catalyst for formaldehyde oxidation at room temperature[J]. Polymers, 2019. DOI: 10.3390/polym11040674.
doi: 10.3390/polym11040674
[26] DING Q W, MIAO Y E, LIU T X. Morphology and photocatalytic property of hierarchical polyimide/ZnO fibers prepared via a direct ion-exchange process[J]. ACS Applied Materials & Interfaces, 2013, 5(12): 5617-5622.
[27] MOUSAVI S, SHAHRAKI F, ALIABADI M, et al. Nanofiber immobilized CeO2/dendrimer nanoparticles: an efficient photocatalyst in the visible and the UV[J]. Applied Surface Science, 2019, 479: 608-618.
doi: 10.1016/j.apsusc.2019.02.119
[28] LI Z J, KANG W M, HAN Z B, et al. Hierarchical MnOx@PVDF/MWCNTs tree-like nanofiber membrane with high catalytic oxidation activity[J]. Journal of Alloys and Compounds, 2019, 780: 805-815.
doi: 10.1016/j.jallcom.2018.11.405
[29] SHI Y Z, YANG D Z, LI Y, et al. Fabrication of PAN@TiO2/Ag nanofibrous membrane with high visible light response and satisfactory recyclability for dye photocatalytic degradation[J]. Applied Surface Science, 2017, 426: 622-629.
doi: 10.1016/j.apsusc.2017.06.302
[30] CHOI J S, CHAN S, JOO H, et al. Three-dimensional (3D) palladium-zinc oxide nanowire nanofiber as photo-catalyst for water treatment[J]. Water Research, 2016, 101: 362-369.
doi: S0043-1354(16)30397-9 pmid: 27286471
[31] LUO Y M, JIA Y R, ZHANG D X, et al. Coaxial electrospinning method for the preparation of TiO2@CdS/PVA composite nanofiber mat and investigation on its photodegradation catalysis[J]. Photochemistry and Photobiology, 2016, 92(4): 515-522.
doi: 10.1111/php.12591
[32] HUANG G Y, CHANG W J, LU T W, et al. Electrospun CuS nanoparticles/chitosan nanofiber composites for visible and near-infrared light-driven catalytic degradation of antibiotic pollutants[J]. Chemical Engineering Journal, 2022. DOI: 10.1016/j.cej.2021.134059.
doi: 10.1016/j.cej.2021.134059
[33] ZHANG X D, LIU X J, ZHANG L, et al. Novel porous Ag2S/ZnS composite nanospheres: fabrication and enhanced visible-light photocatalytic activities[J]. Journal of Alloys and Compounds, 2016, 655: 38-43.
doi: 10.1016/j.jallcom.2015.08.202
[34] CHEN H F, YANG J, CHEN H Q, et al. Solar photocatalytic hydrogen energy production using PbS-ZnS heterojunction/electrospun fiber composites[J]. Energy Exploration & Exploitation, 2019, 37(5): 1477-1486.
[35] SUN D K, SHI J W, MA D D, et al. CdS/ZnS/ZnO ternary heterostructure nanofibers fabricated by electrospinning for excellent photocatalytic hydrogen evolution without co-catalyst[J]. Chinese Journal of Catalysis, 2020, 41(9): 1421-1429.
doi: 10.1016/S1872-2067(20)63576-8
[36] WANG S J, LUO T, ZHU J, et al. A facile way to fabricate cellulose-Ag@AgCl composites with photo-catalytic properties[J]. Cellulose, 2016, 23(6): 3737-3745.
doi: 10.1007/s10570-016-1064-1
[37] YU D D, BAI J, LIANG H O, et al. AgI-modified TiO2 supported by PAN nanofibers: a heterostructured composite with enhanced visible-light catalytic activity in degrading MO[J]. Dyes and Pigments, 2016, 133: 51-59.
doi: 10.1016/j.dyepig.2016.05.036
[38] ZHANG M M, LIU M, JIANG Y, et al. Synthesis of immobilized CdS/TiO2 nanofiber heterostructure photocatalyst for efficient degradation of toluene[J]. Water, Air, & Soil Pollution, 2020. DOI: 10.1007/s11270-020-4461-x.
doi: 10.1007/s11270-020-4461-x
[39] ZHOU Z D, PENG X W, ZHONG L X, et al. Electrospun cellulose acetate supported Ag@AgCl composites with facet-dependent photocatalytic properties on degradation of organic dyes under visible-light irradiation[J]. Carbohydrate Polymers, 2016, 136: 322-328.
doi: 10.1016/j.carbpol.2015.09.009 pmid: 26572362
[40] YAR A, HASPULAT B, ÜSTÜN T, et al. Electrospun TiO2/ZnO/PAN hybrid nanofiber membranes with efficient photocatalytic activity[J]. RSC Advances, 2017, 7(47): 29806-29814.
doi: 10.1039/C7RA03699J
[41] 高云莉, 王琛, 冯伟忠, 等. 负载不同形貌Cu2O/PAN纳米纤维膜光催化性能研究[J]. 现代纺织技术, 2021, 29(3): 1-7.
GAO Yunli, WANG Chen, FENG Weizhong, et al. Study on photocatalytic performance of cuprous oxide/polyacrylonitrile nanofiber membranes with different morphologies[J]. Advanced Textile Technology, 2021, 29(3):1-7.
[42] LI Z Q, YUAN C G, GUO Q, et al. Preparation of stable AgNPs@PAN/GO-SH nanocompsite by electro-spinning for effective degradation of 4-nitrophenol, methylene blue and Rhodamine B[J]. Materials Letters, 2020. DOI: 10.1016/j.matlet.2020.127409.
doi: 10.1016/j.matlet.2020.127409
[43] HUANG X X, WANG R, JIAO T F, et al. Facile Preparation of hierarchical AgNP-loaded MXene/Fe3O4/polymer nanocomposites by electrospinning with enhanced catalytic performance for wastewater treatment[J]. ACS Omega, 2019, 4(1): 1897-1906.
doi: 10.1021/acsomega.8b03615
[44] YIN J J, ZHAN F K, JIAO T F, et al. Highly efficient catalytic performances of nitro compounds via hierarchical PdNPs-loaded MXene/polymer nanocomposites synthesized through electrospinning strategy for wastewater treatment[J]. Chinese Chemical Letters, 2020, 31(4): 992-995.
doi: 10.1016/j.cclet.2019.08.047
[45] MIAO L, LIU G J, WANG J D. Ag-nanoparticle-bearing poly(vinylidene fluoride) nanofiber mats as janus filters for catalysis and separation[J]. ACS Applied Materials & Interfaces, 2019, 11(7): 7397-7404.
[46] GOPIRAMAN M, SARAVANAMOORTHY S, BASKAR R, et al. Green synthesis of Ag@Au bimetallic regenerated cellulose nanofibers for catalytic applications[J]. New Journal of Chemistry, 2019, 43(43): 17090-17103.
doi: 10.1039/C9NJ04428K
[47] ZHAO H M, XIA Q S, XING H Z, et al. Construction of pillared-layer MOF as efficient visible-light photocatalysts for aqueous Cr(VI) reduction and dye degradation[J]. ACS Sustainable Chemistry & Engineering, 2017, 5(5): 4449-4456.
[48] MOHAMED A, EL-SAYED R, OSMAN T A, et al. Composite nanofibers for highly efficient photocatalytic degradation of organic dyes from contaminated water[J]. Environmental Research, 2016, 145: 18-25.
doi: S0013-9351(15)30092-X pmid: 26615225
[49] MOHAMED A, OSMAN T A, TOPRAK M S, et al. Visible light photocatalytic reduction of Cr(VI) by surface modified CNT/titanium dioxide composites nanofibers[J]. Journal of Molecular Catalysis A: Chemical, 2016, 424: 45-53.
doi: 10.1016/j.molcata.2016.08.010
[50] WANG L, ZHANG C B, GAO F, et al. Algae decorated TiO2/Ag hybrid nanofiber membrane with enhanced photocatalytic activity for Cr(VI) removal under visible light[J]. Chemical Engineering Journal, 2017, 314: 622-630.
doi: 10.1016/j.cej.2016.12.020
[51] WANG L, ZHANG C B, CHENG R, et al. Microcystis aeruginosa synergistically facilitate the photocatalytic degradation of tetracycline hydrochloride and Cr(VI) on PAN/TiO2/Ag nanofiber mats[J]. Catalysts, 2018. DOI: 10.3390/catal8120628.
doi: 10.3390/catal8120628
[52] YIN X, XIE X Y, SONG L X, et al. The application of highly flexible ZrO2/C nanofiber films to flexible dye-sensitized solar cells[J]. Journal of Materials Science, 2017, 52(18): 11025-11035.
doi: 10.1007/s10853-017-1287-z
[53] YIN X, XIE X Y, SONG L X, et al. Enhanced performance of flexible dye-sensitized solar cells using flexible Ag@ZrO2/C nanofiber film as low-cost counter electrode[J]. Applied Surface Science, 2018, 440: 992-1000.
doi: 10.1016/j.apsusc.2018.01.264
[54] XU F Y, LE Y, CHENG B, et al. Effect of calcination temperature on formaldehyde oxidation performance of Pt/TiO2 nanofiber composite at room temperature[J]. Applied Surface Science, 2017, 426: 333-341.
doi: 10.1016/j.apsusc.2017.07.096
[55] WANG Q, WANG W, YAN B Y, et al. Well-dispersed Pd-Cu bimetals in TiO2 nanofiber matrix with enhanced activity and selectivity for nitrate catalytic reduction[J]. Chemical Engineering Journal, 2017, 326: 182-191.
doi: 10.1016/j.cej.2017.05.110
[56] ZHANG B B, YE Z Y, QIN M, et al. Palladium complex embedded crosslinked polystyrene nanofibers as a green and efficient heterogeneous catalyst for coupling reactions[J]. Journal of Applied Polymer Science, 2021. DOI: 10.1002/app.49666.
doi: 10.1002/app.49666
[57] DENG H Z, XU F Y, CHENG B, et al. Photocatalytic CO2 reduction of C/ZnO nanofibers enhanced by an Ni-NiS cocatalyst[J]. Nanoscale, 2020, 12(13): 7206-7213.
doi: 10.1039/C9NR10451H
[58] QU T, HU J X, DAI X, et al. Electrospinning highly dispersed Ru nanoparticle-embedded carbon nanofibers boost CO2 reduction in a H2/CO2 fuel cell[J]. ACS Applied Materials & Interfaces, 2021, 13(20): 23523-23531.
[59] KANG S, HWANG J. Fabrication of hollow activated carbon nanofibers (HACNFs) containing manganese oxide catalyst for toluene removal via two-step process of electrospinning and thermal treatment[J]. Chemical Engineering Journal, 2020. DOI: 10.1016/j.cej.2019.122315.
doi: 10.1016/j.cej.2019.122315
[60] HAN W G, DONG F, HAN W L, et al. Mn-polyacrylonitrile nanofibers decorated with co-metal-organic frameworks as precursors of CoMnOx catalysts for the combustion of toluene[J]. ACS Applied Nano Materials, 2020, 3(8): 7818-7828.
doi: 10.1021/acsanm.0c01308
[61] ZHANG Z Y, WU X, KOU Z K, et al. Rational design of electrospun nanofiber-typed electrocatalysts for water splitting: a review[J]. Chemical Engineering Journal, 2022. DOI: 10.1016/j.cej.2021.131133.
doi: 10.1016/j.cej.2021.131133
[62] CHEN M X, XIAO C F, WANG C, et al. Fabrication of tubular braid reinforced PMIA nanofiber membrane with mussel-inspired Ag nanoparticles and its superior performance for the reduction of 4-nitrophenol[J]. Nanoscale, 2018, 10(42): 19835-19845.
doi: 10.1039/c8nr06398b pmid: 30334561
[63] WANG X Y, XIAO C F, LIU H L, et al. Robust functionalization of underwater superoleophobic PVDF-HFP tubular nanofiber membranes and applications for continuous dye degradation and oil/water separation[J]. Journal of Membrane Science, 2020. DOI: 10.1016/j.memsci.2019.117583.
doi: 10.1016/j.memsci.2019.117583
[1] ZHOU Wen, YU Jianyong, ZHANG Shichao, DING Bin. Preparation of green-solvent-based polyamide nanofiber membrane and its air filtration performance [J]. Journal of Textile Research, 2023, 44(01): 56-63.
[2] DAI Lu, HU Zexu, WANG Yan, ZHOU Zhe, ZHANG Fan, ZHU Meifang. Combustion and charring behavior of polyphenylene sulfide/graphene nanocomposite fibers [J]. Journal of Textile Research, 2023, 44(01): 71-78.
[3] LI Liang, PEI Feifei, LIU Shuping, TIAN Sujie, XU Mengyuan, LIU Rangtong, HAI Jun. Preparation and characterization of polylactic acid nanofiber drug loaded medical dressings [J]. Journal of Textile Research, 2022, 43(11): 1-8.
[4] ZHANG Changhuan, LI Xianxian, ZHANG Liran, LI Deyang, LI Nianwu, WU Hongyan. Preparation and performance of lithium iron phosphate/carbon black/carbon nanofibers flexible cathode [J]. Journal of Textile Research, 2022, 43(11): 16-21.
[5] WANG Hongjie, HU Zhongwen, WANG He, FENG Quan, LIN Tong. Research progress in one-way water transport textiles and their applications [J]. Journal of Textile Research, 2022, 43(11): 195-202.
[6] CAO Congcong, TANG Longshi, LIU Yuanjun, ZHAO Xiaoming. Research progress of inorganic antibacterial fabrics [J]. Journal of Textile Research, 2022, 43(11): 203-211.
[7] YAO Ying, ZHAO Weitao, ZHANG Desuo, LIN Hong, CHEN Yuyue, WEI Hong. Preparation of dendritic nanofiber membrane induced by hyperbranched quaternary ammonium salt and its properties [J]. Journal of Textile Research, 2022, 43(10): 1-9.
[8] YU Yangxiao, LI Feng, WANG Yuyu, WANG Shanlong, WANG Jiannan, XU Jianmei. Preparation and properties of polypyrole/silk fibroin conductive nanofiber membranes [J]. Journal of Textile Research, 2022, 43(10): 16-23.
[9] ZHOU Xiaoju, HU Zhenglong, REN Yiming, XIE Landong. Fabrication and photocatalyic performance of Bi2MoO6 modified TiO2 nanorod array photocatalyst [J]. Journal of Textile Research, 2022, 43(10): 97-105.
[10] YANG Li, WANG Tao, SHI Xianbing, HAN Zhenbang. Preparation of modified polyacrylonitrile fiber supported MoSx/TiO2 composite photocatalyst and its performance for dye degradation [J]. Journal of Textile Research, 2022, 43(09): 149-155.
[11] LI Weiping, YANG Guixia, CHENG Zhiqiang, ZHAO Chunli. Preparation and properties of polyvinylpyrrolidone/aloe composite nanofiber membrane [J]. Journal of Textile Research, 2022, 43(08): 55-59.
[12] LIU Jiao, CHEN Shaojuan, WU Shaohua. Preparation and properties of silk fibroin/poly(l-lactic acid) nanofiber yarns-based tendon patches [J]. Journal of Textile Research, 2022, 43(08): 60-66.
[13] LIN Qisong, GAO Feng, LÜ Wangyang, CHEN Wenxing. Thickening behaviour and performance of titanium-based polyethylene terephthalate [J]. Journal of Textile Research, 2022, 43(07): 9-16.
[14] QIAN Jiaqi, QU Jian'gang, HU Xiaolin, MAO Qinghui. Preparation and property of reduced graphene oxide/viscose-based BiVO4 photocatalyst [J]. Journal of Textile Research, 2022, 43(06): 100-106.
[15] FEI Jianwu, LÜ Mingze, LIU Liwei, WANG Chunhong, HAN Zhenbang. Construction of air-liquid-solid tri-phase system from bilayer micro/nanofiber membrane and its photocatalytic performance [J]. Journal of Textile Research, 2022, 43(06): 37-43.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd