Journal of Textile Research ›› 2024, Vol. 45 ›› Issue (07): 140-149.doi: 10.13475/j.fzxb.20230900801

• Dyeing and Finishing Engineering • Previous Articles     Next Articles

Preparation of zeolitic imidazolate framework-8 and its adsorption performance on Congo Red

YANG Liang1(), KONG Hanhan1, LI Weilin1, QI Xiaofen1, ZHANG Tianyun1, WANG Xuemei1, LI Wenquan2   

  1. 1. School of Mechanical and Electronical Engineering, Lanzhou University of Technology, Lanzhou, Gansu 730050, China
    2. Lanzhou Sanmao Industrial Co., Ltd., Lanzhou, Gansu 730316, China
  • Received:2023-09-08 Revised:2024-04-12 Online:2024-07-15 Published:2024-07-15

RichHTML

3

PDF (PC)

17

Abstract:

Objective In order to solve the problem that printing and dyeing wastewater is harmful to the environment and difficult to treat, this research aims to prepare an economical and environmentally friendly adsorbent with excellent adsorption effect, and the adsorption performance of ZIF-8 on azo dyes represented by anionic Congo Red dyes was investigated.

Method In this research, 2-methylimidazole and Zn(NO3)2·6H2O were used as raw materials, and deionized water was used as solvent. The proportion of 2-methylimidazole, Zn(NO3)2·6H2O and deionized water was adjusted and they mixed by mechanical stirring to prepare the homogeneous and clear particles of zeolitic imidazolate framework-8 (ZIF-8) material under normal temperature and normal pressure conditions. The structure of the ZIF-8 material was tested by scanning electron microscopy(SEM), infrared spectrometry, X-Ray diffraction, thermogravimetry, BET and other characterization methods. The adsorption performance of the material on dyes was evaluated by the water-bath constant-temperature shaking method, and the factors affecting the adsorption and the adsorption mechanism were analyzed.

Results It was found from SEM images that the ZIF-8 section was smooth, and that the particles were uniform and had a polyhedral structure. Infrared spectra analysis and X-Ray diffraction results showed that the ZIF-8 material was consistent with the finding reported in docoments. Thermogravimetric analysis and specific surface area tests revealed that the thermal cleavage temperature of the ZIF-8 material was 258 ℃, and the ZIF-8 had a good thermal stability. The specific surface area of BET was 869.63 m2/g, the specific surface area of Langmuir was 1 140.03 m2/g, and the average pore size was 3.27 nm. The adsorption equilibrium was reached in a shorter time at the lower initial concentration, and the adsorption amount reached the maximum when the initial concentration was 95 mg/L. It was found that the adsorption would first rise, then fall and finally tend to equilibrium with the increase of ion concentration, and the adsorption amount could reach the maximum when pH was neutral. It was also revealed that the adsorption rate of ZIF-8 could still be maintained at 69% after 4 cycles. The adsorption of ZIF-8 on Congo Red was more in line with the pseudo-second-order model through the fitting of kinetic model, which was dominated by chemical adsorption. The adsorption isotherm model fitting showed that the adsorption of ZIF-8 on Congo Red was in line with the Langmuir model, which belonged to the adsorption of the monolayer molecules. It was believed that the whole adsorption process was an exothermic reaction, and the low temperature was favorable for the adsorption. Under the conditions of 20 ℃ and pH=7, the adsorption effect of ZIF-8 on 95 mg/L Congo Red solution was the best, and the maximum adsorption rate was 671.41 mg/g.

Conclusion ZIF-8 prepared using deionized water as the solvent is found to reduce cost compared to the situation with methanol as the solvent, and the operation is simple and safe compared to other preparation methods. The ZIF-8 particles prepared are uniform and clear, with good thermal stability and large specific surface area. ZIF-8 has better adsorption performance on anionic dyes represented by Congo Red, so it can be applied to the treatment of general anionic dye waste liquid.

Key words: zeolitic imidazolate framework-8, Congo Red, anionic dye, printing and dyeing wastewater, wastewater treatment, adsorption performance, adsorption mechanism

CLC Number: 

  • TS176

Fig.1

Standard curve of Congo Red"

Fig.2

SEM image of ZIF-8"

Fig.3

Infrared spectra of ZIF-8"

Fig.4

XRD patterns of ZIF-8"

Fig.5

Thermogravimetric diagram of ZIF-8"

Fig.6

Nitrogen adsorption-desorption diagram of ZIF-8"

Fig.7

Influence of initial mass concentration on adsorption"

Fig.8

Influence of ion concentration on adsorption"

Fig.9

Influence of pH value on adsorption capacity (a) and Zeta potential (b)"

Fig.10

Cycling performance of ZIF-8"

Fig.11

Adsorption kinetics model. (a) Pseudo-first-order adsorption kinetic model; (b) Pseudo-second-order adsorption kinetic model; (c) Internal diffusion model (IDM)"

Tab.1

Adsorption kinetic parameters"

C0/(mg·L-1) 准二级动力学模型 准一级动力学模型
qe/(mg·g-1) k2/(g·mg-1·min-1) qt/(mg·g-1) R2 k1/min-1 qt/(mg·g-1) R2
15 52.456 3 0.052 4 8.632 0 0.997 2 0.018 3 53.264 1 0.867 5
45 206.238 9 0.087 4 235.360 0 0.997 6 0.004 4 219.385 0 0.925 6
95 415.654 0 0.520 0 325.513 2 0.998 7 0.002 1 452.361 4 0.970 4

Tab.2

Internal diffusion model parameters"

温度/
℃		 表面扩散 中孔扩散 微孔扩散
K1 R 1 2 K2 R 2 2 K3 R 3 2
20 9.126 6 0.995 7 1.672 5 0.911 3 0.012 4 0.110 0
30 9.842 8 0.992 1 0.923 2 0.840 8 0.028 6 0.367 6
40 0.957 0 0.999 3 1.541 6 0.924 9 0.012 8 0.411 0

Tab.3

Adsorption isotherm parameters"


温度/
℃		 Freundlich模型 Langmuir模型
KF n R2 b/
(L·mg-1)		 qm/
(mg·g-1)		 R2
20 103.967 2 2.963 2 0.996 8 0.060 6 670.632 6 0.997 9
30 59.638 9 2.689 1 0.997 4 0.108 4 430.361 0 0.999 1
40 46.310 5 2.736 4 0.997 0 0.160 4 342.698 1 0.998 9

Fig.12

Adsorption isotherm model. (a) Adsorption isotherms of ZIF-8 on Congo Red; (b) Freundlich adsorption isotherm; (c) Langmuir adsorption isotherm; (d) Van't Hoff diagram"

Tab.4

Thermodynamic parameters of adsorption"

温度/
℃		 ΔG/
(kJ·mol-1)		 ΔS/
(J·mol-1·K-1)		 ΔH/
(kJ·mol-1)
20 -12.444 7 -156.802 0 -58.387 7
30 -10.876 7
40 -9.308 7

Fig.13

XRD patterns (a) and FT-IR spectra (b) before and after adsorption of ZIF-8"

[1] 付玮康, 郭筱洁, 潘孟涛, 等. 柳絮纤维生物质炭的制备及其对染料废液中Cr(Ⅵ)的吸附性能[J]. 纺织学报, 2022, 43(12): 8-15.
doi: 10.13475/j.fzxb.20210905908
FU Weikang, GUO Xiaojie, PAN Mengtao, et al. Preparation of biomass charcoal from willow floss fibers and its adsorption performance on Cr(VI) in dye wastewater[J]. Journal of Textile Research, 2022, 43(12): 8-15.
doi: 10.13475/j.fzxb.20210905908
[2] MOK C F, CHING Y C, MUHAMAD F, et al. Adsorption of dyes using poly(vinyl alcohol) (PVA) and PVA-based polymer composite adsorbents: a review[J]. Journal of Polymers and the Environment, 2020, 28(3): 775-793.
[3] HAMAD M T M H, SAIED M S S. Kinetic studies of Congo red dye adsorption by immobilized aspergillus niger on alginate[J]. Applied Water Science, 2021. DOI: 10.1007/s13201-021-01362-z.
[4] AOOPNGAN C, NONKUMWONG J, PHUMYING S, et al. Amine-functionalized and hydroxyl-functionalized magnesium ferrite nanoparticles for congo red adsorp-tion[J]. ACS Applied Nano Materials, 2019, 2(8): 5329-5341.
[5] RADOOR S, KARAYIL J, PARAMESWARANPILLAI J, et al. Adsorption of methylene blue dye from aqueous solution by a novel PVA/CMC/halloysite nanoclay bio-composite: characterization, kinetics, isotherm and antibacterial properties[J]. Journal of Environmental Health Science and Engineering, 2020, 18(2): 1311-1327.
[6] 王宸杨, 贾洁, 李发学. β-环糊精基金属有机框架材料的制备及其对重金属离子的吸附[J]. 纺织学报, 2023, 44(8): 158-166.
WANG Chenyang, JIA Jie, LI Faxue. Preparation of β-cyclodextrin-based metal-organic framework materials and their adsorption of heavy metal ions[J]. Journal of Textile Research, 2023, 44(8): 158-166.
[7] JAMES J B, LIN Y S. Thermal stability of ZIF-8 membranes for gas separations[J]. Journal of Membrane Science, 2017, 532: 9-19.
[8] FUJIWARA A, WATANABE S, MIYAHARA M T. Flow microreactor synthesis of zeolitic imidazolate framework (ZIF)@ZIF core-shell metal-organic framework particles and their adsorption properties[J]. Langmuir, 2021, 37(13): 3858-3867.
doi: 10.1021/acs.langmuir.0c03378 pmid: 33626277
[9] 张磊, MUHAMMAD I P, 王波涛, 等. 不同方法合成ZIF-8及其对有机染料的吸附动力学研究[J]. 内江科技, 2020, 41(2): 147-148.
ZHANG Lei, MUHAMMAD I P, WANG Botao, et al. Synthesis of ZIF-8 by different methods and its adsorption kinetics on organic dyes[J]. Neijiang Science and Technology, 2020, 41(2): 147-148.
[10] 王静, 娄娅娅, 张书涛, 等. ZIF-8的制备及其对染料的吸附和可见光降解[J]. 印染, 2019, 45(19): 44-47.
WANG Jing, LOU Yaya, ZHANG Shutao, et al. Preparation of ZIF-8 and its adsorption and visible light degradation of dyes[J]. China Dyeing & Finishing, 2019, 45 (19): 44-47.
[11] 杨亮, 孔韩韩, 李韦霖, 等. 聚乙烯醇/ZIF-8复合膜的制备及吸附性能[J]. 印染, 2024, 50(2): 72-78.
YANG Liang, KONG Hanhan, LI Weilin, et al. Preparation and adsorption properties of polyvinyl alcohol/ZIF-8 composite membrane[J]. China Dyeing & Finishing, 2024, 50(2): 72-78.
[12] AHMADIJOKANI F, MOLAVI H, BAHI A, et al. Electrospun nanofibers of chitosan/polyvinyl alcohol/ UiO-66/nanodiamond: versatile adsorbents for waste-water remediation and organic dye removal[J]. Chemical Engineering Journal, 2023. DOI: 10.1016/j.cej.2022.141176.
[13] YANG H, GUO X, CHEN R, et al. Enhanced anti-biofouling ability of polyurethane anti-cavitation coating with ZIF-8: a comparative study of various sizes of ZIF-8 on coating[J]. European Polymer Journal, 2021. DOI: 10.1016/j.eurpolymj. 2020.110212.
[14] VENNA S R, JASINSKI J B, CARREON M A. Structural evolution of zeolitic imidazolate framework-8[J]. Journal of the American Chemical Society, 2010, 132(51): 18030-18033.
doi: 10.1021/ja109268m pmid: 21133378
[15] ZHANG H, HOU J, HU Y, et al. Ultrafast selective transport of alkali metal ions in metal organic frameworks with subnanometer pores[J]. Science Advances, 2018. DOI: 10.1126 /sciadv. aaq0066.
[16] WANG Z, HE Y, ZHU L, et al. Natural porous wood decorated with ZIF-8 for high efficient iodine capture[J]. Materials Chemistry and Physics, 2021. DOI: 10.1016/j.matchemphys.2020.123964.
[17] CHU F, ZHENG Y, WEN B, et al. Adsorption of toluene with water on zeolitic imidazolate framework-8/graphene oxide hybrid nanocomposites in a humid atmosphere[J]. RSC Advances, 2018, 8(5): 2426-2432.
[18] XIAO F, CHENG J, FAN X, et al. Adsorptive removal of the hazardous anionic dye Congo red and mechanistic study of ZIF-8[J]. Desalination and Water Treatment, 2018, 101: 291-300.
[19] BHAT S A, ZAFAR F, MONDAL A H, et al. Efficient removal of Congo red dye from aqueous solution by adsorbent films of polyvinyl alcohol/melamine-formaldehyde composite and bactericidal effects[J]. Journal of Cleaner Production, 2020. DOI: 10.1016/j.jclepro.2020.120062.
[20] HAN L-J, GE F-Y, SUN G-H, et al. Effective adsorption of Congo red by a MOF-based magnetic material[J]. Dalton Transactions, 2019, 48(14): 4650-4656.
[21] NAYAK A, SAHOO J K, SAHOO S K, et al. Removal of congo red dye from aqueous solution using zinc oxide nanoparticles synthesised from Ocimum sanctum (Tulsi leaf): a green approach[J]. International Journal of Environmental Analytical Chemistry, 2022, 102(19): 7889-7910.
[22] SINGH N J, WAREPPAM B, KUMAR A, et al. Zeolite incorporated iron oxide nanoparticle composites for enhanced congo red dye removal[J]. Journal of Materials Research, 2023, 38(4): 1149-1161.
[23] DHANAVEL S, NIVETHAA E A K, DHANAPAL K, et al. α-MoO3/polyaniline composite for effective scavenging of Rhodamine B, Congo red and textile dye effluent[J]. RSC Advances, 2016, 6(34): 28871-28886.
[24] DAI J, CHEN T, CHEN Q, et al. Facile synthesis of ZIF-8-lignosulfonate microspheres with ultra-high adsorption capacity for Congo red and tetracycline removal from water[J]. International Journal of Biological Macromolecules, 2023. DOI: 10.1016/j.ijbiomac.2023.124672.
[1] WU Shouying, HUANG Qichao, ZHANG Kaifeng, ZHANG Linping, ZHONG Yi, XU Hong, MAO Zhiping. Construction of catalytic system by FeⅢ(tpy)Cl3 complexes-activated periodate and its catalytic degradation mechanism for dyeing wastewater [J]. Journal of Textile Research, 2024, 45(06): 105-112.
[2] ZHENG Kang, GONG Wenli, BAO Jie, LIU Lin. Preparation and dynamic adsorption properties of amphoteric cellulose porous hydrogel spheres [J]. Journal of Textile Research, 2024, 45(05): 102-112.
[3] LI Fang, ZHANG Yili, WANG Man, MENG Xiangzhou, SHEN Chensi. Acute toxic effects of antimony contaminants on green algae and cyanobacteria [J]. Journal of Textile Research, 2024, 45(04): 169-179.
[4] LU Yaoyao, YE Juntao, RUAN Chengxiang, LOU Jin. Preparation and photocatalytic performance of titanium dioxide/porous carbon nanofibers composite material [J]. Journal of Textile Research, 2024, 45(04): 67-75.
[5] CHEN Rongxuan, SUN Hui, YU Bin. Preparation and photocatalytic properties of N-TiO2/ polypropylene melt-blown nonwovens [J]. Journal of Textile Research, 2024, 45(03): 137-147.
[6] HUANG Biao, ZHENG Li'na, QIN Yan, CHENG Yujun, LI Chengcai, ZHU Hailin, LIU Guojin. Preparation of porous TiO2 particles and their adsorption for ionic dyes [J]. Journal of Textile Research, 2023, 44(11): 167-175.
[7] LI Jingzi, LOU Mengmeng, HUANG Shiyan, LI Fang. Recycling treatment of dyeing wastewater by metal organic framework/graphene composite membrane based on photothermal utilization [J]. Journal of Textile Research, 2023, 44(09): 116-123.
[8] HAN Bo, WANG Yulin, SHU Dawu, WANG Tao, AN Fangfang, SHAN Juchuan. Reactive dyeing using recycled dyeing wastewater [J]. Journal of Textile Research, 2023, 44(08): 151-157.
[9] WANG Chenyang, JIA Jie, LI Faxue. Preparation of β-cyclodextrin-based organic framework materials and their adsorption on heavy metal ions [J]. Journal of Textile Research, 2023, 44(08): 158-166.
[10] SHAO Yanzheng, SUN Jianghao, WEI Chunyan, LÜ Lihua. Preparation and properties of adsorption fiber made from cotton stalk bark microcrystalline cellulose/modified chitosan [J]. Journal of Textile Research, 2023, 44(08): 18-25.
[11] WANG Guoqin, FU Xiaohang, ZHU Yuke, WU Liguang, WANG Ting, JIANG Xiaojia, CHEN Huali. Photodegradation mechanism and pathway of visible light-response mesoporous TiO2 for Rhodamine B [J]. Journal of Textile Research, 2023, 44(05): 155-163.
[12] SUN Jianghao, SHAO Yanzheng, WEI Chunyan, WANG Ying. Preparation and adsorption analysis of sodium alginate/graphene oxide microporous aerogel fiber [J]. Journal of Textile Research, 2023, 44(04): 24-31.
[13] FU Weikang, GUO Xiaojie, PAN Mengtao, SONG Juyan, XI Bojun. Preparation of catkin fiber biochar and its adsorption properties for Cr(VI) in dye wastewater [J]. Journal of Textile Research, 2022, 43(12): 8-15.
[14] ZHENG Linjuan, YU Jia, YIN Chong, LIANG Zhijie, MAO Qinghui. Preparation and photocatalytic properties of cotton fabrics loaded with polymetallic organic framework material [J]. Journal of Textile Research, 2022, 43(10): 106-111.
[15] ZHOU Xiaoju, HU Zhenglong, REN Yiming, XIE Landong. Fabrication and photocatalyic performance of Bi2MoO6 modified TiO2 nanorod array photocatalyst [J]. Journal of Textile Research, 2022, 43(10): 97-105.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd