JOURNAL OF TEXTILE RESEARCH ›› 2008, Vol. 29 ›› Issue (9): 1-4.

• 纤维材料 •     Next Articles

Studies on coagulation process for cellulose liquid crystalline solution

LI Zhenguo;HU Panpan;HU Zuming;LIU Zhaofeng   

  1. State Key Laboratory for Modification of Chemical Fibers and Polymer Materials;Donghua University;Shanghai 201620;China
  • Received:2007-08-02 Revised:2007-11-21 Online:2008-09-15 Published:2008-09-15

Abstract: Liquid crystalline solutions of cellulose in phosphoric acid/poly-phosphoric acid compound solvent were prepared in a kneader.The coagulation rate was measured based on microscopic observation of the moving boundary associated with coagulation.The effect of the nature of the coagulant,temperature of coagulation bath,and cellulose concentration on the coagulation rate was studied.The results show that the molecular size and molecular structure of the coagulant play an important role in determining the rate of coagulation,coagulation rate decreases with increasing molecular volume for the three monohydric alcohols,ethanol,1-propanol and 2-propanol;an Arrhenius-type relationship exist between the coagulation rate and temperature,coagulation rate increases with increasing the temperature of coagulation bath,the activation energy for coagulation increases in the order ethanol<1-propanol<2-propanol;coagulation rate decreases with increasing cellulose concentration in the solution.Based on these studies,the effect of coagulation variables on coagulation process was depicted.

No related articles found!
Viewed
Full text
901
HTML PDF
Just accepted Online first Issue Just accepted Online first Issue
0 0 0 0 0 901

  From Others local
  Times 835 66
  Rate 93% 7%

Abstract
1057
Just accepted Online first Issue
0 0 1057
  From Others local
  Times 985 72
  Rate 93% 7%

Cited

Web of Science  Crossref   ScienceDirect  Search for Citations in Google Scholar >>
 
This page requires you have already subscribed to WoS.
  Shared   
  Discussed   
No Suggested Reading articles found!