JOURNAL OF TEXTILE RESEARCH ›› 2011, Vol. 32 ›› Issue (5): 5-9.

Previous Articles     Next Articles

Study on water soluble PBT and Microfibers

  

  • Received:2010-07-19 Revised:2010-12-19 Online:2011-05-15 Published:2011-05-15

PDF (PC)

549

Abstract: Abstract: The water-soluble polybutylene terephthalate (WSPBT) was prepared through adding other modified monomer when synthesizing the polybutylene terephthalate (PBT). This WSPBT can be crystallization easily and can dissolution in the boiling water. The existence of SIPE was proved by the FTIR analysis. The thermo-gravimetric analysis(TGA) shows that the WSPBT has good thermal stability. The island-in-sea fiber which composed with WSPBT and common PET was prepared through composite spinning. The island-in-sea fiber were set in boiling water about 45 minutes, then water-soluble property of WSPBT can be tested. The relationship of SIPE content in WSPBT and water-solubility property was discussed.

Key words: water-soluble polyester, crystallization, microfiber, water-soluble property

[1] . Miscibility and crystallization properties of biodegradable poly (3-hydrozybutyrate-co-3-hydroxyvalerate)/poly (lactic acid) blends [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(08): 1-8.
[2] . Preparation and properties of superhydrophobic conductive polyethylene terephthalate fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(08): 88-94.
[3] . Preparation of waterborne polyurethane coating by mechanical foaming based on response surface methodology [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(07): 95-099.
[4] . Preparation and properties of bicomponent spunbond-spunlance nonwoven materials with gradient structure [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(05): 56-61.
[5] . Prediction of pore sizes of polyester/polyamide 6 hollow segmented-pie microfiber nonwovens [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(01): 56-61.
[6] . Crystallization behavior of bio-based polyamide 56 fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(12): 7-13.
[7] . Properties of crosslinking agent modified microfiber synthetic leather base [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(09): 101-108.
[8] . Crystallization behavior and mechanical properties of electrospun polyester/palm fiber-based activated carbon composite  [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(08): 6-10.
[9] . Crystallization behavior and spherulites morphology of stereocompolexed poly(lactic acid)s with different molecular weights [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(2): 27-0.
[10] . Influence of oligomer contents on melt spinning process of poly (lactic acid) [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(8): 133-0.
[11] . Recovery of terephthalic acid from waste of alkali deweighting finishing of polyester using DMF through adductive crystallization [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(10): 67-0.
[12] . Preparation of TiO2 photocatalysts doped with transition metal ions by adsorption phase synthesis [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(3): 20-26.
[13] CONG Sen-Zi, QU Ming-Hai.   Development of anionic polyester/polyamide microfibers [J]. JOURNAL OF TEXTILE RESEARCH, 2012, 33(5): 11-14.
[14] . Wrinkle resistant finishing of silk by acetylating [J]. JOURNAL OF TEXTILE RESEARCH, 2012, 33(12): 44-48.
[15] CHEN Haizhen. Influence of nano-TiO2 on crystallization kinetics of polyester [J]. JOURNAL OF TEXTILE RESEARCH, 2010, 31(4): 25-29.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd