Application of wool keratin solution in wool fabric shaping

  

  • Received:2014-03-24 Revised:2014-10-10 Online:2015-04-15 Published:2015-04-20
  • Contact: 姚金波 YAO Jin-Bo E-mail:yao-yaojinbo@tjpu.edu.cn

PDF (PC)

458

Abstract:

The wool fabric was finished with self-made wool keratin solution, and reasonable finishing process parameters were selected by orthogonal experiments. The result indicate that the optimal finishing process of wool fabric was that the dosage of wool keatin solution was 15% (o.w.f), the processing temperature was 75℃, the processing time was 60 min and liquor ratio was 1:25. The performance of before and after the finishing of wool fabric was compared, the felting shrinkage of finishing wool fabric was decreased from 17.85% to 4.1%, the wrinkle recovery angle was increased from144.2 ° to 215 ° , respectively. Meanwhile the breaking strength was improved and breaking elongation was decreased slightly, and the wool fabric shaping effect is improved.

Key words: shaping, felting shrinkage, wrinkle recovery, mechanical property

[1] . Tensile mechanical properties simulation of viscose woven fabrics based on ABAQUS [J]. Journal of Textile Research, 2018, 39(09): 39-43.
[2] . Development of new fluoroethylene vinyl ether reinforcement membrane and its mechanical properties [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(07): 50-54.
[3] . Influence of humidity and temperature on properties of sized polyester/cotton 65/35 yarn [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(06): 70-74.
[4] . Preparation and properties of collagen/high-molecular weight chitosan composite fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(05): 8-13.
[5] . Biological degumming of oil-flax fibers based on radio frequency treatment [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(03): 73-78.
[6] . Development and property evaluation of fake knitted denim fabric [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(03): 45-49.
[7] . Finite element simulation on tensile mechanical properties of three-elementary weave fabric [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(11): 41-47.
[8] . Structure design and handle evaluation of warp knitted denim [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(09): 45-50.
[9] . Crystallization behavior and mechanical properties of electrospun polyester/palm fiber-based activated carbon composite  [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(08): 6-10.
[10] . Preparation and properties of ethylene-tetrafluoroethylene copolymer fabric [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(05): 43-48.
[11] . Relationship bepure cotton fabruc's wrinkle recovery angle and its organizatonal structure parameters [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(04): 46-49.
[12] . Measurement for fabric wrinkle resistance by simulating actual wear [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(03): 56-60.
[13] . Influence of inorganic fillers on properties of polyamide wet-coating trademark fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(03): 114-121.
[14] . Electrical and mechanical properties of conductive polytrimethylene terephthalate / polyaniline composite yarns [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(02): 40-46.
[15] . Mechanical properties in  wool fibers in engineering anhydrous dyeing using supercritical carbon dioxide [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(02): 53-59.
Viewed
Full text
465
HTML PDF
Just accepted Online first Issue Just accepted Online first Issue
0 0 0 0 0 465

  From Others local
  Times 248 217
  Rate 53% 47%

Abstract
274
Just accepted Online first Issue
0 0 274
  From Others local
  Times 180 94
  Rate 66% 34%

Cited
Web of Science  Crossref   ScienceDirect  Search for Citations in Google Scholar >>
 
This page requires you have already subscribed to WoS.
  Shared   
  Discussed   
[1] . [J]. JOURNAL OF TEXTILE RESEARCH, 1987, 8(02): 41 -44 .
[2] . [J]. JOURNAL OF TEXTILE RESEARCH, 1998, 19(06): 56 -59 .
[3] . [J]. JOURNAL OF TEXTILE RESEARCH, 1995, 16(01): 7 -10 .
[4] . [J]. JOURNAL OF TEXTILE RESEARCH, 1996, 17(01): 20 -23 .
[5] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(04): 36 -37 .
[6] . [J]. JOURNAL OF TEXTILE RESEARCH, 1990, 11(04): 33 -36 .
[7] . [J]. JOURNAL OF TEXTILE RESEARCH, 1987, 8(11): 0 .
[8] . [J]. JOURNAL OF TEXTILE RESEARCH, 1985, 6(07): 58 -59 .
[9] . [J]. JOURNAL OF TEXTILE RESEARCH, 1990, 11(12): 28 -31 .
[10] . [J]. JOURNAL OF TEXTILE RESEARCH, 1995, 16(02): 8 -12 .
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd