Preparation and characterization of plasticizing melting system consisting of cellulose diacetate and plasticizers

  

  • Received:2015-11-13 Revised:2016-01-08 Online:2016-09-15 Published:2016-09-19

Abstract:

Cellulose diacetate (CDA) has high melting temperature, and is an important dervative of cellulose. In HAAKE Rheocord, the plasticizing melting systems of cellulose diacetate (CDA)/ ionic liquid 1-ethyl-3-methylimidazolium acetate ([EMIM]Ac) and CDA/ EMIM]Ac/ dimethyl sulfoxide (DMSO) were prepared. The curves of temperature-time and torque-time in the process of two plasticizing melting systems were analyzed respectively. The structures and performances of the plasticizing melting systems were investigated by XRD, TGA and rheometer, respectively. The results show that, [EMIM]Ac is so effective a plasticizer for CDA that the plasticizing melting system of CDA/[EMIM]Ac is a homogeneous one. DMSO insteaded of the part of [EMIM]Ac, which not only can reduce costs, more to promote plasticizing effect of [EMIM]Ac. The melt processing stability of the plasticizing melting system of CDA/[EMIM]Ac and CDA/[EMIM]Ac/DMSO is good because their thermal decomposition temperature is well above their melt flow temperature, although their thermal decomposition temperature are lower than that of raw CDA.

Key words: ionic liquid, demethyl sulfoxide, cellulose diacetate, cellulose diacetate, plasticizing melting

[1] . Alkali deweighing of polyester fabrics using alkyl imidazolium Gemini ionic liquid [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(01): 79-83.
[2] . Solubility and spectral characteristic of feather and down in different dissolution systems [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(04): 27-31.
[3] . Influence of asymmetry imidazolium-based ionic liquids on retarding dyeing performance of acrylic fiber [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(10): 68-72.
[4] . Preparation and characterization of lauric acid cellulose ester and its film properties [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(01): 11-15.
[5] . Preparation of wool keratin membranes prepared by ionic liquids method and reduction  C method [J]. JOURNAL OF TEXTILE RESEARCH, 2015, 36(06): 55-0.
[6] . Die swell behavior of cellulose diacetate spinning dope [J]. JOURNAL OF TEXTILE RESEARCH, 2015, 36(04): 7-0.
[7] . Ionic liquid as novel solvent in application of preparation of high-value added cellulose fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(2): 133-0.
[8] YU QIN. Rheological property of cellulose diacetate spinning dope [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(6): 8-12.
[9] RONG Zhen, CHEN Yun, TANG Shi-Jun. Components separation of wastes polyester-cotton blended textile with ionic liquid dessolving method [J]. JOURNAL OF TEXTILE RESEARCH, 2012, 33(8): 24-29.
[10] SHI Na, WU Zhi-Yun, WANG Shao-Peng, GAN Sheng-Hua. Recovery of waste polyester textiles via solvent method [J]. JOURNAL OF TEXTILE RESEARCH, 2012, 33(7): 31-36.
[11] . Degradation behavior of cellulose in imidazolium-based ionic liquids [J]. JOURNAL OF TEXTILE RESEARCH, 2012, 33(11): 42-46.
[12] YUAN Jiu-Gang;WANG Qiang;FAN Xuerong;ZHOU Lihua;FENG Fei. Hydrophilic surface modification of wool by ionic liquid/protease treatment [J]. JOURNAL OF TEXTILE RESEARCH, 2010, 31(3): 83-87.
[13] SONG Jun;TAN Xiaorui ;CHENG Bowen ;JI Xiujie ;ZANG Hongjun ;XIA Yucong ;TANG Zanlin. Rheological behavior of cellulose solution with [AMIM]Cl as solvent [J]. JOURNAL OF TEXTILE RESEARCH, 2010, 31(11): 11-15.
[14] YUAN Jiugang;FAN Xuerong;WANG Qiang . Modification of wool fibers using ionic liquid [J]. JOURNAL OF TEXTILE RESEARCH, 2008, 29(8): 60-62.
[15] CHENG Lingyan;LIU Weiwei;ZHANG Yumei;WANG Huaping . Application of ionic liquids in natural polymer materials [J]. JOURNAL OF TEXTILE RESEARCH, 2008, 29(2): 129-132.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!