Influence of dye solution pH value on dyeing effects and antibacterial properties of wool fabrics dyed with tea natural dye

  

  • Received:2016-02-01 Revised:2016-05-21 Online:2016-11-15 Published:2016-11-23

Abstract:

Tieguanyin tea extract was used as natural dye to dye wool fabrics directly at pH vallues of 3.5, 5.5 (pH of original tea extract), 7.5 and 9.5. The antibacterial properties of dyed wool fabrics were studied. The results indicated that dye solution pH value has great influence on K/S value and color of wool fabrics. When the pH value of dye solution was 5.5, the dyed wool fabric exhibited the maximum K/S value. The dyed wool fabrics have good rubbing and washing fastness, but poor sunlight fastness. The fabrics became darker under light, and the effect of light decreased as dye solution pH value rose. When dye solution pH value was 5.5, the antibacterial rate of dyed wool fabrics to Escherichia coli and Staphylococcus aureus was highest, at 98.9% and 93.2%, respectively. The antibacterial rate decreased when dye solution was more acidic or alkaline, especially the dye solution was alkaline.

Key words: tea natural dye, wool fabric, pH value, antibacterial property

[1] . Antibacterial and hydrophilic finishing of moisture absorption and sweat transport polyester knitted fabric [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(05): 74-79.
[2] . Preparation and antibacterial and dyeing properties of chitosan grafted antibacterial viscose fiber  [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(04): 9-13.
[3] . Antibacterial dyeing of wool fabric with nano prodigiosins produced by microorganism [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(02): 91-96.
[4] . Influence of pH value on characteristic colors of Chinese traditional costumes [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(01): 84-88.
[5] . Synthesis and performance evaluation of mothproof naphthoquinone pigments for wool fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(10): 70-74.
[6] . Preparation and properties of nonwoven loofah [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(08): 22-27.
[7] . Influence of rotating-drying model on properties of wool fabric drying in domestic dryer [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(07): 69-74.
[8] . Preparation ana durable antibacterial fabric loaded with doped nano-TiO2 [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(06): 163-168.
[9] . Sizing of polylactic acid filaments at lower temperature [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(03): 85-90.
[10] . Preparation and antibacterial property of high-efficiency low-resistance polyacrylonitrile / graphene nanofiber membrane for gas filtration [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(02): 26-33.
[11] . Preparation and characterization of sliver nanoparticles/TiO2/cellulose acetate composite nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(4): 15-0.
[12] . Fluorine-free water repellent finish of worsted fabric [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(3): 114-0.
[13] . Influence of nano silver loading on dyeing property of cotton fabrec [J]. JOURNAL OF TEXTILE RESEARCH, 2015, 36(07): 61-0.
[14] . Dyeing kinetics and thermodynamics of sorghum husk colorant onto wool fabric [J]. JOURNAL OF TEXTILE RESEARCH, 2015, 36(03): 70-0.
[15] . Dyeing properties of HTCC treated wool fabrics with acid dyes [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(8): 59-0.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!