Preparation of long-afterglow luminescence regenerated cellulose fiber

  

  • Received:2016-01-05 Revised:2016-04-20 Online:2016-12-15 Published:2016-12-21

Abstract:

Silane coupling agent (KH-570) was used to modify the rare-earth strontium aluminate luminescent powder, which has good stability in aqueous solution. The  long-afterglow luminescent regenerated cellulose fibers were prepared regenerated cellulose fibers (prepared from novel NaOH/thiourea/urea solvent system) and the treated rare earth strontium aluminate powder as an additive by wet spinning. The luminescent fiber samples were characterized by Fourier transmission infrared spectroscopy, X-ray diffeaction a tensile tester, and a long-afterglow luminescent tester, respectively. The experimental results showed that the coupling agent was coated on the rare-earth strontium aluminate powder by Si—O—AI chemical bonds. After the coupling process, the luminescent fiber has smooth appearance and the diameter was about 60 μm. The structure of rare-earth strontium aluminate and cellulose Ⅱaluminate in the fiber at the same time, which were not affected by each other. Tensile properties increased by 10%. The initial luminescent intensity was 0.82 cd / m².

Key words: rare-earth strontium aluminate, coupling agent, regenerated cellulose fiber, wet spinning

[1] . Preparation and properties of collagen/high-molecular weight chitosan composite fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(05): 8-13.
[2] . Surface modification of Iron oxide yellow and its application in ultra-high molecular weight polyethylene [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(02): 86-90.
[3] . Preparation and characterization of drug-loading regenerated bacterial cellulose fiber [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(05): 14-18.
[4] . Preparation of keratin/multi-walled carbon nanotubes composite fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(02): 21-25.
[5] . Molecular interactions and characterization of sodium alginate / antarctic krill protein / polyvinyl alcohol composite fiber [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(02): 7-13.
[6] . Preparation and property research of regenerated silk fibroin filaments using CaCl2-formid acid system [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(2): 1-0.
[7] . Study of mechanical properties and pore structure of cellulose fibers regenerated from two ionic liquids by dry-wet spinning [J]. JOURNAL OF TEXTILE RESEARCH, 2015, 36(02): 1-0.
[8] . Structure and properties of cellulose fibers from 1-ethyl-3-methylimidazolium acetate by dry-wet spinning with small gap [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(5): 1-0.
[9] . Caking property of the basalt fiber geogrid with the asphalt [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(5): 21-24.
[10] . Research on novel Ag-loaded antibacterial cotton fabric [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(5): 82-85.
[11] . Comprehensive evaluation of properties of new regenerated cellulose fiber yarns [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(3): 35-39.
[12] Qi LU. Study on Application of Titanate Coupling Agent in CaCO3-filled SF/PVA Blend Films [J]. JOURNAL OF TEXTILE RESEARCH, 2010, 31(8): 12-15.
[13] Halidan Mamat;Wumanjiang Ali. Study on spinning technics of cellulose carbamate Fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2009, 30(02): 5-8.
[14] LI Li;LU Lei;TIAN Jianshu;DAI Lixing. Spinnability of silk fibroin solution containing xanthate [J]. JOURNAL OF TEXTILE RESEARCH, 2007, 28(12): 5-8.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!