Printing performance of UV curable waterborne polyurethane acrylate adhesive

  

  • Received:2015-01-08 Revised:2015-11-17 Online:2016-03-15 Published:2016-03-16

Abstract:

In order to study the effect of UV curing on the printing performance, polyurethane was synthesized from isophoronediisocyanate and polyethylene glycol as the main raw material, then the pentaerythritol triacrylate was employed as blocking agent to synthesis polyurethane acrylate(PUA). The structure of PUA was analyzed by FTIR. The PUA, monomer and photoinitiator were mixed and then applied in fixation of pigment printing via UV irradiation. The effects of component content and UV irradiation time on the printing fabric fastness, K/S value, hand feeling and the printed pattern definition were studied. It indicated that under the condition of 25% PUA, 6% monomer, 5% photoinitiator, UV irradiation 60 s, the washing fastness, dry and wet rubbing fastness of printed fabric can reach 5 grade, 4-5 grade and 3 grade, respectively. The printing patterns also show excellent definition.

Key words: polyurethane acrylate, UV curable, pigment printing, definition

[1] . Synthesis of dihydroxyethyl-terminated polysiloxane and its application in preparation of silicone-acrylate emulsions [J]. Journal of Textile Research, 2016, 37(2): 112-118.
[2] . Influence of inkjet printing parameters on imagine definition of coated pigment ink inkjet printing [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(08): 72-76.
[3] . Syhthsis and printing performances of waterborne polyurethane coating modified by hydroxyl silicone oil [J]. Journal of Textile Research, 2015, 36(11): 82-86.
[4] . Research of polyacrylate/nano-ZnO composite emulsion and its application on textile pigment printing [J]. JOURNAL OF TEXTILE RESEARCH, 2015, 36(08): 78-83.
[5] . Preparation and performance characterization of nano-SiO2 printed fabric with snow camouflage protective properties [J]. Journal of Textile Research, 2015, 36(06): 77-83.
[6] . Influence of novel thickening system EcopO-2 on hand feeling of pigment printing fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(8): 89-0.
[7] . Synthesis and performance of polyacrylate latex modified with double terminated acryloyloxy-propyl polysiloxane [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(12): 90-0.
[8] . Application of super soft pigment printing technology on cotton fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(10): 101-0.
[9] . Synthesis of double terminated acryloyl-polyether silicon oil and property of its modified polyacrylate latex [J]. JOURNAL OF TEXTILE RESEARCH, 2012, 33(10): 72-78.
[10] . The application of microencapsulated organic pigment in pigment printing [J]. JOURNAL OF TEXTILE RESEARCH, 2010, 31(8): 97-102.
[11] Wei WAN;Sha LI. Study of the preparations and properties of the novel eco-friendly ultralow solid containing rate emulsion thickener [J]. JOURNAL OF TEXTILE RESEARCH, 2010, 31(8): 61-67.
[12] DONG Jianpeng;WU Minghua;QI Dongming. Application of polymerizable emulsifier on preparation of pigment printing binder [J]. JOURNAL OF TEXTILE RESEARCH, 2010, 31(6): 100-105.
[13] YANG Jianjun;ZHANG Jian′an;WU Qingyun;WU Mingyuan;QU Xianchao;CUI Guoting;WANG Xiaojun;TANG Lidao. Ketone-hydrazide crosslinking polyurethane-acrylate pigment printing binder [J]. JOURNAL OF TEXTILE RESEARCH, 2008, 29(2): 68-72.
[14] DONG Junzhe;FANG Kuanjun;ZHANG Xia;FU Shaohai;TIAN Anli;WANG Chaoxia;JIANG Xue. Application of glycidyl methacrylate modified polyacrylate binder [J]. JOURNAL OF TEXTILE RESEARCH, 2007, 28(7): 62-64.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
[1] . [J]. JOURNAL OF TEXTILE RESEARCH, 1984, 5(08): 64 .
[2] . [J]. JOURNAL OF TEXTILE RESEARCH, 1984, 5(09): 19 -23 .
[3] . [J]. JOURNAL OF TEXTILE RESEARCH, 1987, 8(01): 49 -52 .
[4] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(03): 64 -65 .
[5] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(04): 94 -95 .
[6] . [J]. JOURNAL OF TEXTILE RESEARCH, 1990, 11(04): 14 -17 .
[7] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(05): 15 -16 .
[8] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(05): 17 -18 .
[9] . [J]. JOURNAL OF TEXTILE RESEARCH, 1981, 2(04): 34 -37 .
[10] . [J]. JOURNAL OF TEXTILE RESEARCH, 2003, 24(06): 35 -36 .