Preparation and characterization of boric acid cross-linking sodium alginate / krill protein composite fiber

  

  • Received:2017-06-13 Revised:2017-10-16 Online:2018-03-15 Published:2018-03-09

Abstract:

In order to solve the swelling problem of sodium alginate / krill protein(SA /AKP) composite fiber in salt solution, salt resistant SA/AKP composite fiber was prepared by cross-linking reaction of boric acid with composite fiber. Fourier transform infrared spectroscopy, thermogravimetric analysis, differential scanning calorimeter and X-ray diffraction were used to study the chemical structure, thermal properties and crystallinity of composite fiber. The relationship between cross-linking degree and fiber morphology was investigated, and the correlation between fiber mechanical properties and cross-linking temperature was evaluated. The results show that the B—O bond is formed by the reaction between boric acid and sodium alginate. The swelling degree of the SA/AKP composite fiber decreases and the equilibrium of the fiber is balanced at 30 min and 80 ℃ after the cross-linking time is prolonged and the cross-linking temperature increases. The swelling degree of the cross-linking fiber can be reduced to 82.30% by 136.99%, and the salt resistance of the fiber is improved obviously. At the point, the breaking strength of the fiber is 2.18 cN/dtex. The breaking strength of the cross-linking fibers with the cross-linking temperature firstly increased and then decreases, and a longitudinal groove structure exists on the surface of the cross-linking fiber and the non-cross-linking fiber. After the cross-linking, the fiber was treated with salt solution, the surface still has the groove structure.

Key words: sodium alginate, krill protein, composite fiber, boric acid, salt otlerance, cross-linking reaction

[1] . Preparation and properties of collagen/high-molecular weight chitosan composite fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(05): 8-13.
[2] . Preparation and characterization of sheath-core energy storage and thermo-regulated composite fibers of polyamide 6 [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(04): 1-8.
[3] . Molecular interactions and characterization of sodium alginate / antarctic krill protein / polyvinyl alcohol composite fiber [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(02): 7-13.
[4] . Research and development of graphene composite fibers and fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(10): 170-0177.
[5] . Mechanical properties and hand style comparison of two kinds of elastic fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(7): 42-0.
[6] . Preparation of alginate-chitosan phase change heat storage microcapsules [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(2): 18-0.
[7] . Thermal property of protein modified cellulose composite fiber [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(11): 15-.
[8] . Analysis on materials of sodium alginate spinning solutions [J]. JOURNAL OF TEXTILE RESEARCH, 2010, 31(2): 1-6.
[9] WANG Qun;QI Lu . Properties of sericin /PVA membrane modified by boric acid [J]. JOURNAL OF TEXTILE RESEARCH, 2008, 29(7): 6-8.
[10] QIAN Jianhua;SUN Fu;LING Ronggen. Preparation and property of anionic polyester fiber [J]. JOURNAL OF TEXTILE RESEARCH, 2007, 28(4): 16-18.
[11] ZONG Lihua;JIN Xiangyu;YIN Baopu. Alkali deweighting treatment of sea-island composite fiber nonwoven [J]. JOURNAL OF TEXTILE RESEARCH, 2007, 28(3): 49-52.
[12] SUN Shiyuan;ZHAO Qingfu;XUE Yuan;JIANG Xiaowei;DOU Haiping. Development of durable water-repellent PP/PE heat-adhesive fiber [J]. JOURNAL OF TEXTILE RESEARCH, 2007, 28(2): 14-16.
[13] WANG Xuejuan;TANG Yi;WU Weiyu;XU Jianjun;YE Guangdou. Research on collagenPPVA composite f ibers with glutaraldehyde as cross2linker [J]. JOURNAL OF TEXTILE RESEARCH, 2007, 28(11): 13-16.
[14] YANG Qing-bin;LI Ke-rang;LIU Yi-xin;YU Wei-dong. Mechanical property of composite fiber of soybean protein/polyvinyl alcohol [J]. JOURNAL OF TEXTILE RESEARCH, 2006, 27(10): 70-73.
[15] QIN Yi-min. Dyeing and finishing effluent treatment with chitosan and sodium alginate [J]. JOURNAL OF TEXTILE RESEARCH, 2005, 26(5): 137-139.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!