Preparation and application of environmental flame-retarded silicone-acrylic flocking adhesive

  

  • Received:2017-08-15 Revised:2018-02-28 Online:2018-06-15 Published:2018-06-15

Abstract:

In order to develop high-added value and environment-friendly flocking adhesives, a flocking adhesive featured low-temperature curing, no formaldehyde releasing, alkylphenol ethoxylates (APEO) and flame-retardancy was synthesized by blending an organic and inorganic compound retardant in semi-continuous emulsion polymerization using ethyl acrylate, butyl acrylate, methyl methacrylate and acrylic acid as polymer monomers. The influence of different retardants, mass ratio of retardants, retardant amount, synergist amount on the flocking were investigated. The result show that flocking adhesive (FR) with 30% retardant (mass ratio of ammonium polyphosphate and FR-5 is 3:1) and 10% organic montmorillonite has properties with flocking fastness, hand feeling and flame-retardancy.

Key words: electrostatic flocking, adhesive, acrylate, alkylphenol ethoxylates, ammonium polyphosphate, flame-retardant, environment-friendly

[1] . preparation of 2-(dimethylamino) ethyl methacrylate grafted by bacterial cellulose aerogels [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(03): 1-6.
[2] . Synthesis of integrated polyurethane acrylate and application thereof in photo-curable ink-jet printing [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(02): 97-105.
[3] . Anti-wrinkle finishing of organosilicone modified polyurethane/acrylate copolymer emulsion for cotton fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(01): 89-93.
[4] . Construction of mercapto-potassium persulfate surface-initiating system and application of grafting on feather surface [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(12): 14-19.
[5] . Synthesis and properties of hydrophilic antistatic polyester masterbatch by melt blending [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(07): 6-10.
[6] . Preparation and its sizing properties of starch-poly(methyl aceylate) size catalyzed by horseradish peroxidase [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(06): 69-74.
[7] . Sizing properties of feather keratin-graft-polyester/cotton warp yarns poly (acrylic acid-co-methyl arylate) for polyester/cotton warp yarns [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(05): 75-79.
[8] . Synthesis and application performance of polyacrylate modified silica sol [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(05): 86-92.
[9] . Synthesis and properties of waterborne polyacrylate coating dyeing binder [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(04): 90-96.
[10] . Preparation and characterization of photodynamic antimicrobial polymethyl methacrylate-co-methacrylic acid electrospun nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(03): 18-22.
[11] . Preapration and characterization of photodynamic antimicrobial poly(methyl mecthacrylate-co-methacrylic acid) electrospun nanofibrous membrane [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(02): 1-6.
[12] . Printing performance of UV curable waterborne polyurethane acrylate adhesive [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(3): 82-0.
[13] . Synthesis of dihydroxyethyl-terminated polysiloxane and its application in preparation of silicone-acrylate emulsions [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(2): 112-0.
[14] . Thermal degradation behaviors and kinetics of intumescent flame-retardant cotton fabric [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(12): 81-86.
[15] . Preparation and application of fluorine-containing acrylate copolymer emulsion as finishing agent [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(09): 100-105.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!