Journal of Textile Research ›› 2020, Vol. 41 ›› Issue (01): 15-20.doi: 10.13475/j.fzxb.20190201606

• Fiber Materials • Previous Articles     Next Articles

Preparation of cotton stalk bast cellulose/graphene oxide fiber and its mechanical properties and adsorption capacity

LI Zhenqun, XU Duo, WEI Chunyan(), QIAN Yongfang, LÜ Lihua   

  1. School of Textile and Material Engineering, Dalian Polytechnic University, Dalian, Liaoning 116034, China
  • Received:2019-02-15 Revised:2019-08-22 Online:2020-01-15 Published:2020-01-14
  • Contact: WEI Chunyan E-mail:weicy@dlpu.edu.cn

RichHTML

3

PDF (PC)

189

Abstract:

In order to improve the adsorption capacity of cellulose-based adsorbent fibers for cationic methylene blue dyes and the fiber strength, cotton stalk cellulose/graphene oxide (GO) fibers containing different mass fractions of GO were prepared by ultrasonic dispersion method and wet spinning method. The morphology and structure of the materials were analyzed by transmission electron microscopy, scanning electron microscopy and Fourier transform infrared spectroscopy. The effects of GO content on the breaking strength and adsorption capacity of the fibers were discussed. Fitting analysis was conducted on the experimental data of adsorption capacity. The results show that the breaking strength of the fiber increases first and then decreases with the increase of mass fraction of GO. When the mass fraction of GO was 0.4%, the fiber breaking strength peaked at 31.12 cN, which is 84% stronger than that without adding GO. The amount of methylene blue adsorption increases with the increase of GO mass fraction. The adsorption process conforms to the pseudo-second-order adsorption kinetic models and Langmuir isotherms adsorption model. The adsorption is related monolayer molecules, and the adsorption process is a spontaneous exothermic reaction.

Key words: cotton stalk bast cellulose, graphene oxide, wet spinning, methylene blue, adsorption capacity

CLC Number: 

  • TS102.2

Fig.1

Effect of GO content on fiber strength"

Fig.2

Effect of GO content on adsorption capacity"

Fig.3

Effect of adsorption time on adsorption capacity"

Tab.1

Effect of temperature on adsorption properties"

温度/K 吸附量/(mg·g-1) 去除率/%
303 9.83 98.3
313 9.58 95.8
323 7.91 79.1

Tab.2

Effect of pH value on adsorption properties"

pH值 吸附量/(mg·g-1) 去除率/%
6 8.98 89.8
8 9.87 98.7
10 9.99 99.9

Fig.4

Effect of MB concentration on adsorption capacity"

Fig.5

Fitting results of pseudo-first-order(a),pseudo-second-order(b)adsorption kinetic models and intraparticle diffusion kinetic models(c)"

Tab.3

Adsorption kinetic parameters for different kinetic models"

温度/K Langmuir等温吸附模型 Freundlich等温吸附模型
qm KL R2 1/n KF R2
303 23.96 83.67 0.999 0.175 13.52 0.983
313 19.28 56.01 0.985 0.168 11.22 0.984
323 16.75 55.5 0.997 0.282 7.24 0.817

Fig.6

Fitting results of Langmuir(a)and Freundlich(b)isothermal adsorption model"

Fig.7

TEM image of GO"

Fig.8

SEM images of fiber surface. (a) Cotton stalk cellulose fibers; (b) Cotton stalk bast cellulose/GO fibers"

Fig.9

FT-IR spectra of GO"

[1] AHMARUZZAMAN M, REZA R A, AHMED J K, et al. Scavenging behavior of schumannianthus dichotomus-derived activated carbon for the removal of methylene blue from aqueous phase[J]. Environmental Progress & Sustainable Energy, 2015,33(4):1148-1157.
[2] WANG M, CAI L, JIN Q, et al. One-pot composite synjournal of three-dimensional graphene oxide/poly(vinyl alcohol)/TiO2 microspheres for organic dye removal[J]. Separation & Purification Technology, 2017,172(Complete):217-226.
[3] LI Y, XIAO H, PAN Y, et al. Novel Composite adsorbent consisting of dissolved cellulose fiber/microfibrillated cellulose for dye removal from aqueous solution[J]. ACS Sustainable Chemistry & Engineering, 2018,6(5):6994-7002.
[4] 黄瑶瑶. 农业废弃物作为生物质吸附剂对废水处理的研究进展[J]. 应用化工, 2017,46(2):173-178.
HUANG Yaoyao. Research progress of agricultural waste as a biomass adsorbent for wastewater treatment[J]. Applied Chemical Industry, 2017,46(2):173-178.
[5] 孙凤玲, 王吟. 天然生物质水凝胶吸附材料研究进展[J]. 材料导报, 2016,30(9):137-143.
SUN Fengling, WANG Yin. A review about hydrogel adsorbents produced from natural biomass[J]. Materials Reports, 2016,30(9):137-143.
[6] BAI Q, XIONG Q, LI C, et al. Hierarchical porous cellulose/activated carbon composite monolith for efficient adsorption of dyes[J]. Cellulose, 2017,24(10):1-15.
doi: 10.1007/s10570-016-1105-9
[7] GUO X, QU L, TIAN M, et al. Chitosan/graphene oxide composite as an effective adsorbent for reactive red dye removal[J]. Water Environment Research, 2016,88(7):579-588.
doi: 10.2175/106143016X14609975746325 pmid: 27329054
[8] 周彩云, 邓娟, 朱君妍, 等. 活化氧化石墨烯的制备及对甲基橙的吸附[J]. 工业水处理, 2016,36(5):66-70.
doi: 10.11894/1005-829x.2016.36(5).066
ZHOU Caiyun, DENG Juan, ZHU Junyan, et al. Preparation of activated graphene oxide and its adsorption for methyl orange[J]. Industrial Water Treatment, 2016,36(5):66-70.
doi: 10.11894/1005-829x.2016.36(5).066
[9] 曹海燕, 毕恒昌, 谢骁, 等. 氧化石墨烯基功能纸的简易制备和染料吸附性能[J]. 物理学报, 2016,65(14):217-228.
CAO Haiyan, BI Hengchang, XIE Xiao, et al. Functional tissues based on graphene oxide: facile preparation and dye adsorption properties[J]. Acta Physica Sinica, 2016,65(14):217-228.
[10] 陶金, 张德锁, 林红, 等. 介孔氧化硅/棉复合纤维对染料的吸附性能[J]. 纺织学报, 2018,39(10):98-103.
TAO Jin, ZHANG Desuo, LIN Hong, et al. Adsorption properties of cotton fiber functionalized by mesoporous nanoparticle for dyes[J]. Journal of Textile Research, 2018,39(10):98-103.
[11] 姚莉丽. 氧化石墨烯/纤维素复合材料的制备和性能[D]. 上海:东华大学, 2014: 32-33.
YAO Lili. The preparation and properties of graphene oxide/cellulose composites[D]. Shanghai: Donghua University, 2014: 32-33.
[12] 于岩. 新型水相吸附材料[M]. 北京: 科学出版社, 2016: 341-347.
YU Yan. New water phase adsorption materials [M]. Beijing: Science Press, 2016: 341-347.
[1] LOU Yaya, WANG Jing, DONG Yanchao, WANG Chunmei. Preparation and decolorization of rayon based zeoliticimidazolate framework functional material [J]. Journal of Textile Research, 2021, 42(02): 142-147.
[2] CHENG Lüzhu, WANG Zongqian, WANG Dengfeng, SHEN Jiakun, LI Changlong. Preparation of highly hollow biomass-based activated carbon fiber and its adsorption property to methylene blue [J]. Journal of Textile Research, 2021, 42(02): 129-134.
[3] MA Yue, GUO Jing, YIN Juhui, ZHAO Miao, GONG Yumei. Preparation and characterization of cellulose/dialdehyde cellulose/Antarctic krill protein antibacterial fibers [J]. Journal of Textile Research, 2020, 41(11): 34-40.
[4] LI Liang, LIU Jingfang, HU Zedong, GENG Changjun, LIU Rangtong. Graphene oxide loading on polyester fabrics and antistatic properties [J]. Journal of Textile Research, 2020, 41(09): 102-107.
[5] PANG Yali, MENG Jiayi, LI Xin, ZHANG Qun, CHEN Yankun. Preparation of graphene fibers by wet spinning and fiber characterization [J]. Journal of Textile Research, 2020, 41(09): 1-7.
[6] ZHAO Zhiqi, LI Qiujin, SUN Yuejing, GONG Jixian, LI Zheng, ZHANG Jianfei. Application of magnetic-graphene oxide/poly(allylamine hydrochloride) microcapsules for adsorption of dyes [J]. Journal of Textile Research, 2020, 41(07): 109-116.
[7] WANG Shubo, QIN Xiangpu, SHI Lei, ZHUANG Xupin, LI Zhenhuan. Preparation and properties of proton exchange membrane made from graphene oxide quantum dots/polyacrylonitrile nanofiber composites [J]. Journal of Textile Research, 2020, 41(06): 8-13.
[8] LI Liping, WU Daoyi, ZHAN Yikai, HE Min. Review on carbon fiber surface modification using electrophoretic deposition of carbon nanotubes and graphene oxide [J]. Journal of Textile Research, 2020, 41(06): 168-173.
[9] WANG Jiankun, JIANG Xiaodong, GUO Jing, YANG Lianhe. Research progress of functionalized graphene oxide adsorption materials [J]. Journal of Textile Research, 2020, 41(04): 167-173.
[10] YUE Chengfei, DING Changkun, LI Lu, CHENG Bowen. Carbodiimide/hydroxysuccinimide crosslinking modification and properties of collagen fibers [J]. Journal of Textile Research, 2020, 41(03): 1-7.
[11] MA Junzhi, WANG Dong, FU Shaohai. Preparation and properties of flame-retardant viscose fiber/dithiopyrophosphate incorporated with graphene oxide [J]. Journal of Textile Research, 2020, 41(03): 15-19.
[12] SONG Le, SHEN Lanping, HUANG Xianwen, HENG Fangfang, MA Hongbo, OUYANG Qin, CHEN Peng, WANG Xuan. Preparation and properties of lignin/polyacrylonitrile composite fibers [J]. Journal of Textile Research, 2020, 41(02): 7-12.
[13] LUO Jiani, LI Lijun, ZHANG Xiaosi, ZOU Hantao, LIU Xueting. Modification of activated carbon fiber using graphene oxide doped titanium dioxide [J]. Journal of Textile Research, 2020, 41(01): 8-14.
[14] OUYANG Pengfei, ZHANG Yufang, JIA Chunzi, ZHANG Jiayu. Properties of regenerated fibers from bamboo pulp/ionic liquid combined system [J]. Journal of Textile Research, 2020, 41(01): 21-25.
[15] YI Ling, ZHANG He, FU Xin, LI Wen. Preparation and far-infrared emission performance of graphene based zirconium/titanium composites modified cotton fabrics [J]. Journal of Textile Research, 2020, 41(01): 102-109.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd