Journal of Textile Research ›› 2024, Vol. 45 ›› Issue (10): 23-30.doi: 10.13475/j.fzxb.20231004001

• Fiber Materials • Previous Articles     Next Articles

Effect of pyrrole-conjugated structure on the thermal cycle stability of carbon fiber reinforced resin-based composites

JIANG Mengmin1, WANG Yifan1, JIN Xin1(), WANG Wenyu2, XIAO Changfa1,3   

  1. 1. School of Materials Science and Engineering, Tiangong University, Tianjin 300387, China
    2. School of Textile Science and Engineering, Tiangong University, Tianjin 300387, China
    3. Shanghai University of Engineering Science, Shanghai 201620, China
  • Received:2023-10-13 Revised:2024-05-23 Online:2024-10-15 Published:2024-10-22
  • Contact: JIN Xin E-mail:jinxin29@126.com

RichHTML

20

PDF (PC)

54

Abstract:

Objective Carbon fiber(CF) reinforced resin matrix composites (CFRPs) have attracted much research attention in due to their good overall performance. However, CFRPs suffer from the problems of weak interfacial bonding between carbon fibers and matrix, and the mismatch of thermal expansion coefficients of the two phase materials brings about interfacial damage during thermal cycling. Existing interfacial modification techniques are difficult to solve the above two problems, and therefore a new solution is proposed in this paper.

Method Optimization of interfacial properties of composites was carried out based on structural adjustment of polypyrrole (PPy) to achieve surface modification by polymerizing a layer of PPy on carbon fiber. The PPy layer with more conjugated structure was obtained by adjusting different polymerization temperature. The interfacial bonding property, thermal expansion property and thermal cycling stability of CFRPs prepared under different polymerization conditions were studied.

Results The results showed that the surface roughness of PPy/CF-0 fibers polymerized at 0 ℃ was higher than that of CF by a factor of 2.09, which was conducive to the anchoring of the epoxy resin on the surface of carbon fibers. Moreover, the PPy on the surface of PPy/CF-0 fibers showed a higher α-α conjugate structure, which led to the negative coefficient of thermal expansion of the composites, and increased the interlayer shear strength and interfacial shear strength of the composites by a maximum of 60 MPa and 47.5 MPa, respectively. The PPy/CF-0 fiber composites also demonstrated excellent thermal cycling stability, and the shear strength was still maintained at more than 70% of the initial value after 100 thermal cycling tests.

Conclusion Compared with unmodified CF, the interlaminar shear strength(ILSS) and interfacial shear strength(IFSS) of PPy/CF-0 fiber-reinforced composites modified by PPy coating reached 88.9 MPa and 65.4 MPa, respectively, which were 1.56 and 1.70 times higher compared with CF, and the shear strength was maintained at more than 70% of the initial value after thermal cycling up to 100 times. The polymerization temperature has a significant effect on the morphology, structure and properties of the PPy layer. Through AFM observation and FT-IR spectra analysis, the surface of PPy/CF-0 fibers prepared by low-temperature polymerization at 0 ℃ has a large roughness and the content of α-α conjugated structure of PPy is as high as 74%. The PPy/CF-0 fiber and its reinforced composites showed negative coefficient of thermal expansion. The PPy-modification technology provides a new way of thinking for the design of composite materials by changing the surface roughness and negative thermal expansion coefficient, thus effectively enhancing the interfacial bonding performance and improving the thermal cycling stability of fiber-reinforced composites.

Key words: carbon fiber reinforced resin matrix composite, polypyrrole, interfacial bonding property, negative thermal expansion coefficient, thermal cycling stability, polymerization temperature

CLC Number: 

  • TS101

Fig.1

SEM images of composite fibers under different conditions"

Fig.2

AFM diagrams of composite fibers under different conditions"

Fig.3

Relationship between thermal expansion coefficient and temperature of different fibers"

Fig.4

Relationship between thermal expansion coefficient and temperature of unidirectional fiber composites"

Tab.1

Thermal expansion coefficient of unidirectional fiber composites"

材料 α90/(10-4℃-1) α150/(10-4℃-1)
CF 6.960 9.410
PPy/CF-0 -1.870 -3.760
PPy/CF-30 -0.118 -1.210
PPy/CF-60 11.900 3.750

Fig.5

DMA diagram of damping factor changing with deposition temperature"

Fig.6

UV visible absorption spectra"

Fig.7

Infrared spectra of PPy under different processing conditions"

Tab.2

α-α content under different processing conditions"

聚合温度/℃ α-α含量/% 聚合温度/℃ α-α含量/%
-15 68 30 69
0 74 45 63
15 69 60 52

Fig.8

Thermal cycling properties of composites. (a) Interlaminar shear strength; (b)Interfacial shear strength"

[1] 杨智勇, 张东, 顾春辉, 等. 国外空天往返飞行器用先进树脂基复合材料研究与应用进展[J]. 复合材料学报, 2022, 39(7): 3029-3043.
YANG Zhiyong, ZHANG Dong, GU Chunhui, et al. Research and application of advanced resin matrix composites for aerospace shuttle vehicles abroad[J]. Acta Materiae Compositae Sinica, 2022, 39(7): 3029-3043.
[2] CHEN Q, PENG Q, ZHAO X, et al. Grafting carbon nanotubes densely on carbon fibers by poly(propylene imine) for interfacial enhancement of carbon fiber composites[J]. Carbon, 2019, 158: 704-710.
[3] FANG H, BAI Y, LIU W Q, et al. Connections and structural applications of fibre reinforced polymer composites for civil infrastructure in aggressive environments[J]. Composites Part B: Engineering, 2019, 164: 129-143.
[4] 林乐乐. 炭纤维表面特性对复合材料表面性能的影响研究[J]. 炭素技术, 2020, 39(4): 57-61.
LIN Lele. Effect of carbon fiber surface properties on the surface properties of composites[J]. Carbon Techniques, 2020, 39(4): 57-61.
[5] MUND M, LIPPKY K, BLASS D, et al. Influence of production based surface topography and release agent amount on bonding properties of CFRP[J]. Composite Structures, 2019, 216(2): 104-111.
[6] SHARMA M, GAO S, MAEDER E, et al. Carbon fiber surfaces and composite interphases[J]. Compos Sci Technol, 2014, 102: 35-50.
[7] XIAO J, ZHANG X, ZHAO Z, et al. Rapid and continuous atmospheric plasma surface modification of PAN-based carbon fibers[J]. ACS Omega, 2022, 7(13): 10963-10969.
doi: 10.1021/acsomega.1c06818 pmid: 35415352
[8] ZHANG Z, WILSON J L, KITT B R, et al. Effects of oxygen plasma treatments on surface functional groups and shear strength of carbon fiber composites[J]. ACS Applied Polymer Materials, 2021, 3(2): 986-995.
[9] 张静静, 梁森, 汤超. 微波对碳纤维的改性作用及其对电子束固化CFRP界面性能的影响[J]. 复合材料学报, 2023, 40(7): 3900-3911.
ZHANG Jingjing, LIANG Sen, TANG Chao. Modification of carbon fiber by microwave and its effect on interfacial properties of electron beam cured CFRP[J]. Acta Materiae Compositae Sinica, 2023, 40(7): 3900-3911.
[10] KRISHNAMURTHY A, TAO R, SENSE E, et al. Multiscale polymer dynamics in hierarchical carbon nanotube grafted glass fiber reinforced composites[J]. ACS Appl Polym Mater, 2019(1): 1905-1917.
[11] 冯俊. 碳纤维的改性及其界面性能[J]. 合成树脂及塑料, 2019, 36(6): 27-30.
FENG Jun. Modification and interface properties of CF[J]. China Synthetic Resin and Plastics, 2019, 36(6): 27-30.
[12] KWON Y J, KIM Y, JEON H, et al. Graphene/carbon nanotube hybrid as a multi-functional interfacial reinforcement for carbon fiber-reinforced composites[J]. Composites Part B, 2017, 122: 23-30.
[13] CAI J Y, LI Q, EASTON C D, et al. Surface modification of carbon fibres with ammonium cerium nitrate for interfacial shear strength enhancement[J]. Composites Part B: Engineering, 2022, 246: 1-8.
[14] YUAN J M, FENG Y R, WU Z J, et al. A carbon fiber network/polypropylene composite with a low thermal expansion coefficient and high stiffnessn[J]. New Carbon Materials, 2017, 32(3): 271-276.
[15] HAN Y C, CHEN P S, XIA Y F, et al. Electrodeposition of polypyrrole on He plasma etched carbon nanotube films for electrodes of flexible all-solid-state supercapacitor[J]. Solid State Electr, 2019, 23: 553-562.
[16] AKSHAYA K B, VARGHESE A, NIDHIN M, et al. Amorphous Ru-Pi nanoclusters coated on polypyrrole modified carbon fiber paper for non-enzymatic electrochemical determination of cholesterol[J]. Electrochem Soc, 2019, 166: 1016-B1027.
[17] CHEN H Y, CAI X F, BI X S. The influence of polypyrrole coating on the mechanical properties of carbon fiber-filled polytetrafluoroethylene composite[J]. Journal of Thermoplastic Composite Materials, 2012, 27(8): 1065-1073.
[18] 洪诗婷. T300碳纤维的表面处理及力学性能研究[D]. 上海: 东华大学, 2020: 11-16.
HONG Shiting. Surface treatment and mechanical properties of T300 carbon fiber[D]. Shanghai: Donghua University, 2020: 11-16.
[19] YAO L, RUAN X Y, HONG S T, et al. Effective treatments for enhancing carbon fiber/epoxy interfacial properties and carbon yarn weavability[J]. Textile Research Journal, 2021, 91(21/22): 2476-2486.
[20] JIN X, WANG W Y, XIAO C F, et al. Improvement of coating durability, interfacial adhesion and compressive strength of UHMWPE fiber/epoxy composites through plasma pre-treatment and polypyrrole coating[J]. Composites Science and Technology, 2016, 128: 169-175.
[21] 王闻宇, 刘亚敏, 金欣, 等. 聚吡咯修饰碳纤维/环氧树脂复合材料的界面剪切强度[J]. 材料研究学报, 2018, 32(3): 210-215.
WANG Wenyu, LIU Yamin, JIN Xin, et al. Effect of polypyrrole modified carbon fiber on interfacial property of composite PPy-carbon fiber/epoxy[J]. Chinese Journal of Materials Research, 2018, 32(3): 210-215.
[22] LIN J S. Effect of polypyrrole deposition of carbon fiber on the thermal expansion of carbon fiber-epoxy composites[J]. Journal of Polymer Research, 1999, 6(4): 237-242.
[23] LI Q, LIN K, LIU Z, et al. Chemical diversity for tailoring negative thermal expansion[J]. Chemical Reviews, 2022, 122(9): 8438-8486.
doi: 10.1021/acs.chemrev.1c00756 pmid: 35258938
[24] AZUMA M, OKA K, NABETANI K. Negative thermal expansion induced by intermetallic charge transfer[J]. Science and Technology of Advanced Materials, 2015, 16(3): 1-7.
[25] 周晓东, 林群芳, 戴干策. 玻璃纤维毡增强聚丙烯复合材料的冷热循环疲劳特性[J]. 复合材料学报, 2000, 17(3): 13-16.
ZHOU Xiaodong, LIN Qunfang, DAI Gance. Thermal-cold fatigue of glassm at rein forced polypropylene[J]. Acta Materiae Compositae Sinica, 2000, 17 (3): 13-16.
[1] CHEN Ying, SHEN Nadi, ZHANG Lu. Structure design and performance of fiber capacitive sensor [J]. Journal of Textile Research, 2024, 45(05): 43-50.
[2] WANG Bo, LIU Meiya, CHEN Mingna, SONG Zican, XIA Ming, LI Mufang, WANG Dong. Strain-sensing performance of polypyrrole/polyurethane filaments and application [J]. Journal of Textile Research, 2024, 45(02): 119-125.
[3] AI Jingwen, LU Dongxing, LIAO Shiqin, WANG Qingqing. Preparation and strain sensing properties of yarn sensor prepared by in-situ freezing interfacial polymerization [J]. Journal of Textile Research, 2024, 45(01): 74-82.
[4] WAN Ailan, SHEN Xinyan, WANG Xiaoxiao, ZHAO Shuqiang. Preparation and sensing response characterization of polydopamine modified reduced graphene oxide/polypyrrole conductive fabrics [J]. Journal of Textile Research, 2023, 44(01): 156-163.
[5] YU Yangxiao, LI Feng, WANG Yuyu, WANG Shanlong, WANG Jiannan, XU Jianmei. Preparation and properties of polypyrole/silk fibroin conductive nanofiber membranes [J]. Journal of Textile Research, 2022, 43(10): 16-23.
[6] ZHOU Xiaoya, MA Dinghai, HU Chengye, HONG Jianhan, LIU Yongkun, HAN Xiao, YAN Tao. Continuous preparation and application of polyester/polyamide 6 nanofiber coated yarns [J]. Journal of Textile Research, 2022, 43(02): 110-115.
[7] LI Bo, FAN Wei, GAO Xingzhong, WANG Shujuan, LI Zhihu. Carbon fiber reinforced epoxy based vitrimer composite material closed-loop recycling [J]. Journal of Textile Research, 2022, 43(01): 15-20.
[8] ZOU Lihua, YANG Li, LAN Chuntao, RUAN Fangtao, XU Zhenzhen. Electromagnetic shielding properties of graphene oxide/polypyrrole coated cotton fabric with layer-by-layer assembling method [J]. Journal of Textile Research, 2021, 42(12): 111-118.
[9] CHEN Ying, FANG Haoxia. Preparation and properties of hydrophobic conductive polypyrrole coating fabrics [J]. Journal of Textile Research, 2021, 42(10): 115-119.
[10] WANG Xiaofei, WAN Ailan, SHEN Xinyan. Preparation and strain sensing of dopamine-modified polypyrrole conductive fabric [J]. Journal of Textile Research, 2021, 42(06): 114-119.
[11] LIU Xiaoqian, CHEN Yu, ZHOU Huimin, YAN Yuan, XIA Xin. Preparation of polyacrylonitrile conductive nanofiber yarn grafted with acrylic acid using plasma technology [J]. Journal of Textile Research, 2021, 42(05): 109-114.
[12] YU Jia, XIN Binjie, ZHUO Tingting, ZHOU Xi. Preparation and characterization of Cu/polypyrrole-coated wool fabrics for high electrical conductivity [J]. Journal of Textile Research, 2021, 42(01): 112-117.
[13] WANG Bo, FAN Lihua, YUAN Yun, YIN Yunjie, WANG Chaoxia. Preparation and electric storage performance of stretchable polypyrrole/cotton knitted fabric [J]. Journal of Textile Research, 2020, 41(10): 101-106.
[14] WANG Xiaofei, WAN Ailan. Preparation of polypyrrole/silver conductive polyester fabric by ultraviolet exposure [J]. Journal of Textile Research, 2020, 41(04): 112-116.
[15] LIN Jiameng, WAN Ailan, MIAO Xuhong. Preparation and properties of polypyrrole/silver conductive polyester fabrics [J]. Journal of Textile Research, 2020, 41(03): 113-117.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd