JOURNAL OF TEXTILE RESEARCH ›› 2018, Vol. 39 ›› Issue (07): 8-14.doi: 10.13475/j.fzxb.20170804207

Previous Articles     Next Articles

Preparation and properties of orientation reinforced composite separator for lithium-ion battery

  

  • Received:2017-08-28 Revised:2018-04-20 Online:2018-07-15 Published:2018-07-16

Abstract:

In order to fabricate the electrospinning Lithium-ion battery separator which possessed excellent mechanical properties in lengthways direction, polyacrylonitrile (PAN) membrane were fabricated at different rotational speeds, concluding that the PAN membrane showed best orientation effect at 700 r/min. Then middle-orientation reinforced PAN membrane which was collected at 700 r/min and two layers of disordered polyester (PET) membrane were combined to pripare orientation reinforced compositeseparators.  Meanwhile, isotropous PET/PAN/PET membrane was fabricated at 100 r/min as contrast membrane. The mechanical and electrochemical properties were evaluated. The results show that the electrolyte uptake is 371%, and the thermal shrinkage is 4.1%. The ionic conductivity at room tempertature reaches 0.553 mS/cm and electrochemical stability was 5.27 V. The initial discharge capacity of battery is 138.2 mA?h/g. The breaking strength of the orientation reinforced composite separators is 9.2 MPa in lengthways direction, which is 130% higher than contrast membrane. The mechanical strength of the orientation reinforced composite separator increases observably, and its overall properties are superior to isotropous PET/PAN/PET membranes.

Key words: Iithium-ion baery separator, electrospinning, oriented nanofibrous membrane,  electrochemical property

[1] . Preparation technology and application progress of solution blown nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(07): 165-173.
[2] . Preparation and properties of electrospun polyacrylonitrile nanofiber coated window screen [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(04): 14-18.
[3] . Overview on mass production of electrospun nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(03): 175-180.
[4] . Oil absorption property of electrospun superfine fibrous membrane [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(02): 7-13.
[5] . Electrospun barium titanate/ poly(vinylidene fluoride) nano-composite flexibility piezoelectric fibrous membranes [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(02): 14-19.
[6] . Preparation of crosslinking and high performance polymers [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(01): 6-10.
[7] . Effects of coaxial electrospinning parameters on morphology and carbonization yield of polyacrylonitrile hollow carbon nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(12): 1-6.
[8] . Research Progress in preparation and application of electrospinning porous carbon nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(11): 168-176.
[9] . Preparation of ultrafine polyacrylonitrile nanofibers via composite electrospinning [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(11): 16-21.
[10] . Synthesis of fluorinated polyurethane and acid-proofness and water permeability of electrospun nanofiber membrane composite fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(10): 7-12.
[11] . In fluence of hydrogen bonding on electrospinning of starch nanofiber in dimethyl sulfoxide/H2O solution [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(09): 19-23.
[12] . Preparation and gas-liquid filtration performance of composite filters of electrospun polyacrylonitrile nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(09): 8-13.
[13] . Crystallization behavior and mechanical properties of electrospun polyester/palm fiber-based activated carbon composite  [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(08): 6-10.
[14] . Preparation and properties of gradient filter materials with different packing density [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(07): 23-27.
[15] . Structure and properties of polylactic acid-polycaprolactone/silk fibroin composite nanofibrous scaffolds [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(05): 8-13.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!