Journal of Textile Research ›› 2020, Vol. 41 ›› Issue (05): 8-14.doi: 10.13475/j.fzxb.20181105807

• Fiber Materials • Previous Articles     Next Articles

Preparation of polyacrylonitrile/cellulose acetate/TiO2 composite nanofiber membrane and its photocatalytic degradation performance

QIAN Yifan1,2, ZHOU Tang3, ZHANG Liying2,4, LIU Wanshuang2,4, FENG Quan3()   

  1. 1. College of Textiles, Donghua University, Shanghai 201620, China
    2. Center for Civil Aviation Composites, Donghua University, Shanghai 201620, China
    3. Anhui Provincial Key Laboratory of Textile Fabric, Anhui Polytechnic University, Wuhu, Anhui 241000, China
    4. Shanghai Collaborative Innovation Center for High Performance Fiber Composites, Donghua University, Shanghai 201620, China
  • Received:2018-11-21 Revised:2020-01-06 Online:2020-05-15 Published:2020-06-02
  • Contact: FENG Quan E-mail:wdyu@dhu.edu.cn

RichHTML

6

PDF (PC)

176

Abstract:

In order to investigate the photocatalytic degradation of composite nanofiber membrane before and after alkali modification, the polyacrylonitrile/cellulose acetate/nano-titanium dioxide (PAN/CA/TiO2) composite nanofibers membrane were first prepared using the electrospinning technology, which was then alkaline treated with 0.05 and 0.10 mol/L NaOH solution respectively to achieve polyacrylonitrile/regenerated cellulose (PAN/RC/TiO2) composite nanofiber membranes. Scanning electron microscopy observation, Fourier transform infrared spectroscopy analysis and static contact angle measurement were used to characterize the mechanical and photocatalytic degradation of the composite nanofiber membrane. The results show that after the alkali treatment, the static contact angle of the composite nanofiber membrane are reduced from 125.3°to 10.2°, the hydrophilic property is greatly improved. The degradation rate of PAN/RC/TiO2 composite nanofiber membrane to MB solution reaches 91.2%, while the degradation rate of blank solution to MB solution is only 10.1%. After 3 repeated uses, the degradation rate caused by the MB solution still reaches 74.7%.

Key words: dye wastewater treatment, electrospining, titanium oxide, nanofibers, photocatalysis

CLC Number: 

  • TQ619.2

Fig.1

Self-made electrospinning device schematic"

Fig.2

SEM images of nanofibers"

Tab.1

Mechanical properties of composite nanofibers before and after modification"

样品 断裂强度/MPa 伸长率/%
PAN/CA 125.61 22.39
PAN/RC 95.70 21.20
PAN/CA/1%TiO2 124.54 20.30
PAN/RC/1%TiO2 87.62 19.80

Fig.3

FT-IR spectra of composite nanofibers"

Tab.2

Static contact angle of composite nanofibers before and after modification"

样品 接触角/(°)
PAN/CA 125.30
PAN/RC 10.20
PAN/CA/1%TiO2 119.10
PAN/RC/1%TiO2 8.72

Fig.4

Curves of photocatalytic degradation of MB by composite nanofibers. (a) Before modification; (b) After modification"

[1] 贾艳萍, 姜成, 郭泽辉, 等. 印染废水深度处理及回用研究进展[J]. 纺织学报, 2017,38(8):172-180.
JIA Yanping, JIANG Cheng, GUO Zehui, et al. Research progress on deep treatment and recycling of dye wastewater[J]. Journal of Textile Research, 2017,38(8):172-180.
[2] 单苗苗, 高献超. 印染废水全过程处理及回用[J]. 针织工业, 2019(7):38-40.
SHAN Miaomiao, GAO Xianchao. Treatment and reuse of printing and dyeing wastewater[J]. Knitting Industries, 2019 (7):38-40.
[3] 方梦祥, 姚鹏, 岑建孟, 等. 活性炭吸附处理含酚废水的研究进展[J]. 化工进展, 2018,37(2):744-751.
FANG Mengxiang, YAO Peng, CEN Jianmeng, et al. Adsorption treatment of phenolic wastewater by activated carbon: a review[J]. Chemical Industry and Engineering Progress, 2018,37(2):744-751.
[4] 陈一萍, 潘吉特. 碳纳米管/铁氧化物复合材料对模拟染料废水的吸附脱色效果[J]. 纺织学报, 2016,37(10):89-93.
CHEN Yiping, PAN Jite. Preparation of carbon nanotubes /iron oxide composite adsorbents for treatment of dye-containing wastewater[J]. Journal of Textile Research, 2016,37(10):89-93.
[5] 马建伟, 任淑鹏, 初阳, 等. 碳纳米管/化学沉淀法处理重金属废水的研究进展[J]. 化工工程师, 2018,32(8):41,57-59.
MA Jianwei, REN Shupeng, CHU Yang, et al. Chemical precipitation method for treating heavy metal wastewater[J]. Chemical Engineer, 2018,32(8):41,57-59.
[6] 张振闯, 韩秀丽, 方书起, 等. 膜分离法处理乙醇发酵废水研究[J]. 水处理技术, 2018,44(8):57-60.
ZHANG Zhenchuang, HAN Xiuli, FANG Shuqi, et al. Study on ethanol fermentation wastewater treatment by membrane separation method[J]. Technology of Water Treatment, 2018,44(8):57-60.
[7] 腾乐天, 赵康, 汤玉斐. 静电纺丝制备TiO2纳米纤维的光催化性能[J]. 硅酸盐学报, 2012,40(8):1215-1219.
TENG Letian, ZHAO Kang, TANG Yufei. Photocatalytic acticity of TiO2 nanofibres prepared via electrospinnin technology[J]. Journal of The Chinese Ceramic Society, 2012,40(8):1215-1219.
[8] 缪月娥, 刘天西. 基于静电纺丝技术的多级结构聚合物纳米纤维复合材料的研究进展[J]. 高分子学报, 2012(8):801-811.
MIAO Yue'e, LIU Tianxi. Recent progress in hierarchically organized polymer nanocomposites based on electrospun nanofibers[J]. Acta Polymerica Sinica, 2012(8):801-811.
[9] 王国平, 王存涵, 胡滨, 等. 离子交换法碳酸钾含氨氮生产废水的处理工艺改进[J]. 工业水处理, 2017,37(8):116-120.
WANG Guoping, WANG Cunhan, HU Bin, et al. Improvement in the treatment process of ammonia nitrogen-containing industrial wastewater in potassium carbonate production by ion-exchange method[J]. Industrial Water Treatment, 2017,37(8):116-120.
[10] 高春涛, 蔡以兵, 王清清, 等. TiO2纳米纤维的制备及对染料的光催化降解性能[J]. 功能材料, 2013,44(2):240-243,248.
GAO Chuntao, CAI Yibing, WANG Qingqing, et al. Preparation and photocatalytic degradation properties on dyes of TiO2 nanofibers[J]. Journal of Functional Materials, 2013,44(2):240-243,248.
[11] 周明, 费燕娜, 杨瑞华, 等. PAN/CA复合纳米纤维膜的制备及性能表征[J]. 化工新型材料, 2011,39(3):76-78.
ZHOU Ming, FEI Yanna, YANG Ruihua, et al. Preparation and characterization of PAN/CA composite nanofiber membranes[J]. New Chemical Materials, 2011,39(3):76-78.
[12] 武丁胜, 凤权. 静电纺再生纤维素复合纳米纤维的制备及其性能研究[J]. 安徽工程大学学报, 2015,30(1):61-65.
WU Dingsheng, FENG Quan. Study on the preparation and properties of electron-spun regenerated cellulose composite nanofiber[J]. Journal of Anhui Polytechnic University, 2015,30(1):61-65.
[13] 许晶晶, 朱平武, 赵丽, 等. Ag/TiO2中空纳米纤维光催化材料的制备及表征[J]. 化学学报, 2011,69:585-590.
XU Jingjing, ZHU Pingwu, ZHAO Li, et al. Preparation and characterization of Ag/TiO2 hollow nano-fiber photocatalytic material[J]. Acta Chimica Sinica, 2011,69(5):585-590.
[14] POLICE A E R, BASAVARAJU S, VALLURI D K, et al. Bismuth modified porous silica preparation characterization and photocatalytic activity evaluation for degradation of isoproturon[J]. Journal of Materials Science & Technology, 2013,29(7):639-646.
[15] 夏鑫, 凤权, 魏取福, 等. PVAc/SnO2杂化纳米纤维的光催化及力学性能[J]. 纺织学报, 2011,32(8):12-16.
XIA Xin, FENG Quan, WEI Qufu, et al. Photocatalytic and mechanical properties of PVAc/SnO2 hybrid nanofiber[J]. Journal of Textile Research, 2011,32(8):12-16.
[16] 凤权, 武丁胜, 桓珊, 等. 再生纤维素纳米纤维膜的制备及其蛋白质分离性能[J]. 纺织学报, 2016,37(12):12-17.
FENG Quan, WU Dingsheng, HUAN Shan, et al. Preparation and protein separation properties of regenerated cellulose nanofiber membrane[J]. Journal of Textile Research, 2016,37(12):12-17.
[17] 陶亚茹, 谢汝义, 张琳萍, 等. 可见光催化剂BiOI的制备及其对活性蓝KN-R的降解机理[J]. 东华大学学报(自然科学版), 2015,41(6):774-780.
TAO Yaru, XIE Ruyi, ZHANG Linping, et al. Synjournal of visible-light induced photocatalyst BiOI and its degradation mechanism of C.I.Reactive Blue KN-R[J]. Journal of Donghua University(Natural Science Edition), 2015,41(6):774-780.
[18] MA Y, WANG J, XU S, et al. Ag2O/sodium alginate-reduced graphene oxide aerogel beads for efficient visible light driven photocatalysis[J]. Applied Surface Science, 2018,430:155-164.
doi: 10.1016/j.apsusc.2017.03.299
[19] 凤权, 钱怡帆, 桓珊, 等. PMMA/OMMT/TiO2复合纳米纤维膜的制备及其光催化性能[J]. 东华大学学报(自然科学版), 2018,44(1):28-32.
FENG Quan, QIAN Yifan, HENG Shan, et al. Preparation and photocatalytic properties of the PMMA/OMMT/TiO2 composite nanofibrous membrane[J]. Journal of Donghua University(Natural Science Edition), 2018,44(1):28-32.
[20] 廉帅唯, 王旭东, 郭利妍, 等. 钙钛矿型光催化剂LaAlO3制备及光催化性能研究[J]. 水处理技术, 2020(1):48-52,56.
LIAN Shuaiwei, WANG Xudong, GUO Liyan, et al. Preparation and photocatalytic performance of perovskite-type photocatalyst LaAlO3[J]. Technology of Water Treatment, 2020 (1):48-52, 56.
[21] WANG H, ZHANG L, HU C, et al. Enhanced degradation of organic pollutants over Cu-doped LaAlO3 perovskite through heterogeneous Fenton-like reactions[J]. Chemical Engineering Journal, 2017,332:572-581.
[22] 孟姝虔, 周德凤, 朱晓飞, 等. TiO2/WO3微纳米纤维复合材料的制备及光催化性能[J]. 无机材料学报, 2014,29(6):605-613.
MENG Shuqian, ZHOU Defeng, ZHU Xiaofei, et al. Fabrication of TiO2/WO3 micro-nanofibers composites and their photocatalytic activity[J]. Journal of Inorganic Materials, 2014,29(6):605-613.
[23] ZHANG Ping, WANG Qingqing, ZHANG Jinning, et al. Preparation of amidoxime-modified polyacrylonitrile nanofibers immobilized with laccase for dye degradation[J]. Fibers and Polymers, 2014,15(1):30-34.
[1] SONG Yingqi, PAN Jiahao, WU Liguang, WANG Ting, DONG Chunying. Fabrication of photocatalytic floating spheres for degradation of methyl-orange under illumination of visible light [J]. Journal of Textile Research, 2020, 41(12): 102-110.
[2] ZHANG Mengyuan, HUANG Qinglin, HUANG Yan, XIAO Changfa. Electrospun poly(tetrafluoroethylene)/TiO2 photocatalytic nanofiber membrane and its application [J]. Journal of Textile Research, 2019, 40(09): 1-7.
[3] ZHANG Yian, DI Jianfeng. Preparation of photocatalyst loaded activated carbon grafted with polyhydrazide for removing formaldehyde [J]. Journal of Textile Research, 2019, 40(03): 109-117.
[4] . Preparation and photocatalytic degradation decoloring of TiO2 / reduced graphene oxide composites [J]. Journal of Textile Research, 2018, 39(12): 78-83.
[5] . Preparation and performance of self-cleaning fabrics based on Ag/TiO2 photocatalysis [J]. Journal of Textile Research, 2018, 39(12): 89-94.
[6] . Preparation and photocatalytic properties of BiVO4 loaded fiber [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(06): 89-95.
[7] . Preparation of weak-light-driven TiO2 composite photocatalysts by adsorption phase synthesis [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(05): 67-73.
[8] . Preparation and photocatalytic property of TiO2 NTs nanotubes [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(04): 22-26.
[9] . Influence of spinning process and pre-oxidation conditions on PAN-based carbon nanofibers fabricated by centrifugal spinning [J]. Journal of Textile Research, 2016, 37(2): 7-12.
[10] . Preparation of graphene/polyvinylidenefluoride composite nanofibers by electrospinning [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(10): 158-0161.
[11] . Preparation and electrical resistivity research of CNFs/ZnO composite nanofiber membrane [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(6): 25-0.
[12] . Morphology and photocatalytic properties of titanium sol prepared by sol-gel method [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(5): 7-0.
[13] . The structures and properties of electrospun silk fibroin/CaSiO3 composite nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2011, 32(6): 1-6.
[14] WU Ning;;WEI Qufu;CHEN Li;XIA Xin. Preparation, characterization and photocatalytic properties of Fe3+ doped TiO2 nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2011, 32(3): 5-9.
[15] Liu Yang;xu anchang;CHENG Qian;PAN Zhijuan. Effect of electrospinning process on structure and property of electrospun PA6/MWNTs yarn [J]. JOURNAL OF TEXTILE RESEARCH, 2010, 31(3): 1-6.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd