Catalytic degradation of dye by metal phthalocyanine/multi-walled carbon nanotubes under simulated solar light

XIA Yun, LÜ Wangyang, CHEN Wenxing()   

  1. National Engineering Laboratory for Textile Fiber Materials & Processing Technology, Zhejiang Sci-Tech University, Hangzhou, Zhejiang 310018, China
  • Received:2020-03-19 Revised:2020-06-24 Online:2020-12-15 Published:2020-12-23
  • Contact: CHEN Wenxing E-mail:wxchen@zstu.edu.cn

RichHTML

5

PDF (PC)

203

Abstract:

In order to expand the pH value of the Fenton system to degrade dye efficiently, the catalyst FePcCl16/multi-walled carbon nanotubes (FePcCl16/MWCNTs), synthesized by means of FePcCl16 loaded on MWCNTs via reflux with H2O2 as oxidant, was employed to degrade Acid Orange 7 dye (AO7) under simulated solar light irradiation. The catalytic performance, influencing factors and catalytic mechanism of the catalytic system were characterized by scanning electron microscope, transmission electron microscope, Fourier transform infrared spectrometer, thermogravimetric analyzer and X-ray diffractomer. The results show that the degradation rate of AO7 is 100% under acidic, inorganic salts and urea conditions in catalytic system, 97% under the neutral condition, and 75% under the alkaline condition. The degradation rate of AO7 is still above 95% after 5 cycles of the catalytic system. The results of catalytic mechanism show that the main active species of AO7 degradation in the catalytic system are hydroxyl radicals and superoxide radicals. Solar light irradiation promotes the production of active species to improve the catalytic performance of the system.

Key words: simulated solar light, metal phthalocyanine, multi-walled carbon nanotube, catalytic degradation, Acid Orange 7 dye, Fenton-like system, wastewater treatment

CLC Number: 

  • O643.32

Fig.1

Microstructure of FePcCl16/MWCNTs. (a) SEM image(×20 000); (b) TEM image (×600 000)"

Fig.2

FT-IR spectra of MWCNTs, FePcCl16 and FePcCl16/MWCNTs"

Fig.3

Thermal stability of MWCNTs, FePcCl16 and FePcCl16/MWCNTs"

Fig.4

XRD patterns of MWCNTs, FePcCl16 and FePcCl16/MWCNTs"

Fig.5

Catalytic activity of different catalytic system on dye A07"

Fig.6

Absorbance of AO7 in FePcCl16/MWCNTs/H2O2 system"

Fig.7

Effect of solar light irradiation on FePcCl16/MWCNTs/H2O2 catalytic activity"

Fig.8

Effect of hydrogen peroxide concentration on FePcCl16/MWCNTs/H2O2 catalytic activity"

Fig.9

Effect of pH values on FePcCl16/MWCNTs/H2O2 catalytic activity"

Fig.10

Effect of inorganic salts and urea on FePcCl16/MWCNTs/H2O2 catalytic activity"

Fig.11

Cyclic performance of FePcCl16/MWCNTs/H2O2"

Fig.12

Effect of IPA and p-BQ on FePcCl16/MWCNTs/H2O2 catalytic activity"

Fig.13

DMPO spin-trapping EPR signal of radicals. (a) Hydroxyl radical; (b) Superoxide radical"

Fig.14

Route of producing active species"

[1] SANCHEZ-SANCHEZ A, IZQUIERDO M T, MATHIEU S, et al. Structure and electrochemical properties of carbon nanostructures derived from nickel(II) and iron(II) phthalocyanines[J]. J Adv Res, 2020,22:85-97.
doi: 10.1016/j.jare.2019.11.004 pmid: 31956445
[2] HUANG W J, AHLFIELD J M, KOHL P A, et al. Heat treated tethered iron phthalocyanine carbon nanotube-based catalysts for oxygen reduction reaction in hybrid fuel cells[J]. Electrochimica Acta, 2017,257:224-232.
doi: 10.1016/j.electacta.2017.10.048
[3] 崔桂新, 董永春, 王鹏. 羊毛/铁配合物非均相芬顿反应光催化剂的制备及其应用性能[J]. 纺织学报, 2019,40(12):68-73.
CUI Guixin, DONG Yongchun, WANG Peng. Preparation and application properties of wool-Fe complex-based heterogeneous Fenton photocatalysts[J]. Journal of Textile Research, 2019,40(12):68-73.
doi: 10.1177/004051757004000110
[4] 庄帅, 阳海, 安继斌, 等. 硫酸根自由基对酸性红37的降解动力学与机制[J]. 纺织学报, 2019,40(11):131-139.
ZHUANG Shuai, YANG Hai, AN Jibin, et al. Degradation kinetics and mechanism of Acid Red 37 under attack of sulfate radicals[J]. Journal of Textile Research, 2019,40(11):131-139.
[5] GHANBARI F, MORADI M. Application of peroxymonosulfate and its activation methods for degradation of environmental organic pollutants: review[J]. Chem Eng J, 2017,310:41-62.
doi: 10.1016/j.cej.2016.10.064
[6] INAGAKI M, KONNO H, TANAIKE O. Carbon materials for electrochemical capacitors[J]. J Power Sources, 2010,195(24):7880-7903.
doi: 10.1016/j.jpowsour.2010.06.036
[7] ATALAY S, ERS Z G. Advanced oxidation pro-cesses [M]//Novel Catalysts in Advanced Oxidation of Organic Pollutants. Cham: Springer International Publishing, 2016: 23-34.
[8] PRIYANKA K P, SANKARARAMAN S, BALAKRISHNA K M, et al. Enhanced visible light photocatalysis using TiO2/phthalocyanine nanocomposites for the degradation of selected industrial dyes[J]. J Alloys Compd, 2017,720:541-549.
doi: 10.1016/j.jallcom.2017.05.308
[9] MPHUTHI N G, ADEKUNLE A S, FAYEMI O E, et al. Phthalocyanine doped metal oxide nanoparticles on multiwalled carbon nanotubes platform for the detection of dopamine[J]. Sci Rep, 2017,7:43181.
pmid: 28256521
[10] ZHU Zhexin, LU Wangyang, LI Nan, et al. Pyridyl-containing polymer blends stabilized iron phthalocyanine to degrade sulfonamides by enzyme-like process[J]. Chem Eng J, 2017,321:58-66.
doi: 10.1016/j.cej.2017.03.039
[11] LIU Hongya, BAO Shuxiang, CAI Zutong, et al. A novel method for ultra-deep desulfurization of liquid fuels at room temperature[J]. Chem Eng J, 2017,317:1092-1098.
doi: 10.1016/j.cej.2017.01.086
[12] FAN X, CHANG D W, CHEN X, et al. Functionalized graphene nanoplatelets from ball milling for energy applications[J]. Current Opinion in Chemical Engineering, 2016,11:52-58.
doi: 10.1016/j.coche.2016.01.003
[13] MARINHO B, GHISLANDI M, TKALYA E, et al. Electrical conductivity of compacts of graphene, multi-wall carbon nanotubes, carbon black, and graphite powder[J]. Powder Technol, 2012,221:351-358.
doi: 10.1016/j.powtec.2012.01.024
[14] LU Wangyang, LI Nan, CHEN Wenxing, et al. The role of multiwalled carbon nanotubes in enhancing the catalytic activity of cobalt tetraaminophthalocyanine for oxidation of conjugated dyes[J]. Carbon, 2009,47(14):3337-3345.
doi: 10.1016/j.carbon.2009.07.055
[15] HU Jirun, LIU Hongya, WANG Lulin, et al. Electronic properties of carbon nanotubes linked covalently with iron phthalocyanine to determine the formation of high-valent iron intermediates or hydroxyl radicals[J]. Carbon, 2016,100:408-416.
doi: 10.1016/j.carbon.2016.01.010
[16] WU F, HUANG H, XU T, et al. Visible-light-assisted peroxymonosulfate activation and mechanism for the degradation of pharmaceuticals over pyridyl-functionalized graphitic carbon nitride coordinated with iron phthalocyanine[J]. Appl Catal B: Environ, 2017,218:230-239.
doi: 10.1016/j.apcatb.2017.06.057
[1] SONG Yingqi, PAN Jiahao, WU Liguang, WANG Ting, DONG Chunying. Fabrication of photocatalytic floating spheres for degradation of methyl-orange under illumination of visible light [J]. Journal of Textile Research, 2020, 41(12): 102-110.
[2] YU Yucong, SHI Xiaolong, LIU Lin, YAO Juming. Recent progress in super wettable textiles for oil-water separation [J]. Journal of Textile Research, 2020, 41(11): 189-196.
[3] LI Qing, GUAN Binbin, WANG Ya, LIU Tianhui, ZHANG Luohong, FAN Zenglu. Photosensitizers sensitized Cu-organic framework for highly efficient photocatalytic degradation of Reactive Dark Blue K-R [J]. Journal of Textile Research, 2020, 41(10): 87-93.
[4] QIAN Yifan, ZHOU Tang, ZHANG Liying, LIU Wanshuang, FENG Quan. Preparation of polyacrylonitrile / cellulose acetate / TiO2 composite nanofiber membrane and its photocatalytic degradation performance [J]. Journal of Textile Research, 2020, 41(05): 8-14.
[5] ZHANG Jiao, GAO Xuefeng, WANG Yuzhou, LIU Haihui, ZHANG Xingxiang. Preparation and properties of polyamide 66/amino-functionalized multi-walled carbon nanotubes fibers [J]. Journal of Textile Research, 2019, 40(11): 1-8.
[6] HAN Ye, ZHANG Hui, ZHU Guoqing, WU Hailiang. Effect of polyethylene glycol on photocatalytic properties of polyethylene terephthalate fibers treated with titanium sulfate under hydrothermal conditions [J]. Journal of Textile Research, 2019, 40(10): 33-41.
[7] SHI Xiaoping, LI Yao, PAN Jiahao, WANG Ting, WU Liguang. Preparation of visible-light-response TiO2 photocatalyst by hydrothermal reduction [J]. Journal of Textile Research, 2019, 40(10): 105-112.
[8] WANG Wencong, FAN Jingjing, DING Chao, WANG Hongbo. Preparation and properties of multifunctional composite conductive wool fabric [J]. Journal of Textile Research, 2019, 40(08): 117-123.
[9] ZHANG Lanhe, ZHANG Mingshuang, GAO Weiwei, LI Zheng, JIA Yanping, GAO Min, LING Liangxiong. Preparation of cobalt aluminate/ceramic honeycomb catalyst and application thereof in dye wastewater treatment [J]. Journal of Textile Research, 2019, 40(03): 125-132.
[10] WANG Fengbo, WANG Jiayi, SUN Zheng, MA Yanxue, LÜ Yingzhi, ZHANG Weifeng, LÜ Yan, LÜ Mingming, CHEN Siyu, LI Yuling, CHEN Xiaoguang. Pilot study on treatment of polyacrylate sizing wastewater [J]. Journal of Textile Research, 2019, 40(01): 108-113.
[11] . Low temperature bonding preparation of functionalized ramie fabrics for formaldehyde photocatalytic degradation  [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(12): 106-111.
[12] . Preparation of keratin/multi-walled carbon nanotubes composite fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(02): 21-25.
[13] . Preparation of carbon nanotubes/iron oxide composite absorbents for treatment of dye-containing wastewater [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(10): 89-93.
[14] . Preparation of SBA-3/PEHA and application in wastewater treatment of dyeing [J]. Journal of Textile Research, 2015, 36(07): 83-88.
[15] . Microwave-assisted low temperature in-situ synthesis and coating of Tungsten-doped TiO2 onto cotton fabric and photocatalytic peerformance of coated fabric [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(7): 88-0.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd