Journal of Textile Research ›› 2021, Vol. 42 ›› Issue (02): 168-173.doi: 10.13475/j.fzxb.20201008807

• Dyeing and Finishing & Chemicals • Previous Articles     Next Articles

Construction of superhydrophobic surface of cotton fabrics via dissolving etching

HAO Shang1,2, XIE Yuan1,2, WENG Jiali1,2, ZHANG Wei1,2(), YAO Jiming1,2   

  1. 1. College of Textile and Garment, Hebei University of Science & Technology, Shijiazhuang, Hebei 050018, China
    2. Hebei Technology Innovation Center for Textile and Garment,Shijiazhuang, Hebei 050018, China
  • Received:2020-10-30 Revised:2020-11-27 Online:2021-02-15 Published:2021-02-23
  • Contact: ZHANG Wei E-mail:weizhang2999@163.com

Abstract:

In order to explor a green, simple and effective preparation method for making superhydrophobic cotton fabrics, polydimethylsiloxane (PDMS) coating was used to finish a cotton fabric with low surface energy, and then the salt particles were deposited and dissolved to form a rough structure. The effects of the amount of PDMS, salt particle size, deposition time and lasting time of the superhydrophobic properties of the fabric were investigated. The microstructure, element composition and stability of the superhydrophobic surface were characterized by of contact angle measuring instrument, scanning electron microscope and X-ray diffraction energy spectrum. The results show that there are micrometer pits on the surface of the cotton fabric. The static water contact angle (WCA) on the fabric surface is found up to 155.47° with the water slip angle of 5.5°. The WCA of the fabric, after immersing in strong acid and strong alkali solution for 12 h, still reaches 143.91°. After soaking the treated fabric in 60 ℃ water for 60 min, the WCA is 144.43°, and the WAC of the fabric drops by 11.31% only after 20 rubbing cycles. In addition, the superhydrophobic surface displays the self-cleaning function and anti-dyeing effect.

Key words: functional finish, superhydrophobic, dissolving etching, polydimethylsiloxane, cotton fabric, chemical stability

CLC Number: 

  • TS195.5

Fig.1

Flow chart of preparation of superhydrophobic fabric"

Fig.2

State of water droplets at different thicknesses of substrate. (a) Coating of 0.5 g PDMS; (b) Coating of 0.2 g PDMS"

Fig.3

Water contact angle of fabric under different salt particles deposition time"

Fig.4

Cassie-Baxter theoretical model"

Fig.5

SEM image of fabric. (a) Cotton fabric; (b) PDMS coated cotton fabric;(c) Salt dissolve etching PDMS coated cotton fabric"

Fig.6

EDS analysis image of superhydrophobic fabric(a) and PDMS chemical structure(b)"

Fig.7

Hairiness morphology of fabric surface after different treatments"

Fig.8

Acid and alkali resistance of fabric"

Fig.9

Influence of soaking time on hydrophobic effect of fabric"

Fig.10

Influence of number of friction cycles on hydrophobic effect of fabric"

Fig.11

Fabric self-cleaning test"

Fig.12

Anti staining test"

[1] 袁晓雨, 李伟, 朱振国, 等. 超疏水聚酯滤布的性能及其在油水分离中的应用[J]. 纺织学报, 2017,38(3):108-113.
YUAN Xiaoyu, LI Wei, ZHU Zhenguo, et al. Performance of superhydrophobic polyester filter cloth and its application in oil/water separation[J]. Journal of Textile Research, 2017,38(3):108-113.
[2] 仇伟, 刘见祥, 曾舒, 等. 超疏水涂料的制备及其防覆冰性能[J]. 表面技术, 2012,41(6):108-110.
QIU Wei, LIU Jianxiang, ZENG Shu, et al. Preparation and anti-icing properties of superhydrophobic coating[J]. Surface Technology, 2012,41(6):108-110.
[3] 刘云鸿, 李光吉, 陈超, 等. 超疏水PET织物的制备及其抗菌性能[J]. 化工学报, 2014,65(4):1517-1525.
doi: 10.3969/j.issn.0438-1157.2014.04.049
LIU Yunhong, LI Guangji, CHEN Chao, et al. Preparation and antibacterial activity of superhydrophobic PET fabric[J]. CIESC Journal, 2014,65(4):1517-1525.
[4] 王婵铭, 杨文芳, 丰万齐. 仿生超疏水表面的研究及其在纺织领域的应用[J]. 纺织科技进展, 2018(11):1-5.
WANG Chanming, YANG Wenfang, FENG Wanqi, et al. Research on bionic super-hydrophobic surface and its application in textile field[J]. Progress in Textile Science & Technology, 2018(11):1-5.
[5] 马伟伟. 超疏水表面的制备及其在建筑防水领域中的应用探索[J]. 中国建筑防水, 2018(22):5-9.
MA Weiwei. Preparation of super-hydrophobic surface and its application in building waterproofing field[J]. China Building Waterproofing, 2018(22):5-9.
[6] 梁婷, 范振忠, 刘庆旺, 等. 超疏水/超双疏表面自修复方式的研究进展[J]. 化工进展, 2019,38(7):3185-3193.
LIANG Ting, FAN Zhenzhong, LIU Qingwang, et al. Research progress on the self-healing on superhydrophobic/superamphiphobic surface[J]. Chemical Industry and Engineering Progress, 2019,38(7):3185-3193.
[7] 皇甫志杰, 郝尚, 张维. 复合无氟修饰与碱刻蚀协同制备涤纶织物超疏水表面[J]. 印染, 2019,45(11):11-16, 42.
HUANGFU Zhijie, HAO Shang, ZHANG Wei. Composite fluorine-free modification combined with alkali etching to prepare superhydrophobic surface of polyester fabric[J]. China Dyeing & Finishing, 2019,45(11):11-16, 42.
[8] 李倩, 徐丽慧, 张健国, 等. 碱刻蚀涤纶织物构筑超疏水表面[J]. 上海纺织科技, 2015,43(9):39-43.
LI Qian, XU Lihui, ZHANG Jianguo, et al. Alkali etching of polyester fabrics and preparation of the superhydrophobic surface[J]. Shanghai Textile Science & Technology, 2015,43(9):39-43.
[9] 盛宇, 徐丽慧, 孟云, 等. 用SiO2/TiO2复合气凝胶制备超疏水光催化防紫外线织物[J]. 纺织学报, 2019,40(7):90-96.
SHENG Yu, XU Lihui, MENG Yun, et al. Preparation of superhydrophobic, photocatalytic and UV-blocking textiles based on SiO2/TiO2 composite aerogels[J]. Journal of Textile Research, 2019,40(7):90-96.
[10] 张维, 邢红立, 皇甫志杰. 基于层层自组装技术构筑棉织物超疏水表面[J]. 针织工业, 2019(10):23-27.
ZHANG Wei, XING Hongli, HUANGFU Zhijie. Construction of super-hydrophobic cotton fabric based on layer-by-layer self-assembly technology[J]. Knitting Industries, 2019(10):23-27.
[1] CAI Lu, KANG Jialiang, LÜ Cun, HE Xuemei. Preparation of self-crosslinking fluorinated polyacrylate emulsion and its application properties [J]. Journal of Textile Research, 2021, 42(02): 161-167.
[2] HOU Wenshuang, MIN Jie, JI Feng, ZHANG Jianxiang, SU Meng, HE Ruixian. Influence of fabric tightness and anti-crease finishing on wrinkle recovery of pure cotton woven fabrics [J]. Journal of Textile Research, 2021, 42(01): 118-124.
[3] ZENG Fanxin, QIN Zongyi, SHEN Yueying, CHEN Yuanyu, HU Shuo. Preparation and flame retardant properties of self-extinguishing cotton fabrics by spray-assisted layer-by-layer self-assembly technology [J]. Journal of Textile Research, 2021, 42(01): 103-111.
[4] ZHANG Yanyan, ZHAN Luyao, WANG Pei, GENG Junzhao, FU Feiya, LIU Xiangdong. Research progress in preparation of durable antibacterial cotton fabrics with inorganic nanoparticles [J]. Journal of Textile Research, 2020, 41(11): 174-180.
[5] WANG Bo, FAN Lihua, YUAN Yun, YIN Yunjie, WANG Chaoxia. Preparation and electric storage performance of stretchable polypyrrole/cotton knitted fabric [J]. Journal of Textile Research, 2020, 41(10): 101-106.
[6] CHEN Shiping, CHEN Min, WEI Cen, WANG Fujun, WANG Lu. Structure and functions of medical protective clothing and trend for research and development [J]. Journal of Textile Research, 2020, 41(08): 179-187.
[7] LIU Guojin, SHI Feng, CHEN Xinxiang, ZHANG Guoqing, ZHOU Lan. Preparation of polyurethane/phase change wax functional finishing agents for heat storage and temperature regulation and their applications on cotton fabrics [J]. Journal of Textile Research, 2020, 41(07): 129-134.
[8] WANG Yating, ZHAO Jiaqi, WANG Bijia, FENG Xueling, QIAN Guochun, SUI Xiaofeng. Research progress in dyeing and functional finishing of artificial microfiber leather [J]. Journal of Textile Research, 2020, 41(07): 188-196.
[9] CHENG Shijie, WANG Chenyang, ZHANG Hongwei, ZUO Danying. Effect of boron nitrogen doped carbon dots on ultraviolet-protection of cotton fabrics [J]. Journal of Textile Research, 2020, 41(06): 93-98.
[10] ZHOU Qingqing, CHEN Jiayi, QI Zhenming, CHEN Weijian, SHAO Jianzhong. Preparation and characterization of flame retardant and antibacterial cotton fabric [J]. Journal of Textile Research, 2020, 41(05): 112-120.
[11] TAN Lin, SHI Yidong, ZHOU Wenya. Study on enhancement of hydrophobicity treatment of cotton fabrics using silica sol [J]. Journal of Textile Research, 2020, 41(04): 106-111.
[12] WEI Tengxiang, LI Min, PENG Hongyun, FU Shaohai. Relationship between open-width mercerization condition and loop structure of weft plain-knitted cotton fabrics [J]. Journal of Textile Research, 2020, 41(04): 98-105.
[13] ZHAO Bing, HUANG Xiaocui, QI Ning, ZHONG Zhou, CHE Mingguo, GE Liangliang. Research progress of antibacterial cotton fabric treated with silver nanoparticles based on covalent bond [J]. Journal of Textile Research, 2020, 41(03): 188-196.
[14] GAO Simeng, WANG Hongbo, DU Jinmei, WANG Wencong. Synthesis of polybetaine antibacterial agent and its applications in cotton textiles finishing [J]. Journal of Textile Research, 2020, 41(02): 89-94.
[15] CHANG Shuo, SHEN Jiajia. Research progress of graphene durable finishing of textiles [J]. Journal of Textile Research, 2020, 41(02): 179-186.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!