Preparation of multi-component organic polysiloxane for flame retardancy of polyamide 6 fabrics with anti-dripping behavior

FAN Shuo1,2(), YANG Peng1,3, ZENG Jinhao1,3, SONG Xiaodi1, GONG Yudan1, XIAO Yao1   

  1. 1. College of Textile Science and Engineering (International Institute of Silk), Zhejiang Sci-Tech University, Hangzhou,Zhejiang 310018, China
    2. School of Chemical & Material Engineering, Jiangnan University, Wuxi, Jiangsu 214122, China
    3. Shengzhou Research Institute of Zhejiang Sci-Tech University, Shaoxing, Zhejiang 312400, China
  • Received:2023-01-05 Revised:2023-09-26 Online:2024-01-15 Published:2024-03-14

RichHTML

12

PDF (PC)

105

Abstract:

Objective Polyamide 6 fabrics are widely used in the fields of textiles and garment, aerospace, construction, and other industries by virtue of its lightweight, softness, high-strength, and abrasion resistance. However, polyamide 6 fabric is a combustible material, which is easy to ignite with fast burning speed, high heat release, and serious melt-dripping behavior, which greatly limits the application of polyamide 6 fabrics in some special regions. Thus, developing the flame-retardant polyamide 6 fabrics with good anti-dripping behavior becomes an important and meaningful task.

Method A multi-component synergistic flame retardant of organic polysiloxane containing phosphorus and Schiff base units was designed by hydrolysis-condensation reaction. Subsequently, flame-retardant polyamide 6 fabric was prepared by dipping method, and its chemical structure, thermal stability, combustion behavior, char residues, and pyrolysis volatiles were systematically investigated by fourier transform infrared spectro scop (FT-IR), thermo-gravimetric analysis (TGA), microscale combustion calorimetry (MCC), and Py-GC/MS test methods, respectively.

Results FT-IR and XPS results showed that polyamide 6 fabric was finished by the synergistic flame retardant successfully. According to TGA results, the degradation behavior of the finished polyamide 6 fabric changed to a two-stage degradation mode under the assistance of flame retardant. The initial degradation temperature (T5%) and the temperature at maximum weight loss rate (Tmax) of the finished polyamide 6 fabric decreased distinctly. On the contrary, the carbon yield (Yc) of the finished fabric approached 33.9%, which was largely higher than that of polyamide 6 fabric (3.6%). The increased carbon residue as a physical barrier was conducive to protecting the underlying fabric from heat and combustible gases. Significant differences were also observed between polyamide 6 fabric and the finished fabric from real-time combustion images. The polyamide 6 fabric was ignited quickly with fast fire spreading speed and serious melt-dripping behavior after being heated, and the fabric kept burning until the whole fabric was burnt up. In contrast, the finished fabric was self-extinguished rapidly after the fire was removed, and no melt droplet was produced during combustion. Meanwhile, the peak of heat release rate (PHRR) and the total heat release rate (THR) values of the finished fabric decreased by 23.8% and 20.4%, respectively, compared with the polyamide 6 fabric. Moreover, the PHRR and THR values of the finished fabric after washing were still lower than that of polyamide 6 fabric. During combustion of flame-retardant polyamide 6 fabric, a compact and dense carbon layer containing large quantities of small-sized SiO2 particles was generated. This generated char layer with lower intensity D-peak/intensity G-peak (ID/IG) value exhibited higher graphitization degree than the char residues of polyamide 6 fabric. The higher graphitization degree represents higher thermal stability of char layer, which is more beneficial to improve the flame retardancy of fabric. Main pyrolysis volatiles of the finished fabric were common with polyamide 6 fabric, including carbon dioxide (CO2), caprolactam, nitriles, and carbonyl fragments. Besides, some phosphorus-containing volatiles were also produced, and the proportion of caprolactam, the major combustible pyrolysis volatiles, was reduced in the pyrolysis process of the finishing fabric, reflecting flame retardant helped to retard the chain degradation reaction of polyamide 6 backbone.

Conclusion A multi-component organic polysiloxane flame retardant is synthesized and adopted to finish a polyamide 6 fabric. With the assistance of flame retardant, the carbonization capacity and fire safety, especially the anti-dripping behavior, of polyamide 6 fabric are improved significantly. In detail, a satisfactory reduction of 23.8% in PHRR value is achieved for the finished polyamide 6 fabric, and the melt-dripping behavior of the finished polyamide 6 fabric is suppressed effectively. This significantly improved flame retardancy of polyamide 6 fabric can be attributed to synergistic effects of the formation of stable carbon layer and the release of incombustible pyrolysis volatiles, which are originated from the cooperation of polysiloxane, phosphorus group, and Schiff base structure. Moreover, the finished fabric after washing still remains good carbonization capacity and fire safety, which is crucial to post-processing and application of fabric. The reported multi-component organic polysiloxane for preparing flame-retardant polyamide 6 fabric results in good anti-dripping behavior, which will help the formation of a versatile strategy for further developing functional polyamide 6 fabric and organic polysiloxane-based flame retardants for various applications.

Key words: polyamide 6 fabric, flame-retardant finishing, flame retardant, functional textile, multi-component organic polysiloxane, anti-dripping behavior

CLC Number: 

  • TS156

Fig.1

Synthesis route of polysiloxane containing phosphorus and Schiff base unit"

Fig.2

Preparation of flame-retardant polyamide 6 fabric"

Fig.3

FT-IR spectra of flame retardant (a), polyamide 6 fabric before and after flame retardant finishing (b) and C1s XPS spectra of flame-retardant polyamide 6 fabric (c)"

Tab.1

Elemental composition of flame-retardant polyamide 6 fabric and its residues"

样品 元素含量/%
C N O P Si
织物 42.0 0.6 29.9 2.6 24.9
炭化层 58.1 5.1 19.5 3.1 14.3

Fig.4

TGA(a) and DTG (b)curves of flame-retardant polyamide 6 fabrics"

Fig.5

Real-time combustion images of samples. (a)Polyamide 6 fabric; (b) Flame-retardant polyamide 6 fabric; (c)Washed fabric"

Tab.2

Results of combustion test for fabrics"

样品 Tpeak/
℃		 PHRR/
(W·g-1)		 THR/
(kJ·g-1)		 LOI值/
%		 现象
自熄 熔滴
锦纶6织物 466 998.1 27.9 20.5 否 有
阻燃锦纶6织物 405 759.9 22.0 25.1 是 无
水洗样 416 857.2 24.1 24.0 是 无

Fig.6

SEM images of residue for polyamide 6 fabric (a) and flame-retardant polyamide 6 fabric (b) after burned"

Fig.7

Raman spectra of residue for polyamide 6 fabric (a) and flame-retardant polyamide 6 fabric (b) after burned"

Fig.8

XPS spectra of flame-retardant polyamide 6 fabric and its residues (a) and Si2p XPS spectra of residues (b)"

Fig.9

Total ion flow chromatograms of polyamide 6 fabric and flame-retardant polyamide 6 fabric"

Tab.3

Main pyrolytic compounds of polyamide 6 fabric and flame-retardant polyamide 6 fabric at 600 ℃"

织物 时间/
min		 面积比/
%		 气相产物
化学式 名称
锦纶6
织物		 1.09 14.36 CO2 二氧化碳
3.03 0.47 C5H5N 吡啶
4.12 1.55 C5H8O 环戊酮
6.51 2.09 C6H9N 5-氰基-1-戊烯
7.00 1.03 C6H11N 正己腈
14.72 39.11 C6H11NO 己内酰胺
18.35 2.13 C5H14N2 N-异丙基乙二胺
阻燃
锦纶6
织物		 1.09 4.28 CO2 二氧化碳
6.56 3.21 C6H9N 5-氰基-1-戊烯
7.03 1.41 C6H11N 正己腈
13.94 0.15 C9H11N 5-氨基茚烷
14.35 15.72 C6H11NO 己内酰胺
16.14 8.87 C12H10 2-乙烯基萘
17.91 14.14 C12H10O 邻羟基联苯
24.64 1.93 C12H8O2P DOPO
[1] 金文杰, 程献伟, 关晋平, 等. 聚酰胺6织物的磺胺阻燃抗熔滴整理[J]. 纺织学报, 2022, 43(2): 171- 175.
JIN Wenjie, CHENG Xianwei, GUAN Jinping, et al. Sulfanilamide finishing to polyamide 6 fabrics for flame retardant and anti-dripping performance[J]. Journal of Textile Research, 2022, 43(2):171-175.
[2] FENG Xiaming, WANG Xin, CAI Wei, et al. Integrated effect of supramolecular self-assembled sandwich-like melamine cyanurate/MoS2 hybrid sheets on reducing fire hazards of polyamide 6 composites[J]. Journal of Hazardous Materials, 2016, 320:252-264.
doi: S0304-3894(16)30733-6 pmid: 27544738
[3] 刘可, 陈爽, 肖茹. 磷杂菲基共聚协效阻燃聚酰胺6纤维的制备及其性能[J]. 纺织学报, 2021, 42 (7): 11-18.
LIU Ke, CHEN Shuang, XIAO Ru. Preparation and properties of synergistic flame retardant copolyamide 6 fiber with phosphaphenanthrene group[J]. Journal of Textile Research, 2021, 42 (7):11-18.
[4] DAHIYA J B, MULLER-HAGEDORN M, BOCKHORN H, et al. Synthesis and thermal behaviour of polyamide 6/bentonite/ammonium polyphosphate composites[J]. Polymer Degradation and Stability, 2008, 93(11): 2038 -2041.
doi: 10.1016/j.polymdegradstab.2008.02.016
[5] CHEN Yinghong, WANG Qi. Preparation, properties and characterizations of halogen-free nitrogen-phosphorous flame-retarded glass fiber reinforced polyamide 6 composite[J]. Polymer Degradation & Stability, 2006, 91 (9):2003-2013.
[6] FEI Guoxia, WANG Qi, LIU Yuan. Synthesis of novolac-based char former: silicon-containing phenolic resin and its synergistic action with magnesium hydroxide in polyamide-6[J]. Fire & Materials, 2010, 34(8):407-419.
[7] ALAEE Mehran, ARIAS Pedro, SJODIN Andreas, et al. An overview of commercially used brominated flame retardants, their applications, their use patterns in different countries/regions and possible modes of release[J]. Environment International, 2004, 29(6):683- 689.
doi: 10.1016/S0160-4120(03)00121-1
[8] COVACI Adrian, HARRAD Stuart, ABDALLAH Mohamed A E, et al. Novel brominated flame retardants: a review of their analysis, environmental fate and behaviour[J]. Environment International, 2011, 37(2): 532 -556.
doi: 10.1016/j.envint.2010.11.007 pmid: 21168217
[9] SEHIC Alisa, TOMSIC Brigita, JERMAN Ivan, et al. Synergistic inhibitory action of P-and Si-containing precursors in sol-gel coatings on the thermal degradation of polyamide 6[J]. Polymer Degradation and Stability, 2016, 128:245-252.
doi: 10.1016/j.polymdegradstab.2016.03.026
[10] 李宝钗, 李小科, 陈国文. 有机硅阻燃剂在聚烯烃应用中的研究进展[J]. 高分子材料科学与工程, 2020, 36(9):157-164.
LI Baochai, LI Xiaoke, CHEN Guowen. Research progress of silicone flame retardants in polyolefin applications[J]. Polymer Materials Science and Engineering, 2020, 36(9):157-164.
[11] FAN Shuo, PENG Bo, YUAN Ruchao, et al. A novel Schiff base-containing branched polysiloxane as a self-crosslinking flame retardant for PA6 with low heat release and excellent anti-dripping performance[J]. Composites Part B: Engineering, 2020, 183(15): 107684.
doi: 10.1016/j.compositesb.2019.107684
[12] SEHIC Alisa, VASILJEVIC Jelena, JORDANOV Igor, et al. Influence of N-, P- and Si-based flame retardant mixtures on flammability, thermal behavior and mechanical properties of PA6 composite fibers[J]. Fibers and Polymers, 2018, 19(6):1194-1206.
doi: 10.1007/s12221-018-8059-5
[13] LI Jialiang, WANG Hongyu, LI Shichao. A novel phosphorus-silicon containing epoxy resin with enhanced thermal stability, flame retardancy and mechanical properties[J]. Polymer Degradation and Stability, 2019, 164:36-45.
doi: 10.1016/j.polymdegradstab.2019.03.020
[14] 顾海洋, 王冬, 张丽平, 等. 制革污泥蛋白质基棉织物阻燃剂的合成及棉织物阻燃整理[J]. 功能材料, 2022, 53(1):1196-1203.
doi: 10.3969/j.issn.1001-9731.2022.01.031
GU Haiyang, WANG Dong, ZHANG Liping, et al. Synthesis of tannery sludge protein based flame retardant and flame retardant finishing of cotton fabric[J]. Functional Materials, 2022, 53(1):1196-1203.
[15] WANG Yiliang, YANG Xiaomei, PENG Hui, et al. Layer-by-layer assembly of multifunctional flame retardant based on brucite, 3-aminopropyltriethoxy silane, and alginate and its applications in ethylene-vinyl acetate resin[J]. Acs Applied Materials & Interfaces, 2016, 8(15):9925-9935.
[16] QIU Yong, QIAN Lijun, CHEN Yajun, et al. Improving the fracture toughness and flame retardant properties of epoxy thermosets by phosphaphenanthrene/siloxane cluster-like molecules with multiple reactive groups[J]. Composites Part B: Engineering, 2019. DOI: 10.1016/j.compositesb.2019.107481.
[17] SHI Xingxing, PENG Xiangfang, ZHU Jingyi, et al. Synthesis of DOPO-HQ-functionalized graphene oxide as a novel and efficient flame retardant and its application on polylactic acid: thermal property, flame retardancy, and mechanical performance[J]. Journal of Colloid & Interface Science, 2018, 524:267-278.
[18] KASHIWAGI Takashi, DU Fangming, DOUGLAS Jack F, et al. Nanoparticle networks reduce the flammability of polymer nanocomposites[J]. Nature Materials, 2005, 4(12):928-933.
pmid: 16267575
[19] HILT F, GHERARDI N, DUDAY D, et al. Efficient flame retardant thin films synthesized by atmospheric pressure PECVD through the high Co-deposition rate of hexamethyldisiloxane and triethylphosphate on polycarbonate andpolyamide-6 substrates[J]. Acs Applied Materials & Interfaces 2016, 8 (19):12422-12433.
[20] ZHAO Wei, ZHAO Haibo, CHENG Jinbo, et al. A green, durable and effective flame-retardant coating for expandable polystyrene foams[J]. Chemical Engineering Journal, 2022. DOI: 10.1016/j.cej.2022.135807.
[21] CAI Tongmin, WANG Junling, ZHANG Chuanhui, et al. Halogen and halogen-free flame retarded biologically-based polyamide with markedly suppressed smoke and toxic gases releases[J]. Composites Part B: Engineering, 2020. DOI: 10.1016/j.compositesb.2019.107737.
[22] ZHAO Dan, WANG Juan, WANG Xiuli, et al. Highly thermostable and durably flame-retardant unsaturated polyester modified by a novel polymeric flame retardant containing Schiff base and spirocyclic structures[J]. Chemical Engineering Journal, 2018, 344:419-430.
doi: 10.1016/j.cej.2018.03.102
[23] COLOVIC Marija, VASILJEVIC Jelena, STIRN Ziga, et al. New sustainable flame retardant DOPO-NH- functionalized polyamide 6 and filament yarn[J]. Chemical Engineering Journal, 2021. DOI: 10.1016/j.cej.2021.130760.
[1] GU Jinjun, WEI Chunyan, GUO Ziyang, LÜ Lihua, BAI Jin, ZHAO Hanghuiyan. Preparation and performonce of cotton stalk bast microcrystalline cellulose/modified graphene oxide composite flame-retardant fiber [J]. Journal of Textile Research, 2024, 45(01): 39-47.
[2] WEI Jianfei, MA Guocong, ZHANG Anying, WU Yuhang, CUI Xiaoqing, WANG Rui. Preparation of gelatin-based carbon dots by pyrolysis and its applications in flame retardant and anti-counterfeiting [J]. Journal of Textile Research, 2023, 44(12): 106-114.
[3] CHEN Shun, QIAN Kun, LIANG Fuwei, GUO Wenwen. Preparation and properties of flame retardant hydrophobic cotton fabric with eugenol-based composite coating [J]. Journal of Textile Research, 2023, 44(12): 115-122.
[4] ZHANG Wenqi, LI Lili, HU Zexu, WEI Lifei, XIANG Hengxue, ZHU Meifang. Preparation method of and anti-dripping and flame retardant properties of polycaprolactam 6 composite resin based on homotriazine ring structure [J]. Journal of Textile Research, 2023, 44(11): 1-8.
[5] ZHANG Guangzhi, YANG Fusheng, FANG Jin, YANG Shun. One bath flame retardant finishing of polylactic acid nonwoven by phytic acid/chitosan/boric acid [J]. Journal of Textile Research, 2023, 44(10): 120-126.
[6] WANG Yutao, CONG Honglian, GU Hongyang. Structural design and thermal-moist comfort of weft knitted knee pads [J]. Journal of Textile Research, 2023, 44(10): 68-74.
[7] QIAN Yaowei, YIN Lianbo, LI Jiawei, YANG Xiaoming, LI Yaobang, QI Dongming. Preparation and properties of flame retardant cotton fabrics by layer-by-layer assembly of polyvinylphosphonic acid and polyethylene polyamine [J]. Journal of Textile Research, 2023, 44(09): 144-152.
[8] SHANG Xiaoyu, ZHU Jian, WANG Ying, ZHANG Xianming, CHEN Wenxing. Synthesis and solid-state polymerization of flame retardant copolyester containing phosphorus side groups [J]. Journal of Textile Research, 2023, 44(07): 1-9.
[9] JIANG Zhiming, ZHANG Chao, ZHANG Chenxi, ZHU Ping. Preparation and properties of flame-retardant viscose fabrics modified with phosphated polyethyleneimine [J]. Journal of Textile Research, 2023, 44(06): 161-167.
[10] YANG Haifu, LUO Lijuan, SHI Jianjun, MA Xiaoguang, ZHENG Zhenrong. Preparation of flame-retardant and waterproof multifunctional polyester tarpaulin [J]. Journal of Textile Research, 2023, 44(06): 168-174.
[11] TAN Qifei, CHEN Mengying, MA Shengsheng, SUN Mingxiang, DAI Chunpeng, LUO Lunting, CHEN Yiren. Preparation and properties of nonwoven flame retardant sound-absorbing material from Hu sheep wool [J]. Journal of Textile Research, 2023, 44(05): 147-154.
[12] LIU Xinyu, LI Jianhao, WANG Zhen, SHEN Junyan, YANG Lei. Preparation and waterproof properties of fluorine-free polyacrylate latex composites [J]. Journal of Textile Research, 2023, 44(04): 124-131.
[13] CHEN Zhijie, JIANG Jikang, YU Yihao, FU Ye, WU Jindan, QI Dongming. Synthesis of silicon phosphorus modified calcium carbonate and its application in polyamide coating [J]. Journal of Textile Research, 2023, 44(04): 146-153.
[14] PANG Mingke, WANG Shuhua, SHI Sheng, XUE Lizhong, GUO Hong, GAO Chengyong, LU Jianjun, ZHAO Xiaowan, WANG Zihan. Preparation and application of flame retardant waterborne polyurethane by alcoholysis of waste polyethylene terephthalate fiber [J]. Journal of Textile Research, 2023, 44(02): 214-221.
[15] REN Jiawei, ZHANG Shengming, JI Peng, WANG Chaosheng, WANG Huaping. Preparation and properties of phosphorus-silicon modified flame retardant and anti-dripping polyester fiber [J]. Journal of Textile Research, 2023, 44(02): 1-10.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd