Journal of Textile Research ›› 2024, Vol. 45 ›› Issue (04): 67-75.doi: 10.13475/j.fzxb.20230403001

• Fiber Materials • Previous Articles     Next Articles

Preparation and photocatalytic performance of titanium dioxide/porous carbon nanofibers composite material

LU Yaoyao, YE Juntao, RUAN Chengxiang(), LOU Jin   

  1. Jiangxi Key Laboratory of Surface Engineering, Jiangxi Science and Technology Normal University, Nanchang, Jiangxi 330036, China
  • Received:2023-04-18 Revised:2024-01-15 Online:2024-04-15 Published:2024-05-13

RichHTML

7

PDF (PC)

32

Abstract:

Objective With the widespread use of organic dyes, the residue of which have gradually become the main component of industrial wastewater and caused serious water pollution. As an environmentally friendly photocatalyst, titanium dioxide (TiO2) nanoparticles have been used in dye degradation, wastewater treatment and other fields due to their high photocatalytic activity, large specific surface area and easy preparation, but they also have problems such as wide band gap and difficult separation and recovery. Therefore, it is urgent to find a suitable carrier material to achieve effective separation and recovery of TiO2 without reducing its photocatalytic activity and stability.

Method Porous carbon nanofibers (PCNF) were prepared by electrospinning, high-temperature calcination, and acid dissolution. Then anatase TiO2 was loaded onto its surface by secondary nucleation method to obtain photocatalytic TiO2/PCNF composites. The morphology, structure, composition, and light absorption properties of TiO2/PCNF nanocomposites were characterized by scanning electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy and UV-Vis diffuse reflection spectroscopy, and the photocatalytic properties of TiO2/PCNF nanocomposites were tested by degradation methylene blue (MB) solution.

Results SEM results showed that TiO2 nanoparticles were uniformly loaded on porous CNF surfaces, while it was difficult to be loaded on smooth CNF surfaces. This showed that the mesoporous surface of carbon nanofibers was the key to the loading of TiO2. XRD results indicated that the three samples prepared, i.e., TiO2, TiO2/PCNF and TiO2/CNF were of anatase phase TiO2. Compared with rutile phase and titanite phase, anatase phase TiO2 had better photocatalytic activity, so it was beneficial to improve the photocatalytic performance of TiO2/PCNF. The full spectrum of XPS showed that Ti, O, C, F and N elements existed in TiO2/PCNF composites, which further proved that TiO2 had been successfully loaded onto the surface of porous carbon nanofibers. The UV-Vis DRS results showed that significant redshift could occur when TiO2 was loaded onto both PCNF and CNF surfaces, which not only increased the utilization rate of visible light, but also reduced the band gap value. Brunauer-Emmett-Teller(BET)results suggested that the prepared TiO2/PCNF composites had mesoporous structures, and the specific surface area was as high as 331.9 m2/g, providing abundant active sites for adsorption and surface reaction. The photocatalytic tests showed that the removal efficiency of TiO2/PCNF composites was higher than that of the control group with the same TiO2 content. After 30 min illumination of TiO2/PCNF composite material, the removal rate of MB solution of 5 mg/L was 98.6%, and after 60 min illumination, the removal rate of MB solution could reach 99.6%. However, the removal rates of TiO2 and TiO2/CNF composites in the control group were only 93.3% and 73.2% for MB solution after 30 min illumination. After repeated use for 5 times, the removal rate of TiO2/PCNF on MB solution remained at 95.0%. All these indicated that TiO2/PCNF composites have excellent photocatalytic and reusable properties.

Conclusion The TiO2/PCNF composite was successfully prepared by secondary nucleation method, and the composite had excellent photocatalytic and reusable properties. Compared with CNF, it was found that PCNF with mesoporous structure was more conducive to the loading of TiO2. The improvement of photocatalytic performance of TiO2/PCNF composites was mainly attributed to the following reasons. ①All the prepared TiO2 were anatase phase, which has better photocatalytic activity than rutile phase and plate titanite phase. ②The TiO2/PCNF composite increased the response range of TiO2 to visible light, which was conducive to improve the utilization rate of TiO2 for visible light. ③PCNF had excellent electrical conductivity, which was conducive to accelerating the separation of TiO2 photogenerated electrons and holes. ④PCNF had a large specific surface area, which providing more active sites both for MB adsorption and surface reactions.

Key words: organic dye, photodegradation, titanium dioxide, electrospinning, carbon nanofiber, methylene blue, secondary nucleation method, photocatalytic performance, wastewater treatment

CLC Number: 

  • TQ619.2

Fig.1

SEM images(×10 000) of CNF(a), PCNF precursor(b), PCNF (c), TiO2(d), TiO2/PCNF(e), TiO2/CNF(f)"

Fig.2

XRD patterns of TiO2,TiO2/PCNF and TiO2/CNF"

Fig.3

XPS patterns of TiO2/PCNF. (a) Total spectrum; (b) C1s spectrogram; (c) Ti2p spectrogram; (d) O 1s spectrogram"

Fig.4

UV-Vis DRS patterns(a) and band-gap energy(b) of prepared samples"

Fig.5

N2 adsorption desorption isotherm(a) and aperture distribution diagram curve(b) of samples"

Tab.1

BET analysis results of TiO2, TiO2/PCNF and TiO2/CNF"

试样名称 孔径/
nm		 孔体积/
(cm3·g-1)		 比表面积/
(m2·g-1)
TiO2 3.943 0.220 275.015
TiO2/PCNF 1.382 0.106 331.940
TiO2/CNF 13.171 0.216 58.418

Fig.6

UV-Vis patterns and degradation efficiency curve of prepared samples. (a) UV-Vis spectrum of TiO2; (b) UV-Vis spectrum of TiO2/PCNF; (c) UV-Vis spectrum of TiO2/CNF; (d) Degradation efficiency curve"

Fig.7

Degradation efficiency curve of TiO2/PCNF cycle experiment"

[1] MAO D, YUAN J, QU X, et al. Size tunable Bi3O4Br hierarchical hollow spheres assembled with {001}-facets exposed nanosheets for robust photocatalysis against phenolic pollutants[J]. Journal of Catalysis, 2019, 369: 209-221.
[2] CHEN J, XIONG Y, DUAN M, et al. Insight into the synergistic effect of adsorption-photocatalysis for the removal of organic dye pollutants by Cr-doped ZnO[J]. Langmuir, 2019, 36(2):520-533.
[3] ZHANG Q, YU L, YANG B, et al. Magnetic Fe3O4@Ru-doped TiO2 nanocomposite as a recyclable photocatalyst for advanced photodegradation of methylene blue in simulated sunlight[J]. Chemical Physics Letters, 2021. DOI:10.1016/j.cplett.2021.138609.
[4] HENG J, TANG K Y, MD R, et al. Solar-powered photodegradation of pollutant dyes using silver-embedded porous TiO2 nanofibers[J]. Nanomaterials, 2021. DOI:10.3390/nano11040856.
[5] 杨丽, 王涛, 石现兵, 等. 改性聚丙烯腈纤维负载 MoSx/TiO2 光催化材料制备及其降解染料性能[J]. 纺织学报, 2022, 43(9): 149-155.
YANG Li, WANG Tao, SHI Xianbing, et al. Preparation of modified polyacrylonitrile fiber supported MoSx/TiO2 composite photocatalyst and its performance for dye degradation[J]. Journal of Textile Research, 2022, 43(9): 149-155.
[6] ZHANG Q, YU L, XU C, et al. A novel method for facile preparation of recoverable Fe3O4@TiO2 core-shell nanospheres and their advanced photocatalytic application[J]. Chemical Physics Letters, 2020. DOI:10.1016/j.cplett.2020.138073.
[7] LI R, LI T, ZHOU Q. Impact of titanium dioxide(TiO2) modification on its application to pollution treatment: a review[J]. Catalysts, 2020. DOI:10.3390/catal10070804.
[8] YU D, BAI J, GU Y, et al. Solvothermal synthesis of TiO2/CNFs heterostructures with photocatalytic activity[J]. Nano, 2015. DOI:10.1142/S1793292015500800.
[9] DODOO-ARHIN D, BUABENG F P, MWABORA J M, et al. The effect of titanium dioxide synthesis technique and its photocatalytic degradation of organic dye pollutants[J]. Heliyon, 2018. DOI:10.1016/j.heliyon.2018.e00681.
[10] 李梦悦, 房国丽, 张刚, 等. TiO2/AC复合材料的吸附性与光催化性能[J]. 河北大学学报(自然科学版), 2018, 38(5):480-489.
doi: 10.3969/j.issn.1000-1565.2018.05.006
LI Mengyue, FANG Guoli, ZHANG Gang, et al. Adsorption and photocatalytic performance of TiO2/AC composites[J]. Journal of Hebei University (Natural Science Edition), 2018, 38(5):480-489.
[11] XIAO F, GUO X, LI J, et al. Electrospinning preparation and dye adsorption capacity of TiO2@carbon flexible fiber[J]. Ceramics International, 2019, 45(9): 11856-11860.
[12] CHUNG W J, CHUN S Y, KIM S S, et al. Photocatalytic removal of tetracycline using TiO2/Ge composite optimized by response surface methodo-logy (RSM)[J]. Journal of Industrial & Engineering Chemistry, 2016,36:320-325.
[13] 费锡智, 杨晶晶, 白仁碧. 光催化-膜分离耦合技术的水处理应用研究进展[J]. 水处理技术, 2014(12): 11-18.
FEI Xizhi, YANG Jingjing, BAI Renbi. Research progress in application of photocatalysis membrane separation coupling technology in water treatment[J]. Water Treatment Technology, 2014(12):11-18.
[14] MARINHO B A, DE SOUZA S M A G U, DE SOUZA A A U, et al. Electrospun TiO2 nanofibers for water and wastewater treatment: a review[J]. Journal of Materials Science, 2021, 56:5428-5448.
[15] ZHOU F L, GONG R H, PORAT I. Mass production of nanofibre assemblies by electrostatic spinning[J]. Polymer International, 2010, 58(4):331-342.
[16] XUE J, WU T, DAI Y, et al. Electrospinning and electrospun nanofibers: methods, materials, and applications[J]. Chemical Reviews, 2019, 119(8):5298-5415.
doi: 10.1021/acs.chemrev.8b00593 pmid: 30916938
[17] CHANG G, ULLAH W, HU Y, et al. Functional carbon nanofibers with semi-embedded titanium oxide particles via electrospinning[J]. Macromolecular Rapid Communications, 2018. DOI:10.1002/marc.201800102.
[18] BLANCO M, MONTESERIN C, ANGULO A, et al. TiO2-doped electrospun nanofibrous membrane for photocatalytic water treatment[J]. Polymers, 2019. DOI:10.3390/polym11050747.
[19] 张梦媛, 黄庆林, 黄岩, 等. 静电纺聚四氟乙烯/二氧化钛光催化纳米纤维膜的制备及其应用[J]. 纺织学报, 2019, 40(9): 1-7.
ZHANG Mengyuan, HUANG Qinglin, HUANG Yan, et al. Electrospun poly(tetrafluoroethylene)/TiO2 photocatalytic nanofiber membrane and its applica-tion[J]. Journal of Textile Research, 2019, 40(9): 1-7.
[20] 钱怡帆, 周堂, 张礼颖, 等. 聚丙烯腈/醋酸纤维素/TiO2复合纳米纤维膜的制备及其光催化降解性能[J]. 纺织学报, 2020, 41(5):8-14.
QIAN Yifan, ZHOU Tang, ZHANG Liying, et al. Preparation of polyacrylonitrile/cellulose acetate/TiO2 composite nanofiber membrane and its photocatalytic degradation performance[J]. Journal of Textile Research, 2020, 41(5):8-14.
[21] AGHASILOO P, YOUSEFZADEH M, LATIFI M, et al. Highly porous TiO2 nanofibers by humid-electrospinning with enhanced photocatalytic proper-ties[J]. Journal of alloys and compounds, 2019, 790:257-265.
[22] XU S, HOU Z, CHUAI X, et al. Overview of secondary nucleation: from fundamentals to application[J]. Industrial & Engineering Chemistry Research, 2020, 59(41): 18335-18356.
[23] 于翔, 张效琳, 孟青青, 等. TiO2/碳纳米纤维膜的制备与光催化性能[J]. 工业水处理, 2020, 40(12):96-99.
doi: 10.11894/iwt.2020-0049
YU Xiang, ZHANG Xiaolin, MENG Qingqing, et al. Preparation of TiO2/carbon nanofibers membrane and its photocatalytic performance[J]. Industrial Water Treatment, 2020, 40(12):96-99.
doi: 10.11894/iwt.2020-0049
[24] BALTA Z, BILGINSIMSEK E, BEREK D. Solvothermal synthesis of WO3/TiO2/carbon fiber composite photocatalysts for enhanced performance under sunlight illumination[J]. Photochemistry and Photobiology, 2019, 95(6):1331-1338.
[25] ETACHERI V, DI VALENTIN C, SCHNEIDER J, et al. Visible-light activation of TiO2 photocatalysts: advances in theory and experiments[J]. Journal of Photochemistry & Photobiology C Photochemistry Reviews, 2015, 25:1-29.
[26] HAN X, KUANG Q, JIN M, et al. Synthesis of titania nanosheets with a high percentage of exposed (001) facets and related photocatalytic properties[J]. Journal of The American Chemical Society, 2009, 131(9):3152-3153.
doi: 10.1021/ja8092373 pmid: 19216572
[27] 张天亮, 李军, 熊巍, 等. 碳酸钾活化一步法制备高比表活性炭及其电容性能的研究[J]. 无机盐工业, 2022, 54(4):159-164.
ZHANG Tianliang, LI Jun, XIONG Wei, et al. Study on one-step preparation of activated carbon with high specific surface by K2CO3 activation and its capacitance performance[J]. Inorganic Chemicals Industry, 2022, 54(4):159-164.
[28] RAZA N, RAZA W, GUL H, et al. Solar-light-active silver phosphate/titanium dioxide/silica heterostructures for photocatalytic removal of organic dye[J]. Journal of Cleaner Production, 2020. DOI:10.1016/j.jclepro.2020.120031.
[1] JIA Lin, DONG Xiao, WANG Xixian, ZHANG Haixia, QIN Xiaohong. Preparation and performance of polycaprolactone/MgO composite nanofibrous filter membrane [J]. Journal of Textile Research, 2024, 45(04): 59-66.
[2] LI Fang, ZHANG Yili, WANG Man, MENG Xiangzhou, SHEN Chensi. Acute toxic effects of antimony contaminants on green algae and cyanobacteria [J]. Journal of Textile Research, 2024, 45(04): 169-179.
[3] SONG Beibei, ZHAO Haoyue, LI Xinyu, QU Zhan, FANG Jian. Application of MXene-loaded cobalt-nitrogen doped carbon nanofibers in lithium-sulfur batteries [J]. Journal of Textile Research, 2024, 45(04): 24-32.
[4] YANG Qi, DENG Nanping, CHENG Bowen, KANG Weimin. Preparation and application properties of dendritic sulfonated polyethersulfone fiber based composite solid electrolyte [J]. Journal of Textile Research, 2024, 45(03): 1-10.
[5] ZHAO Meiqi, CHEN Li, QIAN Xian, LI Xiaona, DU Xun. Preparation and performance of electrospun membrane for Cu(Ⅱ) detection [J]. Journal of Textile Research, 2024, 45(03): 11-18.
[6] CHEN Rongxuan, SUN Hui, YU Bin. Preparation and photocatalytic properties of N-TiO2/ polypropylene melt-blown nonwovens [J]. Journal of Textile Research, 2024, 45(03): 137-147.
[7] TIAN Boyang, WANG Xiangze, YANG Yiwen, WU Jing. Preparation and thermal management properties of asymmetric structured fibrous membranes [J]. Journal of Textile Research, 2024, 45(02): 11-20.
[8] XIAO Hao, SUN Hui, YU Bin, ZHU Xiangxiang, YANG Xiaodong. Preparation of chitosan-SiO2 aerogel/cellulose/polypropylene composite spunlaced nonwovens and adsorption dye performance [J]. Journal of Textile Research, 2024, 45(02): 179-188.
[9] ZHOU Xinru, FAN Mengjing, YUE Xinyan, HONG Jianhan, HAN Xiao. Preparation of conductive micro-nano fiber composite yarns and their gas-sensitive properties [J]. Journal of Textile Research, 2024, 45(02): 52-58.
[10] CHEN Jiangping, GUO Chaoyang, ZHANG Qijun, WU Renxiang, ZHONG Lubin, ZHENG Yuming. Preparation and air filtration performance of electrospun polyamide 6/polystyrene composite membranes [J]. Journal of Textile Research, 2024, 45(01): 56-64.
[11] LEI Caihong, YU Linshuang, JIN Wanhui, ZHU Hailin, CHEN Jianyong. Preparation and application of silk fibroin/chitosan composite fiber membrane [J]. Journal of Textile Research, 2023, 44(11): 19-26.
[12] XU Zhihao, XU Danyao, LI Yan, WANG Lu. Research progress in nanofiber-based biosensors based on surface enhanced Raman spectroscopy [J]. Journal of Textile Research, 2023, 44(11): 216-224.
[13] WANG Xixian, GUO Tianguang, WANG Dengke, NIU Shuai, JIA Lin. Preparation and long-lasting performance of polyacrylonitrile/Ag composite nanofiber membrane for high efficiency filtration [J]. Journal of Textile Research, 2023, 44(11): 27-35.
[14] FAN Mengjing, WU Lingya, ZHOU Xinru, HONG Jianhan, HAN Xiao, WANG Jian. Construction of capacitive sensor based on silver coated polyamide 6/polyamide 6 nanofiber core-spun yarn [J]. Journal of Textile Research, 2023, 44(11): 67-73.
[15] ZHANG Chengcheng, LIU Rangtong, LI Shujing, LI Liang, LIU Shuping. Pore-forming mechanism via non-solvent volatilization induced phase separation and porous nanofiber preparation based on poly-l-lactic acid [J]. Journal of Textile Research, 2023, 44(10): 16-23.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd