JOURNAL OF TEXTILE RESEARCH ›› 2016, Vol. 37 ›› Issue (10): 83-88.

Previous Articles     Next Articles

Preparation and waterproof and water-permeable properties of electrospun fluorinated polyurethanel polyurethane

  

  • Received:2015-09-16 Revised:2016-06-07 Online:2016-10-15 Published:2016-10-31

PDF (PC)

281

Abstract:

In order to obtain a high waterproofness clothing with good permeability, the paper reported a novel waterproof and water permeable fabric, the electrospun nanofibrous membranes was prepared by electrospinning, which possessed low surface free energy and rough surface, and then a polyester-cotton woven fabric with twill was used as a substrate for the nanofibrous membranes. The effects of concentration of fouorinated polyurethane (FPU) on morphological structure of nanofibers, water proof, vapor permission and mechanical properties of the electrospun nanofibrous membranes composite fabrics were studied. The results indicated that the optimum concentration of FPU for the electrospun nanofibrous membranes composite fabrics were 1.00%, meantime, the composite fabrics were endowed with the water contact angle of 141 °, the water vapor transmission rate achieves to 3 958 g/(m² • 24 h）, and the spray grade can reach up to 5 , whilst the air permeability amount to 34.06 mm/s. The mechanical properties test showed that the mechanical properties gradually increased with the increase of FPU amount, when the concentration of FPU is 1.00%, and the value of bursting strength, tearing strength and tensile strength were enhanced by about 5.93%，30.79% and 5.48%, respectively.

Key words: waterproof and water permeable, electrospinning, composite fabric, fluorinated polyruethane/polyurethane nanofiber membrane

参考文献 [1] 高党鸽, 张文博, 马建中. 防水透湿织物的研究进展[J]. 印染, 2011, 37(21): 45-50. GAO Dangge, ZHANG Wenbo, MA Jianzhong. Research and development of moisture-management fabric[J]. Dyeing and Finishing, 2011, 37(21): 45-50. [2] 刘延波, 马营, 孙健, 等. 电纺 PVDF/PVDF-HFP 复合纳米纤维膜及其防水透湿性能评价[J]. 天津工业大学学报, 2014, 33(6): 6-10. LIU Yanbo, MA Ying, SUN Jian. Composite nanofiber membrane based on electrospun PVDF/PVDF-HFP and evaluation for waterproof & breathable properties[J]. Journal of Tianjin Polytechnic University, 2014, 33(6): 6-10. [3] 陈丽华. 不同种类防水透湿织物的性能及发展[J]. 纺织学报, 2012, 33(7): 149-156. CHEN Lihua. Properties and development trends of different kinds of waterproof and moisture permeable fabrics[J]. Journal of Textile Research, 2012, 33(7): 149-156. [4] Hong K A, Yoo H S, Kim E. Effect of waterborne polyurethane coating on the durability and breathable waterproofing of electrospun nanofiber web-laminated fabrics[J]. Textile Research Journal, 2015, 85(2): 160-170. [5] Yoon B, Lee S. Designing waterproof breathable materials based on electrospun nanofibers and assessing the performance characteristics[J]. Fibers and Polymers, 2011, 12(1): 57-64. [6] Wang J, Li Y, Tian H, et al. Waterproof and breathable membranes of waterborne fluorinated polyurethane modified electrospun polyacrylonitrile fibers[J]. RSC Advances, 2014, 4(105): 61068-61076. [7] Hong S K, Lim G, Cho S J. Breathability Enhancement of Electrospun Microfibrous Polyurethane Membranes through Pore Size Control for Outdoor Sportswear Fabric[J]. Sensors and Materials, 2015, 27(1): 77-85. [8] 周颖 姚理荣 高强. 聚氨酯/聚偏氟乙烯共混膜防水透气织物的制备及其性能[J]. 纺织学报, 2014, 35(5): 23-0. ZHOU Ying, YAO Lirong, GAO Qiang. Preparation and characterization of polyurethane/polyvinylidene fluoride waterproof permeable composite fabric[J]. Journal of Textile Research. 2014, 35(5): 23-0. [9] Li Y, Zhu Z, Yu J, et al. Carbon Nanotubes Enhanced Fluorinated Polyurethane Macroporous Membranes for Waterproof and Breathable Application[J]. ACS applied materials & interfaces, 2015, 7(24): 13538-13546. [10] Wang J, Raza A, Si Y, et al. Synthesis of superamphiphobic breathable membranes utilizing SiO 2 nanoparticles decorated fluorinated polyurethane nanofibers[J]. Nanoscale, 2012, 4(23): 7549-7556.
[1] . Preparation and properties of orientation reinforced composite separator for lithium-ion battery [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(07): 8-14.
[2] . Preparation technology and application progress of solution blown nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(07): 165-173.
[3] . Preparation and properties of electrospun polyacrylonitrile nanofiber coated window screen [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(04): 14-18.
[4] . Overview on mass production of electrospun nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(03): 175-180.
[5] . Oil absorption property of electrospun superfine fibrous membrane [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(02): 7-13.
[6] . Electrospun barium titanate/ poly(vinylidene fluoride) nano-composite flexibility piezoelectric fibrous membranes [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(02): 14-19.
[7] . Preparation of crosslinking and high performance polymers [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(01): 6-10.
[8] . Effects of coaxial electrospinning parameters on morphology and carbonization yield of polyacrylonitrile hollow carbon nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(12): 1-6.
[9] . Preparation of ultrafine polyacrylonitrile nanofibers via composite electrospinning [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(11): 16-21.
[10] . Research Progress in preparation and application of electrospinning porous carbon nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(11): 168-176.
[11] . Synthesis of fluorinated polyurethane and acid-proofness and water permeability of electrospun nanofiber membrane composite fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(10): 7-12.
[12] . In fluence of hydrogen bonding on electrospinning of starch nanofiber in dimethyl sulfoxide/H2O solution [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(09): 19-23.
[13] . Preparation and gas-liquid filtration performance of composite filters of electrospun polyacrylonitrile nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(09): 8-13.
[14] . Crystallization behavior and mechanical properties of electrospun polyester/palm fiber-based activated carbon composite  [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(08): 6-10.
[15] . Preparation and properties of gradient filter materials with different packing density [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(07): 23-27.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd