JOURNAL OF TEXTILE RESEARCH ›› 2017, Vol. 38 ›› Issue (02): 34-39.doi: 10.13475/j.fzxb.20161003506

Previous Articles     Next Articles

Pre-oxidation process of polyacrylonitrile nanofiber bundles

  

  • Received:2016-10-14 Revised:2016-11-12 Online:2017-02-15 Published:2017-02-27

Abstract:

The process of pre-oxidation provides the reference for manufacturing of carbon nanofibers with high-performance. The polyacrylonitrile (PAN) nanofiber bundle with high alignment was fabricated by a multi-needle electrospinning process. The structure of nanofibers was investigated, and the influence of pre-oxidation temperature and time on the structures and properties of nanofibers were also discussed. The results indicate that the process of electrospinning could be continuously carried out for more than five hours, and the diameter of nanofibers was about 218 nm, meanwhile, the alignment degree of nanofibers along with the axis of bundle was as far as 76.52%. The cross section of nanofibers was a typical core-shell structure with a tight coating and soft core structure. With the increase of pre-oxidation temperature or time, the degree of dehydrogenation, cyclization and oxidation reactions improved. The degree of crystallinity of pre-oxidation nanofibers first increased, and then decreased with the increase of temperature, and the maximum value was 54.57%. The suitable pre-oxidation temperature was between 260℃ and 280℃ and the time was 1~2h, confirmed by the results of infrared spectroscopy, X-ray diffraction and aromatization index.

Key words: multi-needle electrospinning, nanofiber bundle, polyacrylonitrile, pre-oxidation

[1] . Preparation and properties of laminated nanofiber-based separator with over-temperature protection function [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(07): 21-26.
[2] . Preparation and properties of electrospun polyacrylonitrile / copper sulfate nanofibrous membrane [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(07): 15-20.
[3] . Preparation and properties of electrospun polyacrylonitrile nanofiber coated window screen [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(04): 14-18.
[4] . Properties of pre-oxidized polyacrylonitrile / aramid fiber needled filters [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(03): 61-66.
[5] . Effects of coaxial electrospinning parameters on morphology and carbonization yield of polyacrylonitrile hollow carbon nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(12): 1-6.
[6] . Preparation of ultrafine polyacrylonitrile nanofibers via composite electrospinning [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(11): 16-21.
[7] . Preparation and properties analysis of polyacrylonitrile anti-ultraviolet composite nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(10): 1-6.
[8] . Preparation and gas-liquid filtration performance of composite filters of electrospun polyacrylonitrile nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(09): 8-13.
[9] . Ultraviolet protective properties of polyacrylonitrile/TiO2 nanofiber [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(07): 18-22.
[10] . Recent progress in coordination of modified polyacrylonitrile fiber with metal ions and applications [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(06): 143-150.
[11] . Influence of spinning process and pre-oxidation conditions on PAN-based carbon nanofibers fabricated by centrifugal spinning [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(2): 7-0.
[12] . Influence of polyethylene oxide molecular weights on sizing performances of pre-oxidized polyacrylonitrile staple warps [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(09): 78-83.
[13] . Preparation of silk fibroin modified polyacrylonitrile fiber by coating method [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(01): 6-10.
[14] . Preparation of electrospun polyacrylonitrile nanofiber filament yarn and influence of heat-finishing on its properties [J]. JOURNAL OF TEXTILE RESEARCH, 2015, 36(09): 7-12.
[15] . Water absorbency, retention and wicking properties of electrospun fibrous bundles [J]. JOURNAL OF TEXTILE RESEARCH, 2015, 36(08): 11-15.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!