Function finishing and anti-dripping property of polyethylene terephthalate fabbrie coated with graphene oxide

  

  • Received:2016-10-12 Revised:2016-11-17 Online:2017-02-15 Published:2017-02-27

Abstract:

Polyethylene terephthalate(PET)fabric was functional finished with graphene oxide (GO) and coupling agent KH560 by conventional pad-dry-cure method. The influence of functional finish on anti-dripping property and structure of the fabric was investigated. The results showed that PET fabric had no dripping with the good char forming at time of combustion. SEM result show that the graphene oxide film is formed uniformly on the surface of PET fabric and the residue char after burning had the intrinsic structure of PET fabric with the dense and tight sate. The thermal property changed a little, and XPS data analysis show that the ratio of C/O decreased and the function group C=O increased in the char after vertical burning test. Hence, the addition of GO play the physical role on the dripping resistance of coated PET fabrics apparently.

Key words: function finishing, graphene oxide, polyethylene terephthalate fabric, dripping property

CLC Number: 

  • TS131.9
[1] . Preparation and properties of superhydrophobic conductive polyethylene terephthalate fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(08): 88-94.
[2] . Preparation of wool keratin and its modification to polyester fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(03): 92-97.
[3] . Research progress of graphene-plus adsorption and separation functional materials [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(10): 162-0169.
[4] . Influence of carbon materials on degradation of sodium alginate spinning solution [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(2): 138-0.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!