JOURNAL OF TEXTILE RESEARCH ›› 2017, Vol. 38 ›› Issue (07): 95-100.doi: 10.13475/j.fzxb.20160802206

Previous Articles     Next Articles

Influence of curing process on tribological properties of glass fiber composite

  

  • Received:2016-08-09 Revised:2017-03-23 Online:2017-07-15 Published:2017-07-18

Abstract:

Decomposition products of asbestos friction material are carcinogenic and have severe pollution on the environment. In order to develop new ono-asbestos friction materials, glass fiber fabric which has excellent mechanical properties compared with asbestos was used as substrate, and phenolic resin was used as curing agent, By molding and curing, the friction material products were prepared. The influence of curing temperature, curing time, fiber orientation and phenolic resin on the tribological properties of glass fiber composite was studied in this paper. The results show that the optimum condition is curing time of 1 h and curing temperature of 180°C. Under this condition, the wear rate of the composite is the lowest with a friction coefficient of 0.25. The friction and wear properties of the glass fiber composite meet the application requirements. Furthermore, it can be widely used in various fields due to the advantages of low-cost, environmental friendiness, good heat resistance and mechanical strength.

Key words: glass fiber fabric, phenolic resin, curing process, friction property

[1] . Permeability of glass fiber fabrics under shear deformation [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(08): 58-62.
[2] . Development of new fluoroethylene vinyl ether reinforcement membrane and its mechanical properties [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(07): 50-54.
[3] . Permeation behavior and permeability of warp-knitted quadri-axial glass fiber fabric [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(10): 49-56.
[4] . Friction and wear properties of stratified 3-D woven carbon fiber preform reinforced phenolic resin-based composites [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(02): 75-80.
[5] . Numerical simulation of heat transfer on glass fiber woven fabric [J]. JOURNAL OF TEXTILE RESEARCH, 2015, 36(03): 28-0.
[6] . Preparation of glass fiber fabrics with properties of heat insulation and ablative resistance [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(3): 32-0.
[7] . Microstructure and properties of radar absorbing iron fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(1): 16-19.
[8] Zhang Jinqiu;ZHANG Jianchun;WANG Shanyuan. Effect of softening finishing on properties of hemp fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2010, 31(4): 98-102.
[9] WANG Xu;LIU Ping;WANG Fumei. Fabric friction as affected by different human skin [J]. JOURNAL OF TEXTILE RESEARCH, 2010, 31(3): 45-49.
[10] YAO Yuefei;GAO Lei;YANG Qiongli;YU Laiming;LUO Yongbo;FU Yaqin;LIU Guanfeng. Effect of glass fabric structural parameters on its acoustic insulation property [J]. JOURNAL OF TEXTILE RESEARCH, 2009, 30(02): 52-55.
[11] SUN Yu;ZHENG Guo;DOU Chun-hua. Application of potassium alkyl-phosphate on the surface of polyester staple fiber [J]. JOURNAL OF TEXTILE RESEARCH, 2006, 27(5): 73-75.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!